Elektrolitik nanoAI203 takviyeli nikel kompozitlerinin üretimi
Production of nano Al203 particle reinforced n?ckel composites by electrocodeposition
- Tez No: 216212
- Danışmanlar: DOÇ. DR. AHMET ALP
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Elektrolitik kompozit kaplama, nano MMK, Al2O3 partiküldağılımı, sertlik, asınma, Electrocodeposition, hardness, nano MMC, particle distribution, processoptimization, wear
- Yıl: 2008
- Dil: Türkçe
- Üniversite: Sakarya Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 107
Özet
Bu çalısmada; Ni/Al2O3 metal matrisli kompozit kaplamalar, nano-Al2O3 partikülleriçeren gelistirilmis bir watt's tipi kaplama banyosu kullanılarak doğru akım kaplamayöntemiyle elde edilmistir. Al2O3 nano partikül miktarı ve yüzey aktif madde miktarıparametrelerinin optimize edilerek aglomere olmamıs ve yüksek hacim oranlı Nikaplamaların elde edilmesi hedeflenmistir. Ni kaplamalar düsük yüzey sertliğinesahip oldukları için, bu uygulamayla; kalıplar, takımlar ve otomobiller ile mikroaygıtların farklı parçalarına yeni malzeme sağlaması hedef alınmıstır. Ortalamaboyutu 80 nm olan Al2O3 partiküller çelik altlıklar üzerine Ni matris ile birliktebiriktirilmistir. Kaplamaların karakterizasyonu taramalı elektron mikroskobu (SEM)ve X ısını difraksiyonu (XRD) imkanları kullanılarak gerçeklestirilmistir. Üretilenkaplamaların sertliği Ni matris içerisindeki partikül hacmine bağlı olarak 402-551 Hvarasında ölçülmüstür. Yüzey aktif maddelerin zeta potansiyeline etkisi, Ni matrisiçerisindeki Al2O3 partiküllerinin biriktirilmesi ve dağılımına etkileri incelenmistir.Kaplama tabakasında artan Al2O3 partikül miktarı ile asınma dayanımının arttığı,ancak yüzey aktif madde miktarının 200 mg/l üzerinde olması durumunda düstüğüanlasılmıstır.
Özet (Çeviri)
In the present work, Ni/Al2O3 metal matrix composite (MMC) coatings wereprepared from a modified Watt's type electrolyte containing nano-Al2O3 particles bydirect current (DC) plating method. It was aimed to develop optimum processparameters of Al2O3 content, and surfactant quantity for obtaining non-agglomeratedand high volume of ceramic particles in the deposited Ni matrix. Since Ni coatingshave low surface hardness, this application is thought to provide new materials fordies, tools and different parts for automobiles and microdevices. Al2O3 nano particleswith average particle size of 80 nm were co-deposited with nickel matrix on the steelsubstrates. The characterization of the coatings was investigated by scanning electronmicroscopy (SEM) and X-ray diffraction (XRD) facilities. The hardness of theresultant coatings was also measured and found to be 402 ? 641 Hv depending on theparticle volume in the Ni matrix. The effects of the surfactant on the zeta potential,co-deposition and distribution of Al2O3 particles in nickel matrix were investigated.The wear resistance was found to increase with increasing particle content at thedeposited layer, however increasing surfactant ratio beyond 200 mg/l was fount toreveal inverse effect.
Benzer Tezler
- Elektrolitik nano SiC partikül takviyeli nikel kompozitlerinin özellikleri
Properties of nano SiC particle reinforced nickel composites by electrocodeposition
FATİH KILIÇ
Yüksek Lisans
Türkçe
2009
Metalurji MühendisliğiSakarya ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. SERDAR ASLAN
- Elektrolitik zirkonya ve bor oksidasyonu ile modifiye edilmiş titanyum yüzeylerin in vitro analizi
In vitro analysis of titanium surfaces modified with electrolytic zirconia and boron oxidation
MELİKE AYTEKİN
Doktora
Türkçe
2024
Diş Hekimliğiİstanbul ÜniversitesiOral İmplantoloji Ana Bilim Dalı
PROF. DR. VOLKAN ARISAN
- Elektrolitik nikel kaplamanın demir esaslı T/M parçaların yorulma ömürlerine etkisi
Effect of electrolitic nickel coating on fatique life of iron based P/M parts
ÜMİT ÖZKARA
Yüksek Lisans
Türkçe
2005
Metalurji MühendisliğiGazi ÜniversitesiMetal Eğitimi Ana Bilim Dalı
DOÇ.DR. RAMAZAN ÇITAK
- Electrolytic magnesium production using coaxial electrodes
Eş eksenli elektrotlar ile magnezyum üretimi
GÖKHAN DEMİRCİ
Doktora
İngilizce
2006
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. İSHAK KARAKAYA
- Elektrolitik çinko kaplama ve işletme parametrelerinin kaplama kalitesine etkisi
Electrolitic zinc plating and effect of the effects of process
KÜBRA ÇELİK
Yüksek Lisans
Türkçe
2006
Kimya MühendisliğiAnadolu ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ.DR. SÜLEYMAN KAYTAKOĞLU