Fiber levha kompozitlerin fiziksel ve mekaniksel özelliklerinin polimerlerle iyileştirilmesi için alternatif yöntemler

Alternative methods for improving of mechanical and physical properties of fiber board with polymer

  1. Tez No: 131022
  2. Yazar: OĞUZHAN ÖZTÜRK
  3. Danışmanlar: PROF. DR. MENEMŞE GÜMÜŞDERELİOĞLU
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Wood polymer composites, water repellent, fiber board, methyl methacrylate
  7. Yıl: 2003
  8. Dil: Türkçe
  9. Üniversite: Hacettepe Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 92

Özet

FİBER LEVHA KOMPOZİTLERİN FİZİKSEL VE MEKANİK ÖZELLİKLERİNİN POLİMERLERLE İYİLEŞTİRİLMESİ İÇİN ALTERNATİF YÖNTEMLER Oğuzhan ÖZTÜRK Hacettepe Üniversitesi, Kimya Mühendisliği Bölümü, Kimya Mühendisliği Anabilim Dalı ÖZ Sunulan çalışmada termoset esaslı reçine (üre formaldehit reçinesi) kullanılarak hazırlanacak odun kompozitinin su alma eğilimi ve mekaniksel özelliklerindeki değişimin MMA (metil metakrilat) monomeri ilavesiyle ne yönde olacağının incelenmesi amaçlanmıştır. Çamsan A.Ş 'den temin edilen lifler kullanılarak, deneysel çalışmalar K.T.Ü Orman Fakültesi, Orman Endüstri Mühendisliği Bölümü laboratuvarlarında çalışmalar yapılmıştır, öncelikle levha üretiminin gerçekleştirilmesi amacıyla pres koşullarının optimizasyonuna çalışılmıştır. Yapılan denemeler neticesinde pres basıncının 28 kgf/cm2, pres sıcaklığının 160°C ve pres süresinin de 5,5-6,5 dakika aralığında olmasına karar verilmiştir. Pres koşullarının optimizasyonunun ardından liflere, kuru temelde hesaplanan lif miktarının % 12'si oranında UF (üre formaldehit) tutkalı ve kuru temelde hesaplanan lif ağırlığının % 0, 5, 15 ve 25'i oranlarında MMA monomerinin ilavesiyle farklı oranlarda MMA içeren levha üretimi gerçekleştirilmiştir. Üretilen levhalardan hazırlanan numunelerle eğilme direnci ve su alma testleri yapılmıştır. Yapılan testler sonucunda % 5 MMA içeren levhanın su alma eğiliminin azaldığı, eğilme direncinde ise artış olduğu gözlenmiştir. %15 ve %25 MMA ilave edilen levhaların su alma ve eğilme direnci değerlerinde ise istenilen değişimin sağlanamadığı belirlenmiştir. Bu durum MMA'nın hidrofobik karakterinden dolayı liflere püskürtülen üre formaldehit (UF) reçinesinin life homojen bir şekilde dağılamaması ve tutkalın lifin belli bölümlerinde kümeleşmesine yol açması sonucu levhanın fiziksel ve mekaniksel özelliklerini zayıflatması şeklinde açıklanmıştır. Çalışma kapsamında hazırlanan levha örneklerinin yüzey ve kesitlerinden alınan SEM (Taramalı Elektron Mikroskobu) fotoğrafları da bu düşünceyi doğrulamıştır. Yapılan çalışmayla endüstride yüksek kapasitelerde üretimi gerçekleştirilen odun termoset kompozitinin fiziksel ve mekaniksel özelliklerinin çevresel etkilere ve suya dayanımı yüksek olan MMA vinil monomeriyle daha da iyileştirilebileceği görülmüştür. Ancak çok daha iyi sonuçlar alınabilmesi için çalışmalar, bu araştırma sonucunda öngörülen koşullarda gerçekleştirilmelidir. Anahtar Kelimeler Odun polimer kompozitleri; su iticilik; lif levha; metil metakrilat Danışman: Prof. Dr. Menemşe GÜMÜŞDERELİOĞLU Hacettepe Üniversitesi, Kimya Mühendisliği Bölümü, Kimya Mühendisliği Anabilim Dalı

Özet (Çeviri)

ALTERNATING METHODS FOR IMPROVEMENT OF PHYSICAL & MECHANICAL PROPERTIES OF FIBER BOARD COMPOSITES WITH POLYMER Oğuzhan ÖZTÜRK Hacettepe Universty, Department of Chemical Engineering, Chemical Engineering Section ABSTRACT The aim of this study is to determine the change of water absorption and the mechanical properties of the thermoset resin (urea formaldehyde resin) bonded wood composite with the addition of MMA (methyl methacrylate) monomer. The experiments were carried out in the laboratory of Forest Faculty of the Karadeniz Technical University in Trabzon.Turkey. The wood fibers were provided by ÇAMSAN Wood Ind. and Trade Co. Prior to commencement of the experiments, several trials were done to get the optimum pres conditions. As a result, the following conditions were realized: 160 °C pres temperature, 28 kg/cm2 pres pressure and 5,5/6 minute pressing time. Second stage of the experiments was to prepare the fiber mats, which contain 12 percent solid resin (urea resin) based on dry fiber weight and MMA contents ranging from 0 percent to 25 percent. Fiber mats were pressed at the previously determined conditions. The water absorption and bend strenght values of the board samples were determined. Somewhat better result is obtained for the affected boards prepared with 5% MMA. Physical and mechanical properties of the boards were negatively affected by the higher MMA contents i.e (15 to 25 %). This result can be explained that, the hydrophobic characteristic of MMA monomer may cause the heterogeneous dispersion of urea formaldehyde resin on the fibers since of they are incompatible materials. Thus, this situation leads to the poor mechanical properties of composit. In this study, we consider that the physical and the mechanical properties of thermoset resin bonded wood composites that manufactured with high capacity could improve by addition of vinyl monomers because of their resistance to water and weather condiations. It was hoped that they would combine the tensile strenght of the lignocellulose fibers with the hardness, abrasion resistance and incompressibility of the polymeric materials.

Benzer Tezler

  1. Çeşitli elyaflarla takviye edilmiş termoplastik kompozitlerin levha ekstrüzyonunun ve özelliklerinin incelenmesi

    Sheet extrusion of various fiber reinforced thermoplastic composite and investigation of properties

    ÜMİT HÜNER

    Doktora

    Türkçe

    Türkçe

    2014

    Makine MühendisliğiTrakya Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. ERTUĞRUL SELÇUK ERDOĞAN

  2. Production of shield panels with polymer composites and investigation of mechanical properties

    Polimerik malzemelerden zırh plakası üretimi ve mekanik mukavemetlerinin incelenmesi

    EMİNE BAŞ

    Yüksek Lisans

    İngilizce

    İngilizce

    2012

    Kimya MühendisliğiMarmara Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. GÖKÇEN ALTUN ÇİFÇTİOĞLU

  3. Bazı selülozik esaslı sekonder lifsel hammaddeler katılarak üretilmiş alçı esaslı kompozitlerin teknolojik özelliklerinin araştırılması

    Investigation of the technological properties of gypsum composites produced from some cellulosic based secondary fiber sources

    İLKHAN DEMİR

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Ormancılık ve Orman MühendisliğiIsparta Uygulamalı Bilimler Üniversitesi

    Orman Endüstri Mühendisliği Ana Bilim Dalı

    PROF. DR. HALİL TURGUT ŞAHİN

  4. Doğal veya sentetik liflerle dokunmuş kumaşların güçlendirici olarak PP esaslı çok katmanlı odun plastik kompozit üretiminde kullanımı

    Use of fabrics woven with natural and synthetic fibers as reinforcers in the production of PP-based multi-layered wood plastic composite

    FURKAN KOCABAŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Ağaç İşleriKahramanmaraş Sütçü İmam Üniversitesi

    Orman Endüstri Mühendisliği Ana Bilim Dalı

    PROF. DR. FATİH MENGELOĞLU

  5. MDF tozu ve pirinç sapı atıklarının termoplastik kompozitlerin üretiminde değerlendirilmesi

    Evaluation of MDF dust and rice straw wastes in the thermoplastic composites production

    HALİME ACAR

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    Ağaç İşleriKahramanmaraş Sütçü İmam Üniversitesi

    Orman Endüstri Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. ERTUĞRUL ALTUNTAŞ

    PROF. DR. MEHMET HAKKI ALMA