Hızlı katılaştırılmış al-%12si-%xsb (x=0.5, 1.0)alaşımlarının mekanik özelliklerinin dinamik mikrosertlik tekniği ile incelenmesi

The Investigation of micro mechanical properties of rapidly solidified al-%12si-%xsb (x=0.5, 1.0)alloys by dynamic microhardness technique

PDF İndir

  1. Tez No: 182018
  2. Yazar: MUHAMMED FATİH KILIÇASLAN
  3. Danışmanlar: DOÇ.DR. ORHAN UZUN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Fizik ve Fizik Mühendisliği, Metalurji Mühendisliği, Physics and Physics Engineering, Metallurgical Engineering
  6. Anahtar Kelimeler: Hızlı katılaştırma, Eriyik eğirme tekniği, Al-Si alaşımları, Mekaniközellikler, Derinlik duyarlı çentme, Çentik boyutu etkisi (ISE), Rapid solidification, Melt-spinning technique, Al-Si alloys, Mechanicalproperties, Depth-sensing indentation
  7. Yıl: 2006
  8. Dil: Türkçe
  9. Üniversite: Gaziosmanpaşa Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Fizik Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 90

Özet

Bu çalışmada, hızlı katılaştırılmış Al-%12Si-0.5Sb ve Al-12%Si-1.0Sbalaşımları eriyik eğirme yöntemi ile üretildi. Hem Al-12%Si-0.5Sb ve hem de Al-12%Si-1.0Sb alaşımı önce 20m/s sonra da 40 m/s disk devir hızında katılaştırıldı. Eldeedilen numunelerin mikroyapısına ve mekaniközelliklerine disk hızının ve bileşimdekiSb katkısının etkisi optik mikroskop altında incelendi. Soğuma hızındaki artışnumunelerin daha iyi mikromekanik özelliklere sahip olmasını sağlayarak daha ince vehomojen bir mikroyapı oluşumuna neden oldu. Çentme deneylerinde, Vickers uçludinamik mikrosertlik (derinlik duyarlı çentme) cihazı (Shimadzu, DUH-W201S)kullanıldı. Bütün testler oda sıcaklığında ve her numune için aynı şartlar altında yapıldı.Mikrosertlik verilerini analiz etmek için Meyer Kanunu ve Geliştirilmiş OrantılıNumune Direnci (MPSR) modeli kullanıldı. Elde edilen sonuçlarda bütün numunelerindisk yüzeylerinin hava yüzeylerine kıyasla daha sert oldukları görüldü. Ağırlıkça%0.5Sb katkılı numunelerin %1.0Sb katkılı numunelere göre daha sert oldukları tespitedildi. Ayrıca 40 m/s disk devir hızında katılaştırılan numunelerin sertlik değerlerinin,20 m/s disk devir hızında katılaştırılan numunelerin sertlik değerlerinden daha yüksekolduğu da tespit edildi.

Özet (Çeviri)

In this study, Al-Si-Sb alloys with nominal composition Al-12wt%Si-0.5wt%Sb and Al-12wt%Si-1.0wt%Sb were rapidly solidified by using melt-spinning technique at surfacevelocities first 20 m/s and then 40 m/s in order to examine the influence of coolingrate/conditions and Sb concentration on microstructure and micromechanical properties. Themicrostructure of the rapidly solidified ribbons was investigated by optical microscopy. It wasseen that increasing of the solidification rate results in finer and more homogeneousmicrostructure which implies better micromechanical properties. In the indentationexperiments, a Vickers indenter was used in a dynamic ultra microhardness (depth sensingindentation) tester (Shimadzu, DUH-W201S). All tests were carried out at room temperature.All tests were performed under same operating conditions. The Meyer?s Law and ModifiedProportional Specimen Resistance (MPSR) model were used to analyze the microhardnessbehavior. The results showed that disc sides of the all ribbons have higher hardness valuesthan the air sides. Besides, it was found that the specimens with 0.5Sb composition are harderthan those with 1.0Sb concentration. Additionally, micromechanical characterization resultsrevealed that the melt spun alloys prepared at 40 m/s surface velocity have higher harnessvalues than those of the ribbons with 20 m/s surface velocity for both Sb additions.

Benzer Tezler

  1. Tez No

    179620

    Nanokristal Al-Si-Sb alaşımlarının enerji yaklaşımı ile mikromekanik karakterizasyonu

    Micromechanical characterization of nanocrystalline Al-Si-Sb alloys by work of indentation approach

    FİKRET YILMAZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2008

    Fizik ve Fizik MühendisliğiGaziosmanpaşa Üniversitesi

    Fizik Ana Bilim Dalı

    DOÇ. DR. ORHAN UZUN

  2. Tez No

    397963

    Al12Si matrisli SiCp takviyeli kompozit kaplamaların soğuk gaz dinamik püskürtme yöntemi ile üretilmesi ve sulu ortamdaki tribolojik davranışının incelenmesi

    Production of Al12Si matrix with SiCp reinforced composite coatings by cold gas dynamic spray coating method and investigation of tribological behaviour of the coatings in water

    ÖZDE DEPREM

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. HÜSEYİN ÇİMENOĞLU

  3. Tez No

    77220

    Hızlı katılaştırılmış Al-%(2,5-5-7,5) Mg alaşımlarının üretilmesi ve üretilen numunelerin yapı, fiziksel, elektriksel ve mekanik özelliklerinin incelenmesi

    Production of rapidly solidfied Al-(2,5-5-7,5)wt0/0Mg alloys and investigation of structure, physical, electrical and mechanic properties of produced samples

    TUNCAY KARAASLAN

    Doktora

    Türkçe

    Türkçe

    1998

    Fizik ve Fizik MühendisliğiErciyes Üniversitesi

    Fizik Ana Bilim Dalı

    PROF. DR. MUSTAFA KESKİN

  4. Tez No

    651619

    Hızlı katılaştırılmış Al-7075 alaşımının mikroyapı ve mekanik özelliklerine Nb katkısının etkileri

    Effects of Nb addition on the microstructure and mechanical properties of rapidly solidified Al-7075 alloy

    ADEM KUPÇAK

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    Metalurji MühendisliğiKastamonu Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MUHAMMED FATİH KILIÇASLAN

  5. Tez No

    859530

    Hızlı katılaştırılmış Al-esaslı alaşımlarının özelliklerinin incelenmesi

    Investigation of the properties of fast solidized Al-based alloys

    AHMET SARSICI

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Elektrik ve Elektronik MühendisliğiKayseri Üniversitesi

    Elektrik-Elektronik Mühendisliği Ana Bilim Dalı

    PROF. DR. ERCAN KARAKÖSE

Geri Dön