Production and characterization of activated carbon from apricot stones

Kayısı çekirdeğinden aktif karbon üretimi ve karekterizasyonu

  1. Tez No: 153146
  2. Yazar: NEZİH URAL YAĞŞİ
  3. Danışmanlar: PROF. DR. HAYRETTİN YÜCEL
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Aktif Karbon, Kayısı Çekirdeği, Gözenek Yapısı, H3P04 Aktivasyonu vı, Activated Carbon, Apricot Stones, Pore Structure, H3P04 Activation IV
  7. Yıl: 2004
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 132

Özet

oz KAYISI ÇEKİRDEĞİNDEN AKTİF KARBON ÜRETİMİ VE KARAKTERİZASYONU Yağşi, Nezih Ural Yüksek Lisans, Kimya Mühendisliği Bölümü Danışman: Prof. Dr. Hayrettin YÜCEL Nisan 2004, 114 sayfa Bu çalışmada, kimyasal aktivasyon tekniği ile aktive edici madde olarak fosforik asit (H3P04) kullanılarak oldukça düşük sıcaklıklarda (300, 400 ve 500°C) kayısı çekirdeğinden üretilen aktif karbonun karakterizasyonu incelendi. Aktif karbon üretmek için asit emprenye edilmiş örnekler 20°C/dak. ısıtma hızıyla son karbonizasyon sıcaklığı olan 300°C, 400°C ve 500°C ye ısıtıldı. Her bir sıcaklık için dört farklı karbonizasyon zamanı (90, 120, 180 ve 210 dak.) kullanıldı. Sonuçta, oniki değişik aktif karbon bu yöntemle elde edildi.Aktif karbonların gözenek yapıları şöyle belirlendi: Gözenek çapları 8180- 50 nm arasında olan makrogözeneklerin hacmi ve yüzey alanı civa (intrusion) porozimetresi ile belirlendi. Mezogözenek (50-2nm arasındaki) yüzey alanları ve hacimleri -195. 6°C de N2 gaz adsorbsiyon tekniği kullanılarak belirlendi, BET yüzey alanları da 0.05-0.02 bağıl basınç aralığında aynı teknikle belirlendi. Yarıçapları 2 nm den küçük olan mikrogözeneklerin gözenek hacmi ve yüzey alanı 0°C de C02 adsorpsiyon ölçümleriyle Dubinin-Raduskhevic denkleminin kullanılmasıyla elde edildi. Oniki aktif karbonun yüzey alanları 444-709 m2/g değerleri aralığında bulunmuştur. Ürünlerin C02 (D-R) yüzey alanları 433-650 m2/g değerleri aralığında çıktığı saptanmıştır. Bu aktif karbonlar içinden maksimum BET ve C02 alanı değerleri sırasıyla 709m2/g ve 650m2/g olarak AC 4.2 örneğinden (karbonizasyon sıcaklığı 400°C ve karbonizasyon zamanı 120 dak.) bulundu. Aktif karbonların gözenek yapıları yüzde 10 civarında mezogözenekler ve yüzde 90'ın üzerinde mikrogözeneklerden oluşuyor. IM2 adsorpsiyon izotermleri de gözeneklerin mikrogözenek aralığında olduğunu kanıtlıyor.

Özet (Çeviri)

ABSTRACT PRODUCTION AND CHARACTERIZATION OF ACTIVATED CARBON FROM APRICOT STONES Yağşi, Nezih Ural M.Sc. Department of Chemical Engineering Supervisor: Prof. Dr. Hayrettin YÜCEL April 2004, 114 pages In this study, characterization of activated carbon produced from apricot stones by chemical activation technique using phosphoric acid (H3P04) as activating agent, at relatively low temperatures (300, 400 and 500°C), was investigated. To produce activated carbon acid impregnated samples were heated; at a heating rate of 20°C/min to the final carbonization temperatures, 300°C, 400°C and 500°C. For each temperature four different carbonization time (90, 120, 180 and 210 min.) were used to produce twelve different activated carbons. mThe pore structures of activated carbons were determined as follows: The volume and area of macropores in the pore diameter range of 8180-50 nm were determined by mercury intrusion porosimetry. Mesopore (in the range of 50-2 nm) areas and volumes were determined by N2 gas adsorption technique at - 195. 6°C, BET surface areas of the samples were also determined, in the relative pressure range of 0.05 to 0.02, by the same technique. The pore volume and the area of the micropores with diameters less than 2 nm were determined by C02 adsorption measurements at 0°C by the application of Dubinin Radushkevich equation. N2 (BET) and C02 (D-R) surface areas of the samples were in the range of 444-709m2/g and 433-650m2/g, respectively. AC4.2 sample (carbonization temperature of 400°C and carbonization time of 120 min.) was found to have the maximum BET and C02 area as 709m2/g and 650m2/g, respectively. Surface areas of the samples consisting of around 10% mesopores and over 90% micropores. N2 adsorption isotherms also confirm that pores are in the micropore range.

Benzer Tezler

  1. Tez No

    246951

    Fındık kabuklarından aktif karbon elde edilmesi ve karakterizasyonu

    Production of activated carbons from hazelnut shell and its characterization

    NİHAL ŞEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2009

    Kimya MühendisliğiFırat Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. AHMET ÖZER

  2. Tez No

    83908

    Fosforik asitle aktifleştirilen şeker pancarı küspesinden aktif karbon elde edilmesi, karakterizasyonu ve Pb(11) iyonlarının adsorpsiyonunda kullanılması

    Production of activated carbons from sugar beet pulp impregenated with phosphoric acid, its characterization and use in adsorpstion of Pb(11) ions

    GÜLÜFER ÇAM

    Yüksek Lisans

    Türkçe

    Türkçe

    1999

    Kimya MühendisliğiFırat Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    DOÇ. DR. AHMET ÖZER

  3. Tez No

    56875

    Effect of activation degree on the pore size distribution and mechanical strength of activated carbons of apricot stone origion

    Kayısı çekirdeklerinden üretilen aktif karbonlarda aktifleştirme derecesinin gözenek boyutu dağılımı ve mekanik da yanım üzerindeki etkisi

    MEHMET FATİH ÖZBAYOĞLU

    Yüksek Lisans

    İngilizce

    İngilizce

    1996

    Maden Mühendisliği ve MadencilikOrta Doğu Teknik Üniversitesi

    Maden Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ALİ İHASAN AROL

  4. Tez No

    83941

    Şeker pancarı küspesinden aktif karbon elde edilmesi ve karakterizasyonu ve Cu(II) iyonlarının adsorpsiyonunda kullanılması

    Production of activated carbon from sugar beet pulp, its characterisation and use in adsorption of Cu(II) ions

    MUHAMMET ŞABAN TANYILDIZI

    Yüksek Lisans

    Türkçe

    Türkçe

    1999

    Kimya MühendisliğiFırat Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. AHMET ÖZER

  5. Tez No

    865213

    Atıkların yüksek sıcaklıkta sürekli pirolizi için yarı-pilot ölçek yeni bir vidalı reaktör geliştirilmesi

    Development of a new semi-pilot scale screw reactor for continuous pyrolysis of wastes at high temperature

    ANIL ÜNSAÇ

    Doktora

    Türkçe

    Türkçe

    2024

    Enerjiİstanbul Teknik Üniversitesi

    Enerji Bilim ve Teknoloji Ana Bilim Dalı

    PROF. DR. NİLGÜN YAVUZ

    PROF. DR. HASAN CAN OKUTAN

Geri Dön