Üç farklı dayanak materyalinin dinamik yükleme sonucunda implant-dayanak birleşiminde meydana gelen değişiklikler ve dayanıklılık yönünden incelenmesi
Comparison of changes in the implant-abutment interface after dynamic loading and strength of three different abutment materials
- Tez No: 124407
- Danışmanlar: PROF. DR. MEHMET AVCI
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental Implant, Dinamik Yükleme, Estetik Dayanak, Kırılma Dayanıklılığı, Dental Implant, Dynamic Loading, Esthetic Abutments, Fracture Strength
- Yıl: 2003
- Dil: Türkçe
- Üniversite: Hacettepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protez Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 134
Özet
ÖZET Yüzügüllü B., Üç Farklı Dayanak Materyalinin Dinamik Yükleme Sonucunda İmplant-Dayanak Birleşiminde Meydana Gelen Değişiklikler ve Dayanıklılık Yönünden İncelenmesi, Hacettepe Üniversitesi Sağlık Bilimleri Enstitüsü Protez (Diş) Programı Doktora Tezi, Ankara, 2003. Bu çalışmada dayanaklar, Brânemark implantlar üzerine Procera® yöntemi ile beşerli 3 grup halinde, alüminyum oksit, zirkonyum oksit ve titanyum kullanılarak hazırlanmış ve tüm örneklere yine Procera® yöntemi ile hazırlanan zirkonyum kopingler uygulanmıştır. İmplant-dayanak birleşimindeki mikroaralık ölçümleri, yükleme öncesinde scanning elektron mikroskobu (SEM) ile yapılmıştır. Her örnek, dinamik yükleme cihazında 30° eğim ile, sinüzoidal dalga formunda 20-200 N yük altında, 1 Hz frekans ile, 47250 devir dinamik yüklemeye tabi tutulmuştur. Yükleme tamamlandıktan sonra örneklerin implant-dayanak birleşimi mikroaralık ölçümleri yine SEM aracılığı ile yapılmıştır. Test örnekleri son olarak, dinamik yüklemede kullanılan düzeneklere aynı şekilde yerleştirilerek statik yük altında kırılma dayanıklılık testine tabi tutulmuştur. Elde edilen dinamik yükleme öncesi ve sonrası implant-dayanak birleşimi mikroaralık değerleri; grup içi ve gruplar arasında karşılaştırılmıştır. Bu karşılaştırmalar sonucunda istatistiksel olarak anlamlı bir fark bulunmamıştır (p>0.05). Kırılma dayanıklılık test verileri karşılaştırıldığında ise, dayanak-koping sistemleri arasında kırılma değerleri bakımından istatistiksel olarak anlamlı bir fark olmadığı saptanmıştır (p>0.05). Alüminyum oksit, zirkonyum oksit ve titanyum dayanakların kullanılmasının dayanıklılık açısından fark yaratmadığı saptanmıştır ancak dayanak grupları arasında başarısızlık şekilleri bakımından farklılıklar bulunduğu gözlenmiştir.
Özet (Çeviri)
ABSTRACT Yüzügüllü B., Comparison of Changes in the Implant-Abutment Interface After Dynamic Loading and Strength of Three Different Abutment Materials. Hacettepe University Health Sciences Institute PhD Thesis in Prosthodontics, Ankara, 2003. In this study, the abutments were manufactured by the Procera® system on Brânemark implants, three groups of five specimens each, using aluminum oxide, zirconium oxide and titanium. Zirconium copings were also manufactured by the Procera® system and placed on all specimens. The measurements of microgaps in the implant- abutment interface were made via scanning electrone microscope (SEM) analysis before dynamic loading. A mechanical testing machine applied 47250 cycles of 30° off-axis compressive cyclic sine wave load of 20 and 200 N at 1 Hz on a contact area on each specimen. After dynamic loading, the microgaps at the implant-abutment interface was measured once again via SEM analysis. Finally, using the same testing apparatus of dynamic loading conditions, a static load was applied on each specimen until fracture occured. The data obtained on microgap formation before and after dynamic loading was compared within- and between-groups. The comparisons revealed no statistically significant differences (p>0.05). In addition, there were no statistically significant differences when the fracture strength values of implant-abutment-coping systems were compared (p>0.05). Aluminum oxide, zirconium oxide and titanium abutments do not lead to differences on fracture strength values, however there were differences in fracture patterns between the abutment groups.
Benzer Tezler
- Dinamik yüklenen titanyum ve zirkonya implant dayanaklarının kantileverli sabit dental protezler altında kırılma dayanıklılıklarının değerlendirilmesi
Comparing the fracture resistance of zirconia and titanium abutments with cantilevered fdps after exposure to the artificial mouth
DUYGU KARASAN
Doktora
Türkçe
2014
Diş HekimliğiHacettepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. RAGİBE ŞENAY CANAY
- Arı sütü ve rosmarinik asitin yara iyileştirme potansiyelinin araştırılması
Investigation of wound healing potential of royal jelly and rosmarinic acid
YUNUS AKSÜT
Doktora
Türkçe
2024
Biyolojiİstanbul ÜniversitesiMoleküler Biyoloji ve Genetik Ana Bilim Dalı
PROF. DR. EMİNE ŞEKÜRE NAZLI ARDA
- Structural optimization of the UAV composite wing-box by adaptive genetic algorithm methods
İHA kompozit kanat kutusunun uyarlanabilir genetik algoritma yöntemleri ile yapısal optimizasyonu
BERK GÜNDÜZ
Yüksek Lisans
İngilizce
2024
Havacılık ve Uzay Mühendisliğiİstanbul Teknik ÜniversitesiSavunma Teknolojileri Ana Bilim Dalı
PROF. DR. ŞAFAK YILMAZ
- Farklı açıda üç farklı estetik dayanak materyalinin CAD/CAM sistemi ile üretilen kronlara bağlanma dayanımının değerlendirilmesi
Evaluation of bond strength of three different aesthetic abutment material with different angles to the crowns produced by CAD/CAM system
İREM SALGINCI
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş Hekimliğiİnönü ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ GÜLER YILDIRIM AVCU
- Vidasız konik kilit implant dayanak bağlantılı kısa implantlarda üst yapı materyalinin implant çevresi streslere etkisinin sonlu elemanlar analizi ile incelenmesi
Effect of different prosthetic materials on the stress distribution of self-locking taper short implants: A THREE-dimensional finite element analysis
BERK ESİN
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiMarmara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. RİFAT GÖZNELİ