Fiber optik kablo üretiminde MCVD sürecinin deneysel ve teorik olarak incelenmesi

Experimental and theoretical study of MCVD process in fiber optic cable production

  1. Tez No: 136710
  2. Yazar: ÜMİT YURDAGÜL
  3. Danışmanlar: YRD. DOÇ. DR. MUSTAFA BAYRAK
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2003
  8. Dil: Türkçe
  9. Üniversite: Niğde Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 64

Özet

ÖZET FİBER OPTİK KABLO ÜRETİMİNDE MCVD SÜRECİNİN DENEYSEL VE TEORİK OLARAK İNCELENMESİ YURDAGÜL, Ümit Niğde Üniversitesi Fen Bilimler Enstitüsü Makine Mühendisliği Anabilim Dalı Danışman : Yrd.Doc.Dr. Mustafa BAYRAK MCVD prosesinde bir quartz maddeden yapılmış tüp bir tornada döndürülerek bir Eb, O2 yakıcısı ile 1800°C'nin üzerine çıkılarak işlem yapılır. SİCI4 ve benzer biçimde GeCL; ve POCI3 yaklaşık 1300°C'de okside olurlar ve submikron düzeyinde silika ve diğer dopantlarm oksitlerini oluştururlar. Bu partiküller gaz dalgası içinde taşınırken termoforetik olarak gazdaki düşük sıcaklık bölgesine doğru hareket ederler. Partiküllerin takip ettiği yol bu nedenlerle termoforetik hız ve gaz hızına bağımlıdır. Daha soğuk çepere yeterince yalan olan partiküller depolanırlar. Reaksiyon bölgesi, partikülün izlediği yörüngesi ve kütle profili, yakıcı gibi hareketli değildir. Yakıcı, daha önceden depolanan“soot”üzerinde ilerler ve onu sinterleyerek 10-100 mikron kalınlığında gözeneksiz bir cam tabakaya dönüştürür. Yakıcının her seferinde farklı kimyasallar içeren çoklu geliş gidişleri substrat cam tüp içinde kontrollü kırılma indisi profiline sahip tabakalar oluşmasını sağlar. Depolamanın tamamlanmasının ardından tüpte kalan boşluk yüksek sıcaklıkta çöktürülerek yok edilir. Yapılan bu çalışmada, MCVD üretim tekniği teorik ve deneysel olarak incelenmiştir. Tüp yüzeyinde ölçülen sıcaklığın alevin ilerleme hızma ve tüpün dönme hızına bağlı olarak değişimi yapılan 9 adet deney ile ortaya konmuştur. Yapılan deneylerde alevin ilerleme hızının artmasıyla sıcaklığın düştüğü, rotasyon hızının değişimi ile sıcaklığın çok fazla değişimin olmadığı ancak küçük oranlarda arttığı görülmüştür. Anahtar Sözcükler : Fiber Optik, MCVD iii

Özet (Çeviri)

SUMMARY EXPERIMENTAL AND THEORETICAL STUDY OF MCVD PROCESS IN FIBER OPTIC CABLE PRODUCTION YURDAGUL, Umit Nigde University The Institute of Science Department of Mechanicel Engineering In MCVD process a quartz substrate tube is rotated on a lathe and heated up by H2 and O2 burner over 1800 °C. At the reaction zone SİCI4 and likely GeCU and POCI3 are being oxide approximately at 1300 °C and they create silica and other dopant's oxides at submicron level. When these particles are being carried in gas wave, thermophoretically they move to the lower temperature zone in the gas. With this reason, the route of the particulars is related with the termophoretic speed and gas speed, slightly closer particles are doped to the cold side. The reaction zone, the route of the particle and the mass profile are not mobile as the burner. The burner travels on the soot which is doped before and by sintering it creates a glass layer with no porous at a thickness of 10-100 microns. Each travel of the burner, which is consists different chemicals, provides layers, which has controlled index profiles inside the substrate glass tube. After the deposition is completed, the left inside the tube is removed by collapsing at high temperature. In this study, MCVD production method was researched according to theoretical and practical result. Temperature on the surface of the tube was measured according to burner flame and tube rotation speed in 9 experiment. In this experiment, temperature is decreased when the burner speed increased and it isn't changed as much as burner speed effect when the rotation speed changed but it is slightly increased. Key Words : Fiber Optic, MCVD iv

Benzer Tezler

  1. Tez No

    128228

    Fiber optik kablo üretim tekniklerinin incelenmesi

    Researching the fabrication techniques of optical fiber cables

    ADEM ÜKTE

    Yüksek Lisans

    Türkçe

    Türkçe

    2002

    Elektrik ve Elektronik MühendisliğiPamukkale Üniversitesi

    Elektrik-Elektronik Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MUSTAFA TEMİZ

  2. Tez No

    478634

    Fiber bragg ızgara sensör üretiminde farklı parametrelerin sensör tepkilerine ve karakteristiğine etkilerinin incelenmesi

    Investigation of effects of different parameters on the responses and characteristics of fiber bragg grating (FBG) sensors

    ÜMİT BAYRAM

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Mühendislik BilimleriBursa Teknik Üniversitesi

    İleri Teknolojiler Ana Bilim Dalı

    YRD. DOÇ. İSRAFİL KÜÇÜK

  3. Tez No

    874473

    MEMS sensor platform for vital monitoring under mri and intraocular pressure measurement

    Yaşamsal işaretlerin ve göz içi basıncın ölçülmesine yönelik MEMS basınç ölçer platformunun geliştirilmesi

    PARVIZ ZOLFAGHARI

    Doktora

    İngilizce

    İngilizce

    2023

    Elektrik ve Elektronik Mühendisliğiİstanbul Teknik Üniversitesi

    Elektronik ve Haberleşme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ONUR FERHANOĞLU

  4. Tez No

    39940

    Optik fiberlerde zayılama ve kayıplar

    The Atunoation and loues of the optical fibers

    SEMİH SALMAN

    Yüksek Lisans

    Türkçe

    Türkçe

    1995

    Elektrik ve Elektronik MühendisliğiSakarya Üniversitesi

    Y.DOÇ.DR. ETEM KÖKLÜKAYA

  5. Tez No

    201648

    Fiber optik kablo ile gigabit ethernet kartı tasarımı

    Design of gigabit ethernet card with optical fiber cable

    MUSTAFA BAHA BAYRAM

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve KontrolMarmara Üniversitesi

    Elektronik-Bilgisayar Eğitimi Ana Bilim Dalı

    YRD. DOÇ. DR. AYNUR AKAR

Geri Dön