Polimer elektrolit yakıt hücreleri için nano-boyutlu elektro-katalizör sentezi ve karekterizasyonu
Synthesis of nano particle sized electro-catalyst for polymer electrolyte fuel cells and characterization
- Tez No: 179249
- Danışmanlar: YRD. DOÇ. DR. HASAN SADIKOĞLU
- Tez Türü: Yüksek Lisans
- Konular: Kimya Mühendisliği, Chemical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2008
- Dil: Türkçe
- Üniversite: Gebze Yüksek Teknoloji Enstitüsü
- Enstitü: Mühendislik ve Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 136
Özet
Hidrojen enerji çevriminin en önemli unsuru şüphesiz hidrojeni elektrokimyasal yöntemle elektriğe dönüştüren Yakıt Pilleridir. Yakıt pillerinde pahalı platin ve zar kullanımından kaynaklanan maliyet unsurları yaygın kullanımda en önemli engellerdir. Elektro-katalizörlerde katalitik aktiviteyi artırmak ve pahalı olan platini daha az ve etkin kullanmak için, geniş yüzey alanına sahip iletken destekler üzerine platin küçük parçacıklar halinde homojen bir şekilde dağıtılır. Karbon destekli platinin geniş bir yüzey alanına sahip olması daha yüksek bir katalitik aktivite göstermesini sağlamakta, ayrıca platin parçacıklarının büyüklüğü, oksijen indirgenme kinetiği üzerinde önemli rol oynamaktadır.Bu tezde, PEM (Polimer Elektrolit Membran) tipi yakıt hücrelerinde kullanılan karbon destekli Pt temelli katalizörlerden farklı oranlarda Pt/C, PtCo/C ve PtRu/C katalizörlerinin mikrodalga destekli ve konveksiyonel ısıtmalı polyol metotlarına göre sentezi ile ilgili bir çalışma yapılmıştır. Katalizörlerin elektrokimyasal yüzey alanları (EYA) 0,5 M H2SO4 ve 0,1 M HClO4 elektrolitler içersinde, oda sıcaklığında ve 20 mV/s ve 100 mV/s tarama hızlarında yapılan döngüsel voltametri ölçümleriyle ve yine 20 mV/s ve 100 mV/s tarama hızlarında oksijen indirgenme aktiflikleri 0-2500 rpm aralığında farklı döndürme hızlarında tespit edilmiştir. TEM (Tranmisyon Elektron Mikroskopu) analiziyle tanecik boyutu ve dağılımı, EDX (Energy Dispersive X-ray) analiziyle de kalitatif olarak katalizör bileşenleri belirlenmiştir. Ayrıca sentezlenen katalizörler X-ışınları Kırınım (XRD) Cihazıyla 40 kV ve 30mA'de bir CuK? kaynağı kullanılarak analiz edilmiş, XRD grafiği 2? açısının 200 ile 700 aralığında dakikada 20 tarama hızıyla elde edilmiştir. Bu sayede metal kristal boyutu ve metal lattice parametreleri (alaşım derecesi) tayin edilmek istenmiş ancak taneciklerin nano boyutlu olması dolayısıyla tam bir kristal yapı görülememiş yani katalizörler için istenen amorf bir yapı gözlenmiştir.
Özet (Çeviri)
The most significant element of the hydrogen cycle is undoubtedly fuel cells converting hydrogen to electrical energy via electrochemical method. The most important handicap is economic consideration stemming from expensive platinum and membrane usage in fuel cells. To increase catalytic activity in electro catalysts and use expensive platinum in a small amount and effective way, platinum is dispersed uniformly onto conductive supports having large contact area in the form of small size. Carbon supported platinum having large area provide high catalytic activity and also the size of the platinum particle has a vital role in the kinetics of the oxygen reduction.In this thesis, A study related with the synthesis of Pt/C, PtCo/C and PtRu/C catalysts from carbon supported platinum catalysts used in polymer electrolyte fuel cells in different proportions by microwave support and convection heating poliol method was done. The electrochemical surface areas of the catalysts were found under the condition of 0,5 M H2SO4, 0,1 M HClO4 electrolytes, room temperature, by cyclic voltammetric measurements in 20 mV/s and 100 mV/s scanning velocities. In addition to this, oxygen reduction activities in 20 mV/s and 100 mV/s and different rotations between 0-2500 rpm were found. Particle size and distribution via TEM(Transmission Electron microscope) and catalyst components as qualitative via EDX(Energy Dispersive X-ray) were determined. Additionally, synthesized catalysts were analysed by X-ray diffraction (XRD) device by using CuK? source in 40 kV and 30mA, XRD graph was obtained by 20 scanning per minute velocity between 200 and 700 of 2? angle. Thus, metal crystal size and metal lattice parameters (alloying degree) were wanted to be determined, however exact crystal structure was not seen due to the fact that particles are in nano size. Therefore, amorphous structure which is must for catalyst was observed.
Benzer Tezler
- Investigation of rotating ring disk electrode (RRDE) studies on nano-sized cathode catalysts for PEM fuel cells
PEM yakıt hücrelerine yönelik nano boyutlu katot katalizörlerinde döner halka disk elektrot çalışmalarının incelenmesi
NİHAT EGE ŞAHİN
Yüksek Lisans
İngilizce
2013
Kimyaİstanbul Teknik ÜniversitesiNanobilim ve Nanomühendislik Ana Bilim Dalı
PROF. DR. FİGEN KADIRGAN
- Investigation of polymer electrolyte membrane (PEM) fuel cell and investigation of usage areas in Turkey
Polimer elektrolit membran (PEM) yakıt pilinin araştırılıması ve Türkiye'deki kullanım alanlarının incelenmesi
BENJAMIN AYIM-OTU
Yüksek Lisans
İngilizce
2021
Elektrik ve Elektronik MühendisliğiSiirt ÜniversitesiElektrik-Elektronik Mühendisliği Ana Bilim Dalı
DOÇ. DR. MELİH KUNCAN
PROF. DR. ÖMER ŞAHİN
- Nano boyutlu modifiye katalizörler üzerinde alkollerin elektrooksidasyonu
Electrooxidation of alcohols on nanosized modified catalysts
MÜGE CİVELEKOĞLU ODABAŞ
- Synthesis and characterization of various tungsten carbide powders from tungsten hexachloride powders via mechanochemical reaction and autoclave/pressure vessel methods
Mekanokimyasal reaksiyon ve otoklav/basınçlı kap metodlarıyla tungsten hekzaklorür tozundan çeşitli tungsten karbür tozlarının sentezi ve karakterizasyonu
NİHAN ÖZKAN AYTEKİN
Doktora
İngilizce
2020
Mühendislik Bilimleriİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA LUTFİ ÖVEÇOĞLU
- Development of multi-layer conductive polymer nanocomposites for electromagnetic shielding application
Elektromanyetik kalkanlama uygulamaları için katmanlı iletken polimer nano kompozitlerinin geliştirilmesi
FATMA ZEHRA ENGİN SAĞIRLI
Doktora
İngilizce
2017
Bilim ve Teknolojiİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. EYÜP SABRİ KAYALI
PROF. DR. ABDÜLKADİR SEZAİ SARAÇ