Effects of injection molding conditions on the mechanical properties of polyamide/glass fiber composites

Enjeksiyon makinesi çalışma şartlarının cam elyaf takviyeli-poliamid karma malzemelerinin mekanik özelliklerine olan etkisi

PDF İndir

  1. Tez No: 201806
  2. Yazar: CAHİT CAN CANSEVER
  3. Danışmanlar: PROF. DR. ÜLKÜ YILMAZER
  4. Tez Türü: Yüksek Lisans
  5. Konular: Polimer Bilim ve Teknolojisi, Polymer Science and Technology
  6. Anahtar Kelimeler: Karma Malzeme, Enjeksiyon Makinesi, Poliamid-6, Cam Elyaf, Mekanik Özellikler, Cam elyafı, Enjeksiyon kalıplama, Kompozitler, Poliamid, Composite, Injection Molding, Polyamide-6, Glass fiber, Mechanical Properties, Fiberglass, Composites, Polyamide
  7. Yıl: 2007
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Polimer Bilim ve Teknolojisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Bu çalısmada, enjeksiyon makinesi proses parametrelerinin elyaf boyutlarına ve cam elyaf takviyeli Poliamid-6 karma malzemesinin mekanik özelliklerine etkisi incelenmistir. lk olarak Poliamid-6 ve E-tipi cam elyaf ekstrüsyonda harmanlanmıstır. Daha sonra bu malzeme ile birlikte, enjeksiyon makinesinin kovan sıcaklıgı enjeksiyon basıncı, ütüleme basıncı, kalıp sıcaklıgı, sogutma zamanı ve vida hızı degistirilerek, 25 tip deney yapılmıstır. Enjeksiyonla kalıplanmıs örnekleri kullanarak, darbe, çekme, viskosite, ısı egilme testi, DSC diferansiyel ısı ölçümü tarama testi yapılmıstır. Bu testler yapılarak, proses parametrelerinin mekanik özellikleri ve elyaf boyu üzerindeki etkileri incelenmistir. Mekanik özelliklerdeki degisimi anlamak amacı ile termal testler de yapılmıstır. Ayrıca, örneklerin elyaf boyutu dagılımı da ölçülmüstür. Deneysel veriler ve test sonuçlarına göre; enjeksiyon basıncı ve vida hızı arttırıldıgında, elyaf kırılmasının azaldıgı; kovan sıcaklıgı, kalıp sıcaklıgı ve sogutma zamanı arttırıldıgında ise elyaf kırılmasının azaldıgını göstermistir. Elyaf boyu; ütüleme basıncından neredeyse hiç etkilenmemistir. Bu çalısmada, kristal yüzdesinin, enjeksiyon basıncı, ütüleme basıncı ve vida hızından etkilenmedigi farz edilmektedir. Kovan sıcaklıgı ve sogutma zamanı artırıldıgında, kristal yüzdesi artarken, kalıp sıcaklıgı arttırıldıgında kristal yüzdesi azalmıstır. Ortalama elyaf boyutu arttıgında, darbe, çekme ve modulus artarken, kopmadaki uzama azalmıstır. Kristal yüzdesi arttıgında ise çekme ve modulus olumlu olarak etkilenmistir.

Özet (Çeviri)

In this study, effect of injection molding process parameters on fiber length and on mechanical properties of Polyamide-6 / glass fiber composite were investigated to produce higher performance composites. Polyamide-6 was first compounded with an E-grade glass fiber in a co-rotating intermeshing twin screw extruder. Then, by using this composite, twenty-five types of experiments were performed by injection molding by changing the barrel temperature, injection pressure, hold pressure, mold temperature, cooling time and screw speed. Izod notched impact, tensile, viscosity, heat deflection temperature, differential scanning calorimetry tests were performed on injection molded samples. By performing these tests, the effects of process parameters on mechanical properties and on fiber length were observed. In order to understand the variation in mechanical properties, thermal tests were also conducted. Also, fiber length distributions of the samples were measured. Experimental data show that fiber breakage decreases with increasing screw speed, injection pressure, however, fiber length increases with increasing barrel temperature, mold temperature and cooling time. Fiber length is almost not affected with the hold pressure. It is assumed in this study that crystallinity is not affected with injection pressure, hold pressure and screw speed. As barrel temperature and cooling time increase, crystallinity increases, however, as mold temperature increases, crystallinity decreases. Impact strength, tensile modulus and tensile strength increase, whereas elongation at break decreases with the average fiber length. Crystallinity affects the tensile strength and modulus positively. The tensile strength and modulus increase with increasing crystallinity.

Benzer Tezler

  1. Tez No

    1016602

    Effects of injection parameters on mechanical properties of glass-fiber, glass-fiber-talc hybrid and recycled polypropylene composites using the Taguchi Method

    Taguchı Yöntemi kullanılarak cam elyaf, cam elyaf-talk hibrit ve geri dönüştürülmüş polipropilen kompozitlerin mekanik özellikleri üzerindeki enjeksiyon parametrelerinin etkilerinin incelenmesi

    YAŞAR SECCAT KESİCİ

    Yüksek Lisans

    İngilizce

    İngilizce

    2026

    Makine MühendisliğiDokuz Eylül Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. EVREN MELTEM TOYGAR

  2. Tez No

    343008

    Effects of moisture after injection on the mechanical properties of PA 6 and PA 66 materials

    PA 6 ve PA 66 malzemelerinde enjeksiyon sonrası nemin mekanik özelliklere etkisi

    HİLMİ BURAK MORALIOĞLU

    Yüksek Lisans

    İngilizce

    İngilizce

    2013

    Makine MühendisliğiDokuz Eylül Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. EMİNE ÇINAR YENİ

  3. Tez No

    82537

    Effects of twin serew compounding conditions on the mechanical properties of nylon-6 glass fiber composites

    Çift burgulu ekst-under çalışma şartlarının cam elyaf takviyeli naylon-6 karma malzemesinin mekanik özelliklerine etkisi

    MURAT CANSEVER

    Yüksek Lisans

    İngilizce

    İngilizce

    1999

    Kimya MühendisliğiOrta Doğu Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. ÜLKÜ YILMAZER

  4. Tez No

    557092

    Polipropilen köpüklerde proses parametrelerinin mekanik, mikroyapı ve yüzey kalite özelliklerine etkisinin araştırılması

    Investigation of the effects of process parameters on mechanical, microstructure and surface quality properties of polypropylene foams

    İBRAHİM BADEM

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Polimer Bilim ve TeknolojisiBursa Teknik Üniversitesi

    Lif ve Polimer Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ MERAL AKKOYUN

  5. Tez No

    689958

    Kalın cidarlı HDPE (YYPE) malzemelerin plastik enjeksiyon yöntemiyle kalıplanmasında soğutma parametrelerinin parça kalitesine etkilerinin incelenmesi

    Investigation of the effects of cooling parameters on parts quality in the molding of thick-walled HDPE (HDPE) materials by plastic injection

    MUHAMMET DAĞLI

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Makine MühendisliğiSakarya Uygulamalı Bilimler Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. AHMET DEMİRER

Geri Dön