Östemperlenmiş küresel grafitli dökme demirde östenit-martenzit dönüşümü
Austenite-martensite transformation on austempered ductile iron
- Tez No: 128767
- Danışmanlar: PROF. DR. NİHAT G. KINIKOĞLU
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Östemperleme, küresel grafıtli dökme demir, kalıntı östenit, martenzit, martenzitik dönüşüm. ıx, Küresel grafitli dökme demirler, Martensit, Martensitik dönüşüm, Ostemperleme, Östenit, Austempering, ductile iron, retained austenite, martensite, martensitic transformation, Nodular graphite cast irons, Austenite
- Yıl: 2002
- Dil: Türkçe
- Üniversite: Yıldız Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Malzeme Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Dökme demirler çok uzun süredir kullanılmakta olan ve üzerinde çok sayıda çalışma yapılan bir malzeme grubudur. Ancak östemperlenmiş küresel grafitli dökme demirlerin kullanımı nispeten yeni sayılır. 1970'lerden sonra bu konudaki araştırmalar yoğunlaşmış ve 1980'lerin sonlarına doğru kullanım alanı bulmuştur. Üstün özelliklerine rağmen bu malzeme ailesi yeterince iyi tanınmamaktadır ve özelliklerini geliştirmeye dair çalışmalar sürmektedir. Östemperleme sonucu yapıda kalan kalıntı östenit çeşitli şartlar altında kalıntı östenit martenzite dönüşebilmektedir. Parça yüzeyinin sertleşmesine yol açan bu dönüşüm bazı koşullarda avantajlı olmaktadır. Bu çalışmada, hangi koşullar altında Östenit-martenzit dönüşümünün oluştuğu araştırılmıştır. Deneysel çalışmalarda, östemperleme sonucu yapıda en çok miktarda kalıntı östenitin bırakılmıştır. Bunun nedeni kalıntı östenit miktarı ne kadar fazla olursa dönüşümün gözlemesinin o kadar kolay olacağıdır. Kalıntı östenit martenzit dönüşümünün en önemli noktası, malzemenin normal çalışma şartları altında bu dönüşümü göstermesidir. Bu da normal çalışma şartları altında dayanımı çalıştıkça artan bir malzemeyi işaret etmektedir. Bu araştırmada GGG60 malzemeden teker numuneler östemperlenmiş ve döner bir ezme cihazında ezilmiştir. Ezilme öncesi ve sonrası mikroyapı farklılıkları da metalografi, görüntü çözümleme ve x-ışını kırınımı araçlarıyla tespit edilmiştir.
Özet (Çeviri)
ABSTRACT Cast irons are a material group that is used in the industry for plenty of years and researched. But usage of austempered ductile cast irons is quite newer. Studies on this material family had increased after 1970's and found place in usage toward late 1980's. Superior properties are having attention in spite of short lasting researehes.This material family is not considered enough and studies for advancing properties are still going on. Retained austenite in the microstructure can be transformed to martensite in various conditions. This transformation resulting surface strengthening is advantageous in some circumstances. In this study, it is investigated how this transformation occurs. In practical studies, maximum amount of retained austenite was held in the structure. Because it is easier to investigate the transformation as the retained austenite percent increses. The key point of austenite martensite transformation is the occurance of this transformation under normal working conditions. And İt indicates a material that strengthens under normal working conditions. In this study, mini wheel specimens are austempered and then processed at a cyclic squash device. Microstructural differences before and after squashing are determined by the mean of metallography, image analyzing and x-ray diffraction tools.
Benzer Tezler
- Östemperlenmiş küresel grafitli dökme demirde alaşım elementlerinin östenit-martenzit dönüşümüne etkisi
The Effect of alloying elements on the austenite-marstensite transformation in austempered ductile iron
CEM AKÇA
Doktora
Türkçe
2006
Metalurji MühendisliğiYıldız Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. NİHAT KINIKOĞLU
- Mikroalaşımlı östemperlenmiş küresel grafitli dökme demirlerde vanadyum ve niyobyumun mekanik özelliklere etkisi
Effect of vanadium and niobium on mechanical properties in microalloyed austempered ductile iron
BEYZA METE DOĞAN
Yüksek Lisans
Türkçe
2024
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DR. NURİ SOLAK
- GGG 40-80 sınıfı küresel grafitli dökme demirlerde ostemperleme ısıl işleminin darbe direnci ve darbe geçiş sıcaklığına etkisinin incelenmesi
Investigation of the effect of Austempering heat treatment on the impact strenght and impact transition temperature in GGG 40-80 class ductile irons
AHMET ÖZEL
- Characterization of austempered ductile and vermicular graphite high simo and alsimo alloyed cast iron
Östemperlenmiş yüksek simo ve alsimo katkılı, küresel ve vermiküler grafitli dökme demirlerin karakterizasyonu
ALPER ÖZDEMİR
Yüksek Lisans
İngilizce
2016
Mühendislik Bilimleriİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
YRD. DOÇ. NURİ SOLAK
- Optimization of alloying and heat treatment process parameters of austempered ductile iron (ADI) castings
Östemperlenmiş küresel grafitli dökme demirlerde alaşımlama ve ısıl işlem parametrelerinin optimizasyonu
MUSTAFA ALP YALÇIN
Yüksek Lisans
İngilizce
2019
Metalurji MühendisliğiAtılım ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ KEMAL DAVUT