Microstructural characterization of hypoeutectoid steels quenched from the Ae1-Ae3 intercritical temperature range by magnetic barkhausen noise technique
Ae1-Ae3 kritik sıcaklık aralığından su verilen ötektoid-altı çeliklerde manyetik barkhausen gürültüsü tekniği ile mikroyapı karakterizasyonu
- Tez No: 172243
- Danışmanlar: DOÇ.DR. HAKAN GÜR
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Ötektoid-altı Çelik, Ferrit, Martensit, Mikroyapı, Manyetik Barkhausen Gürültüsü, Hypoeutectoid Steel, Ferrite, Martensite, Microstructure, Magnetic Barkhausen Noise iv
- Yıl: 2006
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Bölümü
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 78
Özet
ÖZ Aei - Ae3 KRİTİK SICAKLIK ARALIĞINDAN SU VERİLEN ÖTEKTOİD-ALTI ÇELİKLERDE MANYETİK BARKHAUSEN GÜRÜLTÜSÜ TEKNİĞİ İLE MİKROYAPI KARAKTERİZASYONU Boyacıoğlu, Beril Yüksek Lisans, Metalürji ve Malzeme Mühendisliği Bölümü Tez Yöneticisi: Doç. Dr. C. Hakan Gür Ocak 2006, 66 Sayfa Bu tezin amacı Manyetik Barkhausen Gürültüsü (MBG) tekniğinin Ad - Ae3 kritik sıcaklık aralığından su verilen ötektoid-altı çeliklerin ferritik-martensitik iç yapılarının karakterizasyonu için kullanılabilme olasılığını incelemektir. Bu amaçla, SAE 1020, 1040 ve 1060 çeliklerinden dikdörtgen numuneler hazırlandı. Bu numuneler, Aei - Ae3 kritik sıcaklık aralığında farklı sıcaklıklarda ısıtıldıktan sonra su verildi. Numunelerin iç yapılan metalografik incelemeler ve sertlik ölçümleriyle karakterize edildi. MBG ölçümleri hem Rollscan hem de uSCAN üniteleri kullanılarak yapıldı. Aynı karbon oranına sahip numunelerde, ısıtılma sıcaklığı arttıkça Barkhausen emisyonunun düştüğü gözlendi. Ayrıca, aynı sıcaklıkta ısıtılan numunelerde, numunenin karbon oram arttıkça, Barkhausen emisyonu azaldı. Elde edilen sonuçlar MBG'nün sertlikle ters orantılı olduğunu ve malzemenin mikroyapısına oldukça duyarlı olduğunu gösterdi. Bu çalışma, MBG tekniğinin Aeı - Ae3 kritik sıcaklık aralığından su verilen ötektoid-altı çeliklerin mikroyapılarını değerlendirmek için uygun bir yöntem olduğunu göstermiştir. Bu teknik, özellikle otomotiv endüstrisinde kullanılan çift fazlı çeliklerin karakterizasyonu için de kullanılabilir.
Özet (Çeviri)
ABSTRACT MICROSTRUCTURAL CHARACTERIZATION OF HYPOEUTECTOID STEELS QUENCHED FROM THE Aei - Ae3 INTERCRITICAL TEMPERATURE RANGE BY MAGNETIC BARKHAUSEN NOISE TECHNIQUE Boyacıoğlu, Beril M.S., Department of Metallurgical and Materials Engineering Supervisor: Assoc Prof. Dr. C. Hakan Gür January 2006, 66 pages This thesis aims to examine the possibility of using Magnetic Barkhausen Noise technique in characterizing the ferritic-martensitic microstructure of hypoeutectoid steels quenched from the intercritical temperature range. For this purpose, rectangular specimens were prepared from SAE 1020, 1040 and 1060 steels. The specimens were heated at different temperatures within the intercritical temperature range and then quenched into water. Microstructures of the specimens were characterized by metallographic examinations and hardness measurements. The measurements of the Magnetic Barkhausen Noise (MBN) were performed by using both Rollscan and uSCAN sensor connectors. It was seen that, for specimens having identical carbon content, Barkhausen emission decreased as the heating temperature increased. Moreover, in specimens heated at the same temperature, Barkhausen emission decreased as the carbon content of the specimen increased. In both cases, the decrease in Barkhausen emission is associated with the increase in martensite content. The results indicate that MBN is inversely proportional to hardness and that MBN is very sensitive to the microstructural condition of the material. It has been shown that using MBN is a powerful tool for evaluating the microstructure of hypoeutectoid steels quenched from the intercritical temperature range and that the use of this technique could be extended to characterize industrial dual phase steels.
Benzer Tezler
- Östemperlenmiş gri dökme demirin yüksek sıcaklık aşınma davranışının incelenmesi
Investigation of wear behaviour of austempered gray cast iron at elevated temperature
ALİ ULAŞ MALCIOĞLU
Yüksek Lisans
Türkçe
2015
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. MURAT BAYDOĞAN
- Geleneksel döküm ve hızlı katılaştırma yöntemleri ile üretilen Al- 8Si -5.1Cu ve Al-20Si-5.1Cu alaşımlarının mikroyapısal karakterizasyonu
Microstructural characterization of ternary Al-8Si-5.1Cu and Al-20Si-5.1Cu alloys produced by convenional casting and rapid solidification techniques
TANER LİLA
Yüksek Lisans
Türkçe
2001
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiPROF. DR. M. LÜTFİ ÖVEÇOĞLU
- Hızlı katılaşmış ötektikaltı Al.Si.Cu alaşımlarının karakterizasyonu
Characterization of rapidly solidified hypo-eutectic Al.Si.Cu. alloys
OSMAN SERDAR ATAFIRAT
Yüksek Lisans
Türkçe
2001
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. NİYAZİ ERUSLU
- Alüminyum-silisyum alaşımlarının ve alçak basınçlı döküm prosesinin simülasyon destekli tasarımı
Simulation assisted design of aluminum-silicon alloys and low pressure die casting process
TUĞÇE YAĞCI
Doktora
Türkçe
2021
Metalurji MühendisliğiDokuz Eylül ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ÜMİT CÖCEN
PROF. DR. OSMAN ÇULHA
- Al-si alaşımlarında stronsiyum modifikasyonu ile döküm kalitesi arasındaki ilişkinin karakterizasyonu
Characterisation of relation between strontium modification and casting quality in al-si alloys
İNAL KAAN DUYGUN
Yüksek Lisans
Türkçe
2017
Metalurji Mühendisliğiİstanbul ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. DERYA DIŞPINAR