DEVELOPING LOW PRESSURE INJECTION MOLD MANUFACTURING BY USING 3D PRINTING
3D BASKI KULLANARAK DÜŞÜK BASINÇLI ENJEKSİYON KALIBI ÜRETİMİNİN GELİŞTİRİLMESİ
- Tez No: 1023879
- Danışmanlar: PROF. DR. ÖMER EYERCİOĞLU
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Düşük Basınçlı Enjeksiyon Kalıplama, 3D Baskı, Maskeli Stereolitografi, Hızlı Kalıp, Kürleme Süresi, Eğme Özellikleri, Low Pressure Injection Molding, 3D Printing, Masked Stereolithography, Rapid Tooling, Post-Cure Duration, Flexural Properties
- Yıl: 2026
- Dil: İngilizce
- Üniversite: Gaziantep Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Konstrüksiyon ve İmalat Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET 3D BASKI KULLANARAK DÜŞÜK BASINÇLI ENJEKSİYON KALIBI ÜRETİMİNİN GELİŞTİRİLMESİ ÖZALP, Müslüm Yüksek Lisans Tezi, Makine Mühendisliği Danışman: Prof. Dr. Ömer EYERCİOĞLU Ağustos 2026 117 sayfa Düşük basınçlı enjeksiyon kalıplama (LPIM), prototip ve küçük ölçekli üretim için pratik bir yol sunmaktadır. Bu çalışma, yüksek sıcaklık reçinesinden üretilen maskeli stereolitografi (MSLA) 3 boyutlu baskı kalıp parçalarını, HDPE ve alümina (Al2O3) dolgulu hammaddenin LPIM'i için hızlı kalıplama aracı olarak incelemektedir. Faz 1'de, eğilme numuneleri ASTM D790 standardına göre dört farklı üretim yönünde (dikey, yatay ve iki 45° konfigürasyon) ve çeşitli UV son kürleme sürelerinde test edilmiştir. Sonuçlar, eğilme mukavemeti ve modülünün, 60 dakikaya kadar son kürleme süresiyle arttığını ve daha sonra plato oluşturduğunu göstermektedir; termal son kürleme daha da artış sağlamıştır; ve termal-basınç döngüsü 175-200 °C'lik bir çatlama eşiği ortaya koymuştur. Ayrıca, Faz 2'de üç farklı kalıp duvar kalınlığı (5, 10, 15 mm) için kalıp duvar kalınlığının kalıp hasar özellikleri üzerindeki etkisi araştırılmıştır. 10 mm duvar kalınlığına sahip alümina dolgulu hammadde için 14 dolum boyunca herhangi bir hasar gözlemlenmemiştir. HDPE ile, kalıp kullanım ömrü duvar kalınlığıyla birlikte keskin bir şekilde artarken, arıza yeri giriş bölgesinde sabit kalmıştır. 5 mm kalınlığındaki kalıp ilk dolumda parçalanırken, 10 mm'lik kalıp üç dolum içinde çatlamıştır. 15 mm'lik kalıp sekiz doluma dayanmıştır. Sonuçlar, MSLA baskılı yüksek sıcaklık reçine kalıplarının, son kürleme programı ve enjeksiyon sıcaklığı belirlenen çalışma aralığında kontrol edildiğinde, hızlı kalıplama olarak LPIM'i destekleyebileceğini göstermektedir.
Özet (Çeviri)
ABSTRACT DEVELOPING LOW PRESSURE INJECTION MOLD MANUFACTURING BY USING 3D PRINTING ÖZALP, Müslüm M.Sc. in Mechanical Engineering Supervisor: Prof. Dr. Ömer EYERCİOĞLU August 2026 117 pages Low pressure injection molding (LPIM) offers a practical route for prototype and small-batch manufacturing. This study investigates masked stereolithography (MSLA) 3D-printed mold inserts, fabricated from a high-temperature resin, as rapid tooling for LPIM of HDPE and an alumina (Al2O3)-filled feedstock. In Phase 1, flexural specimens were tested under ASTM D790 across four build orientations (vertical, horizontal, and two 45° configurations) and various UV post-cure durations. The results show that flexural strength and modulus increased with post-cure duration up to 60 minutes before plateauing; thermal post-cure gave a further increase; and thermal-pressure cycling found a 175-200 °C cracking threshold. Also, the effect of mold wall thickness on the mold damage characteristics is investigated in Phase 2 for three mold wall thicknesses (5, 10, 15 mm). No damage was observed for the alumina-filled feedstock across 14 shots for the 10 mm wall. With HDPE, mold service life rose sharply with wall thickness while the failure location stayed constant at the gate region. The 5 mm thick mold shattered on its first shot while the 10 mm mold cracked within three shots. The 15 mm mold survived eight shots. Results indicate that MSLA-printed high-temperature resin molds can support LPIM as rapid tooling when the post-cure schedule and injection temperature are controlled within the identified operating window.
Benzer Tezler
- Dokuma kumaşlarda örgü tipinin ham kumaşın boyutları ve geometrik özellikleri üzerindeki etkilerinin araştırılması
Başlık çevirisi yok
EMEL ÖNDER
Yüksek Lisans
Türkçe
1985
Tekstil ve Tekstil MühendisliğiEge ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
DOÇ. DR. GÜNGÖR BAŞER
- Düz atkı örme kumaşlarda ilmek eğikliğinin iplik özellikleri ile ilişkisi üzerine bir araştırma
Başlık çevirisi yok
FATMA ÇEKEN
Yüksek Lisans
Türkçe
1985
Tekstil ve Tekstil MühendisliğiEge ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
DOÇ. DR. GÜNGÖR BAŞER
- Çukurova bölgesinde biyoklimatik veriler kullanılarak açık ve yeşil alan sistemlerinin belirlenmesi ilkeleri üzerinde bir araştırma
A research on the determination of the principles in open and green spaces systems by using the bioclimatic data in Çukurova region
MEHMET FARUK ALTUNKASA
Doktora
Türkçe
1987
Çevre MühendisliğiÇukurova ÜniversitesiPeyzaj Mimarlığı Ana Bilim Dalı
DOÇ. DR. ERDOĞAN GÜLTEKİN
- Ülkemizdeki çeşitli büyüklükteki yerleşim merkezlerinde uygulanabilecek kültür yapısı planlama modeli
The Planning model of the cultural building which applicable at different size of settlement center
MUSTAFA İNCESAKAL
Yüksek Lisans
Türkçe
1986
Şehircilik ve Bölge PlanlamaGazi ÜniversitesiMimarlık Ana Bilim Dalı
DOÇ. DR. UMUR ERKMEN
- Antakya tarihi ticaret merkezi mekansal yapı değişim ve gelişim sürecinin kent ticaret merkezi planlamasına etkinliği
The Effectiveness of spatial structural chance and development period of the historical trade center of Antakya in the urban trade planning
NEVİN TURGUT
Yüksek Lisans
Türkçe
1986
Şehircilik ve Bölge PlanlamaGazi ÜniversitesiŞehir ve Bölge Planlama Ana Bilim Dalı
YRD. DOÇ. DR. NURCAN UYDAŞ