Metal lif takviyeli pamuk ipliklerinden üretilmiş örme kumaşların mekanik ve termal özelliklerinin incelenmesi
Investigation of mechanical and thermal properties of fabrics knitted with cotton yarn containing metal fibre
- Tez No: 201589
- Danışmanlar: YRD. DOÇ. DR. İSMAİL USTA
- Tez Türü: Yüksek Lisans
- Konular: Tekstil ve Tekstil Mühendisliği, Textile and Textile Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2007
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Tekstil Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Metalik iplikler, fantezi iplikler ve metal lif içeren iplikler olarak iki gruba ayrılmaktadır. İlk zamanlarda fantezi iplikler altın, gümüş gibi gerçek metallerden üretilmekteydi. Bu iplikler artık metalik boyalı sentetik ipliklerden üretilmektedir. Günümüzde de metal takviyeli iplikler, diğer geleneksel ipliklerle birlikte metal liflerden üretilmektedir. Yapılan çalışmanın amacı, metal lif takviyeli pamuk ipliklerinden örülmüş kumaşların mekanik ve termal özelliklerinin araştırılmasıdır. Çalışmanın deneysel kısmında, çekirdek malzeme olarak 0.035 mm paslanmaz çelik tel kullanılmıştır. Manto malzeme ise, %100 pamuk fitilidir. Modifiye edilmiş ring iplik makinesinde kompleks çekirdek iplik üretilmiştir. Eğirme sürecinde, metal tel ön silindirden beslenmiş ve kompleks çekirdek ile eğirmek için çekilmiştir. Kılavuz aygıt, metal telin eğirme istikrarını arttırmak için silindir basınç kolu üzerine yerleştirilmiştir. Ayrıca, %100 pamuk iplikleri de aynı makinede modifiye edilmeden üretilmiştir. Bu iki türden ipliklerin örülmesinde, çorap örme makinesi kullanılmıştır. Üretilen iplikler üzerinde düzgünsüzlük, mukavemet, uzama ve tüylülük testleri, kumaşlar üzerinde de gramaj, kalınlık, sürtünme, boncuklanma ve ısı iletim testleri yapılmıştır. Kompleks çekirdek iplikler üzerinde düzgünsüzlük testi yapılamamıştır. Kompleks çekirdek ipliklerin mukavemetleri, %100 pamuk ipliklerinden düşük olarak ölçülmüştür. Kompleks çekirdek ipliklerin uzama değerleri, yüksek uzama değerine sahip paslanmaz çelik filament içerdiğinden, %100 pamuk ipliklerinden yüksek bulunmuştur. Çekirdek ipliklerin iplik tüylülük değerleri, %100 pamuk ipliklerinden yüksek bulunmuştur. Kompleks çekirdek ipliklerden üretilmiş kumaşlara uygulanan gramaj, kalınlık ve sürtünme dayanım testleri, %100 pamuk ipliklerinden üretilmiş örneklerden daha düşük olduğunu göstermiştir. Kompleks çekirdek ipliklerin boncuklanma değerleri, %100 pamuk ipliklerinden üretilmiş numunelerden düşük bulunmuştur. Kompleks çekirdek ipliklerden üretilmiş kumaş numunelerinin boncuklanma değerleri, %100 pamuk ipliklerinden üretilmiş kumaş örneklerinden düşük olduğu bulunmuştur. Yine çekirdek ipliklerden üretilmiş kumaşların ısı iletim değerlerinin, %100 pamuk ipliklerinden üretilmiş kumaş örneklerinden düşük olduğu bulunmuştur.
Özet (Çeviri)
Metallic yarns are grouped into two: fancy yarns and metal fibre containing yarns. In the early days fancy yarns were produced from real metals. Nowadays they are produced from metallic coloured synthetic yarns. Today?s metal containing yarns are produced using metal fibers together with other conventional yarns. The aim of the present study is to investigate the menhanical and thermal properties of fabrics knitted with cotton yarn containing metal fibre. In the experimental part of the study, stainless steel wire of 0.035 mm diameter was used as the core material. The cover material was 100% cotton roving. The core spun yarn was fabricated using a modified ring-spinning machine. During the spinning process, the stainless steel wire was fed from the front rollers and underwent drafted roving to spin yarn with a complex core. The guide device was designed and installed on the roller-weighting arm to increase the stability of spinning of the stainless steel wire. 100% cotton yarns were also produced using the same but unmodified ring-spinning machine. Sock knitting machine was used to weave fabrics from both of these yarns. The mechanical tests performed on the yarns were unevenness, strength, elongation and hairiness; and those performed on the knitted fabrics were density, thickness, abrasion and pilling. Heat transmitting tests were performed on the two fabric samples. Unevenness test could not be performed on the core spun yarns. Strength of core spun yarns was measured to be lower than that of 100% cotton yarns. Elongation values of core spun yarns were found to be higher than those of 100% cotton yarns because of the high elongavity of the stainless steel filament contained. Yarn hairiness values of the core spun yarns were found to be higher than those of 100% cotton yarns. Tests conducted of fabric samples showed the density, thickness and abrasion values of the sample fabricated from core spun yarns to be lower than those of the sample fabricated from 100% cotton yarns. Pilling values of the sample fabricated from core spun yarns were found to be lower than those of the sample fabricated from 100% cotton yarns. Heat transmitting values of the sample fabricated from core spun yarns were found to be lower than those of the sample fabricated from 100% cotton yarns.
Benzer Tezler
- Metal flament takviyeli pamuk ipliklerinden üretilmiş boşluklu (spacer) örme kumaşların elektrik iletkenliği ve elektromanyetik kalkanlama özellikleri
The electrical conductivity and electromagnetic shielding effectiviness of knitted spacer fabrics produced metal filament supported cotton yarn
SİBEL KUTLUK
Yüksek Lisans
Türkçe
2014
Mekatronik MühendisliğiMarmara ÜniversitesiMekatronik Ana Bilim Dalı
DOÇ. DR. İSMAİL USTA
- Krom-nikel(Cr/Ni) filament takviyeli çekirdek ipliklerden üretilmiş tekstil yüzeylerinin ısıtma amaçlı kullanılması
The usage of the surfaces produced by using chrome-nickel (Cr/Ni) reinforced core fiber in heating
MAHİR TORSUN
Yüksek Lisans
Türkçe
2009
Makine MühendisliğiMarmara ÜniversitesiTekstil Eğitimi Ana Bilim Dalı
YRD. DOÇ. DR. İSMAİL USTA
- Hafif agregalı beton blokların mekanik özellikleri üzerine çelik lif kullanımının etkisi
The Effect of the use of steel fibres on mechanical properties of lightwight aggregate concrete blocks
EMRE SANCAK
Yüksek Lisans
Türkçe
1999
İnşaat MühendisliğiSüleyman Demirel ÜniversitesiYapı Eğitimi Ana Bilim Dalı
Y.DOÇ.DR. OSMAN ÜNAL
- Nanopartikül takviyeli geri dönüşüm PET (rPET) polimeri esaslı cips ve lif formuna sahip nanokompozit üretimi ve karakterizasyonu
Production of nanocomposites with the form of chips and fiber from nanoparticle-reinforced recycling PET (rPET) polymers and analysis of their properties
HANDAN KILIÇ
Yüksek Lisans
Türkçe
2016
Tekstil ve Tekstil MühendisliğiSüleyman Demirel ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. DEMET YILMAZ
- Vanadyum ve niyobyum karbür/oksit partikül takviyeli alüminyum metal matriks kompozitlerin toz metalurjisi yöntemleriyle üretimi ve karakterizasyonu
Production and characterization of vanadium and niobyum carbide/oxide particle reinforced aluminum metal matrix composites by powder metallurgy methods
MELİKE KORKMAN
Yüksek Lisans
Türkçe
2025
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
DOÇ. DR. DUYGU AĞAOĞULLARI