Antioksidan katkıların magnezya-karbon refrakterlerin oksidasyon davranışlarına etkisi

Effect of the antioxidation behavior of the magnesia-carbon refractories

  1. Tez No: 142605
  2. Yazar: ALİ SERKAN GÖKÇE
  3. Danışmanlar: PROF. DR. SÜHEYLA AYDIN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2003
  8. Dil: Türkçe
  9. Üniversite: İstanbul Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Üretim Metalurjisi Bilim Dalı
  13. Sayfa Sayısı: 96

Özet

ANTIOKSIDAN KATKILARIN MAGNEZYA- KARBON REFRAKTERLERİN OKSİDASYON DAVRANIŞINA ETKİSİ ÖZET Demir-çelik endüstrisinde görülen teknolojik değişiklikler ve bunun sonucunda oluşan farklı servis şartlarını karşılayabilmek amacıyla oksit-grafit refrakter sistemleri geliştirilmiştir. Bunların içerisinde magnezya-karbon tuğlalar önemli bir yer tutmaktadır. Özellikle yüksek cüruf dirençleri, yüksek termal şok dirençleri, katransız ve ziftsiz bir çalışma temizliği sağlamaları nedeniyle reçine bağlı magnezya-karbon refrakterler geniş bir uygulama potansiyeli bulmuşlardır. Karbon olumlu özelliklere sahip olmasına karşın, yüksek sıcaklıklarda oksitlenmeye meyillidir. Karbonun ıslanma açısı çok yüksek olduğu için cüruf tarafından kolayca ıslatılamaz. Böylece cüruf yapıya nüfuz edemez. Ancak, yüksek sıcaklıklarda karbon oksitlenir. Böylece MgO-C yapısı bozulur ve cüruf, yapının içlerine doğru nüfuz eder. İşte bu sorunu gidermek için yapıya, antioksidan adı verilen, oksitlenmeye yatkınlığı yüksek olan metal ve bileşikler ilave edilir. Bu çalışmada, magnezya- karbon refrakterlerin yapısındaki karbonun oksidasyon davranışları incelenmiş ve antioksidan ilavelerinin oksidasyon üzerindeki koruyucu etkileri araştırılmıştır. Çalışmanın birinci bölümünde tuğla üretiminde kaliteyi kontrol eden parametrelerden olan porozite ve hacim ağırlığına farklı cins ve miktarlardaki antioksidan ilavelerin etkileri incelenmiştir. Yapılan çalışmalarda antioksidan ilavelerinin poroziteyi artırdığı, hacim ağırlığını ise düşürdüğü gözlenmiştir. Antioksidan ilavesinin bu olumsuz sonuçlara yol açmasının nedeni, antioksidanlar için Andreasen denklemi 'nin kullanılmamış olmasıdır. Çalışmanın ikinci bölümünde ise, farklı antioksidanların (Al, Si, SiC ve B4C), farklı süre ve sıcaklıklarda (1300°C ve 1500°C) MgO-C refrakterlerin oksidasyon davranışlarına etkileri incelenmiştir. Buna ilaveten, antioksidan miktarındaki artışın, MgO-C refrakterlerin oksitlenmelerine etkisi de araştırılmıştır. İlave edilen antioksidan miktarı arttığında tuğlanın oksidasyona karşı direnci de aynı ölçüde gelişmektedir. Çalışılan sıcaklıklarda sadece SiC'de miktar-etki ilişkisi doğru orantılı olarak artmamış, SiC miktarının artması, koruyucu etkiyi az miktarda etkilemiştir. 1300°C ve 1500°C'de en etkili antioksidanın B4C olduğu görülmüştür. Bu çalışmada, oksitlenmiş numunelerin poroziteleri de incelenmiştir. Oksitlenmiş numunelerin porozitelerinin yükseldiği, hacim ağırlıklarının ise düştüğü görülmüştür. Oksidasyon dayanımı yüksek olan numunelerin oksidasyondan sonraki poroziteleri, diğer numunelere göre daha düşük, hacim ağırlıkları ise daha yüksektir. xı

Özet (Çeviri)

EFFECT OF THE ANTIOXIDANTS ON THE OXIDATION BEHAVIOUR OF THE MAGNESIA-CARBON REFRACTORIES SUMMARY The oxide-graphite refractory systems were developed in order to meet the different manufacturing conditions as a result of the technological modifications in the iron and steelmaking industry. The magnesia-carbon refractories have an important place in these systems. The resin bonded magnesia-carbon refractories have a high usage potential because of their excellent slag resistance, good thermal shock resistance and good process conditions without tar and pitch. Despite the advantages of graphite, it is susceptible to oxidation in the high temperatures. Carbon can not be wetted by the slag easily because of the low wettability of graphite. Thus slag can not penetrate into the refractory. But carbon oxidizes in the high temperatures. So the structure of the MgO-C refractory is broken down and the slag penetrates into the refractory. Metals and compounds, so called antioxidants, which has tendency to oxidation are added to the refractories in order to overcome this problem. The oxidation behaviour of the carbon in the magnesia- carbon refractories and the protective behaviours of the antioxidants were investigated in this study. In the first stage of the study, the effects of the antioxidants on the porosity and bulk density as some of the parameters designating the quality at the manufacturing of bricks were investigated. In these studies, it was determined that the antioxidant additions increased apparent porosity and decrease bulk density of the refractories. The reason of these poor results is not applying Andreasen's equation for antioxidants. In the second stage of the study, the effects of the various antioxidants (Al, Si, SiC and B4C) on the oxidation behaviours of the MgO-C refractories at different temperatures (1300°C and 1500°C). Moreover, the effects of the quantities of the antioxidants on the oxidation of the MgO-C refractories were studied. Increasing the quantity of the antioxidants caused better oxidation resistance. But increasing SiC additives did not increase protective effect much at 1300°C and 1500°C. It was determined that B4C was the most effective antioxidant in these temperatures. In addition, the porosities of the oxidized bricks were investigated too. It was observed that the oxidized samples' porosities increased and bulk densities decreased. It was also determined that the antioxidants with better protective effects have lower porosities and higher bulk densities. Xll

Benzer Tezler

  1. Antioksidan katkıların bitümlü bağlayıcıların reolojik özellikleri ve yaşlanma davranışları üzerindeki etkisinin araştırılması

    Investigating characteristics of antioxidant modified bituminous binders and effect on aging behaviour

    OMAR MOHAMMED SHUHADEH ALQUDAH

    Doktora

    Türkçe

    Türkçe

    2016

    İnşaat MühendisliğiEge Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. PERVİZ AHMEDZADE

  2. Bazı doğal antioksidanların ve farklı pişirme koşullarının köftelerde heterosiklik aromatik amin oluşumu üzerine etkileri

    Effects of some natural antioxidants and different cooking conditions on the formation of heterocyclic aromatic amine in meatballs

    BEYZA ERDOĞAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    Gıda MühendisliğiEge Üniversitesi

    Gıda Bilimi ve Teknolojisi Ana Bilim Dalı

    DOÇ. DR. ÖZGÜL ÖZDESTAN OCAK

  3. Deniz marulundan (Ulva lactuca Linnaeus, 1753) elde edilen ekstraktların antimikrobiyal ve antioksidan etkilerinin incelenmesi

    Investigation of antimicrobial and antioxidant effects of extracts obtained from sea lettuce (Ulva lactuca Linnaeus, 1753)

    YASİN ORHAN

    Doktora

    Türkçe

    Türkçe

    2019

    Besin Hijyeni ve Teknolojisiİstanbul Üniversitesi

    Balıkçılık ve Su Ürünleri İşleme Teknolojisi Ana Bilim Dalı

    PROF. ÖZKAN ÖZDEN

  4. Bazı doğal katkıların buzdolabı koşullarında depolanan alabalık çorbasının raf ömrüne etkisi

    The effects of some natural additives on the shelf-life of trout soup stored at refrigerated conditions

    RECEP GÜZEL

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Balıkçılık TeknolojisiKaradeniz Teknik Üniversitesi

    Balıkçılık Teknolojisi Mühendisliği Ana Bilim Dalı

    PROF. DR. SEVİM KÖSE

  5. Investigation of the effects of nucleating agents on the mechanical behaviour of recycled polypropylene

    Çekirdeklendirici katkıların geri dönüştürülmüş polipropilenin mekanik davranışına etkisinin araştırılması

    BUKET ŞENTÜRK

    Yüksek Lisans

    İngilizce

    İngilizce

    2014

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. NURSELİ UYANIK

    DR. TOLGA GÖKKURT