Effect of high volume natural pozzolan addition on the properties of pozzolanic cements
Yüksek hacimde doğal puzolan ilavesinin puzolanik çimentoların özelliklerine etkisi
- Tez No: 119013
- Danışmanlar: DR. LUTFULLAH TURANLI
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Portland Çimentosu, Doğal Puzolan, Katkılı Çimento, Öğütme, İncelik, Tane Boyutu Dağılımı, Normal Kıvam, Priz Süresi, Basınç Dayanımı, Alkali-Silis Reaksiyonu vı, Portland Cement, Natural Pozzolan, Blended Cement, Grinding, Fineness, Particle Size Distribution, Normal Consistency, Initial and Final Setting Times, Compressive Strength, Alkali-Silica Reaction IV
- Yıl: 2002
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 116
Özet
oz YÜKSEK HACİMDE DOĞAL PUZOLAN İLAVESİNİN PUZOLANİK ÇİMENTOLARIN ÖZELLİKLERİNE ETKİSİ UZAL, Burak Yüksek Lisans Tezi, İnşaat Müh. Bölümü Tez Yöneticisi: Dr. Lutfullah TURANLI Ocak 2002, 98 Sayfa Son yıllarda, yüksek oranda (%50 ve üzeri) uçucu kül içeren katkılı çimentoların fiziksel ve mekanik özelliklerinin araştırıldığı çalışmalar, bu tip çimentoların çok iyi fiziksel-mekanik özellikler ile dayanıklılık özelliğine sahip olduğunu göstermiştir. Bununla birlikte, puzolanik malzemelerin katkılı çimento üretiminde yüksek oranlarda kullanımı, klinker üretimi sırasında atmosfere verilen CO2 miktarını önemli ölçüde düşürerek çevresel bir avantaj sağlamaktadır. Bu çalışmada, yüksek oranda (%55) doğal puzolan ilavesinin puzolanik çimentoların özelliklerine etkisini tespit etmek için deneysel çalışmalar gerçekleştirilmiştir. Bu amaçla, bir tip portland çimentosu klinkeri ve farklı bölgelerden iki farklı doğal puzolan kullanılarak, 12 tip puzolanlı çimento süper akışkanlaştırıcılı ve süper akışkanlaştırıcısız olarak farklı öğütme süreleri ile laboratuvarda üretilmiştir. Süper akışkanlaştırıcılı çimentolar için toz haldeki süper akışkanlaştırıcı kimyasal katkı maddesi klinker, doğal puzolan ve alçı taşı ile birlikteöğütülmüştür. Ayrıca, kontrol numunesi olarak doğal puzolan katkısı kullanılmadan farklı inceliklerde iki portland çimentosu üretilmiştir. Hammaddelerin birlikte öğütülmesiyle elde edilen katkılı çimentolara ek olarak ayrı ve birlikte öğütmeyi karşılaştırmak amacıyla, portland çimentosu ile öğütülmüş doğal puzolanın kanştırılmasıyla 4 farklı katkılı çimento elde edilmiştir. Bununla birlikte öğütmenin doğal puzolanların incelik, su ihtiyacı ve dayanım aktiviteleri üzerindeki etkisi araştırılmıştır. Genel olarak, ağırlıkça %55 doğal puzolan içeren puzolanik çimentoların performansları belli öğütme süreleri için incelik, tane boyutu dağılımı, normal kıvam, priz süreleri, otoklav genleşmesi ve basınç dayanımı gibi fiziksel ve mekanik özellikler açısından karşılaştırılmıştır. Ayrıca bir dayanıklılık parametresi olarak, katkılı çimentoların alkali-silis reaksiyonu sonucunda oluşan genleşmelerin azaltılmasındaki etkinliği hızlandırılmış bir test metodu kullanılarak değerlendirilmiştir. Yüksek hacimde doğal puzolan ilavesi çimento harçlarının erken dayanımlarını önemli ölçüde azaltmıştır. Ancak 91 günlük değerler için basınç dayanımındaki düşüş çok azdır. Ayrıca % 55 doğal puzolan içeren katkılı çimentolar alkali-silis reaksiyonu açısından çok iyi dayanıklılık özelliği göstermiştir.
Özet (Çeviri)
ABSTRACT EFFECTS OF HIGH VOLUME NATURAL POZZOLAN ADDITION ON THE PROPERTIES OF POZZOLANIC CEMENTS UZAL, Burak M.S., Department of Civil Engineering Supervisor: Dr. Lutfullah TURANLI January 2002, 98 pages In recent years, scientific studies are carried out to investigate the physical- mechanical properties and durability characteristics of blended cements containing high volumes of fly ash (more than 50%). This type of blended cement has shown good mechanical properties and durability characteristics. Furthermore, the use of pozzolanic materials as addition in large proportions for cement production provides important environmental advantages such as low CO2 released into atmosphere during the clinker production. In this study, experimental work was carried out for the purpose of finding out the effect of high amount of natural pozzolan addition (55%) on the properties of pozzolanic cements. For this purpose, twelve types of blended cements with or without superplasticizer were produced with different grinding times in the laboratory by using one type of portland cement clinker and two natural pozzolans from different sources. The six types of the blended cements were produced as iiisuperplasticized by intergrinding the superplasticizer in a dry powder form together with clinker, natural pozzolans, and gypsum. Two types of portland cements were also produced with any addition of natural pozzolan but with different fineness values. In addition to blended cements obtained by intergrinding, four types of blended cements were also obtained by mixing the portland cement and ground natural pozzolans for comparison with intergrinding and separate grinding. Furthermore, it is investigated that the effect of the grinding on the fineness, water requirement and strength activity index of natural pozzolans. Generally speaking, the performance of the blended cements containing 55 percent natural pozzolans and portland cements were compared in terms of the physical and mechanical properties such as fineness and particle size distribution for a given grinding time, normal consistency, setting times, autoclave expansion and compressive strength of mortars. Also as a durability parameter, effectiveness of the blended cements in reducing the expansions due to alkali-silica reaction was evaluated by an accelerated test method. High volume pozzolan addition reduced the compressive strength of mortars significantly with respect to portland cements at early ages, however at 91 days of age the reduction in strength was very low. Furthermore the blended cements containing 55 percent natural pozzolan showed a superior durability characteristic in terms of the alkali-silica reaction.
Benzer Tezler
- Yüksek oranda doğal puzolan katkılı çimentoların hidratasyon, hamur içyapısı ve mekanik özellikleri üzerine nanotanecik ilavesinin etkisi
The effect of nanoparticle addition on hydration, paste microstructure and mechanical properties of cements added high volume natural pozzolan
SERHAN İLKENTAPAR
Doktora
Türkçe
2017
İnşaat MühendisliğiErciyes Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. CENGİZ DURAN ATİŞ
DOÇ. DR. BURAK UZAL
- Kendiliğinden yerleşen betonlarda ince malzemeve en büyük agrega boyutunun beton özelliklerineve agrega kenetlenmesine etkisi
The effects of fine material content and maximumaggregate size on concrete properties and aggregateinterlocking for self-compacting concrete
HAYATİ HİLMİOĞLU
Doktora
Türkçe
2022
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA HULUSİ ÖZKUL
- Doğal puzolan katkılı kireç bağlayıcının otoklavla kür koşullarının değerlendirilmesi
The evaluation of autoclave curing conditions of natural pozzolan blended lime binder
KÜBRA EKİZ BARIŞ
Yüksek Lisans
Türkçe
2016
Mimarlıkİstanbul Teknik ÜniversitesiMimarlık Ana Bilim Dalı
PROF. DR. LEYLA TANAÇAN
- Karma llif içeren çimento esaslı kompozitlerin mekanik davranışı - bir optimum tasarım
Mechanical behavior of cement based composites reinforced with hybrid fibres - an optimum design
ÖZGÜR EKİNCİOĞLU
Yüksek Lisans
Türkçe
2003
İnşaat Mühendisliğiİstanbul Teknik ÜniversitesiYapı Malzemesi Ana Bilim Dalı
DOÇ. DR. CANAN TAŞDEMİR
- Kalsiyum hidroksitin hidratasyon yoluyla aktivasyonu
Activation of calcium hydroxide by hydration
NİLÜFER ERDOĞAN
Yüksek Lisans
Türkçe
1997
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. AYŞEGÜL ERSOY (MERİÇBOYU)