Kendiliğinden yerleşen betonların reolojik ve mekanik özelliklerine su/ince malzeme oranı ile çelik lif katkısının etkisi
The effect of water/fine powder material ratio and fiber content on the mechanical and rheological properties of self-compacted concrete
- Tez No: 223434
- Danışmanlar: DOÇ.DR. YILMAZ AKKAYA
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Kendiliginden Yerlesen Beton, Reolojik Özellikler, Mekanik Özellikler, Self Compacting Concrete, Rheological Characteristics, Mechanical Properties
- Yıl: 2007
- Dil: Türkçe
- Üniversite: İstanbul Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Yapı Mühendisliği Bilim Dalı
- Sayfa Sayısı: 88
Özet
Bu tez çalısmasında sabit hacimsel 0,52 su/pudra oranlı 5 farklı su/çimento oranına sahip karısımla çalısılmıstır. Bu karısımlarda (0-45) mikron arası dane boyutuna sahip silis unu çimentoyla ikameli olarak kullanılmıstır. Kullanılan çimento dozajları sırasıyla 833 kg/m3, 645 kg/m3, 546 kg/m3, 444 kg/m3 ve 318 kg/m3`dir. Karısımlarda azalan çimento miktarına karsılık aynı hacimde silis unu eklenmis böylece çimento ve silis unu toplam hacminin sabit kalması saglanmıstır. Karısımlarda, toplam su miktarının aynı olmasından dolayı su/ince malzeme oranı sabit kalırken azalan çimento miktarından dolayı su/çimento oranı artmıstır. Sabit su/ince malzeme oranına sahip karısımlarda su/çimento oranları sırasıyla 0,24, 0,31, 0,38, 0,45 ve 0,63 olmustur. Daha sonra bu karısımlar 1 m3 betonda 78 kg olacak sekilde kullanılan liflerle üretilmistir. Yapılan deneysel çalısmalarda su/ince malzeme oranı sabitken artan su/çimento miktarının betonun gerek taze haldeki özelliklerini ve gerekse sertlesmis haldeki mekanik davranıslarını nasıl etkiledigi arastırılmıstır. Ayrıca lif katılarak üretilen karısımlarda, liflerin betonun taze haldeki özelliklerini ve sertlestikten sonraki egilme dayanımı, enerji yutma yetenegi gibi mekanik davranıslarına nasıl etkidigi arastırılmıstır. Yapılan deneysel çalısmaların sonucunda 0,52 sabit hacimsel su/pudra oranlı lifsiz karısımlarda su/çimento miktarının 0,24'den 0,38 degerine artmasına ve çimento dozajının 833 kg/m3 den 546 kg/m3 degerine azalmasına karsın basınç mukavemetlerinde bir düsüs gözlenmemistir. Bu özellik lifli üretimlerde de görülmüstür. Ayrıca lif katkısının betonun dayanımından çok yutulan enerjiyi artırdıgı gözlenmistir.
Özet (Çeviri)
In this work, 5 different concrete mixtures were produced that have the same volumetric water/powder ratio of 0,52. In the mixtures, cement was replaced with the same volume of finely ground silica powder that has a particle dimension of (0-45) ?. Cement dosages used in the mixtures were 833 kg/m3, 645 kg/m3, 546 kg/m3, 444 kg/m3 and 318 kg/m3 respectively. The amount of silica powder added to mixtures was equal to the amount of cement removed so that the water/fine powder material ratio remained constant in all 5 mixtures. However, water/cement ratios were increased because the total amount of water was kept constant for all mixtures while the amount of cement used was decreasing. These water/cement ratios were 0,24, 0,31, 0,38, 0,45, 0,63 respectively. Then, these mixtures were re-produced by using steel fibers with a dosage of 78kg/m3 The main objective of this work is to analyse the effects of water/fine powder material ratio and fiber content on the mechanical properties of self-compacted concrete and to determine the optimum values of water/cement ratio for various fresh and hardened concrete properties. Experiments showed that, with constant water/powder ratio of 0,52, the compressive strengths of concretes with and without steel fibers did not change significantly even though the water/cement ratio was increased from 0,24 to 0,38 and the cement dosage was decreased from 833 kg/m3 to 546 kg/m3. Addition of steel fibers affected the ductility of concrete rather than the strength. Moreover, it is come out that fiber content may affect the fresh concrete properties. The mixtures with the cement dosage of 546 kg/m3, having the water/cement ratio of 0,38 were determined to be the highly workable, optimum mixtures.
Benzer Tezler
- Nano silika kullanımının kendiliğinden yerleşen betonların reolojik, mekanik ve içyapısal özellikleri üzerine etkilerinin araştırılması
Investigating the effects of nano silica usage on rheological, mechanical and microstructural properties of self-consolidating concretes
MUHAMMED YASİN DURGUN
Doktora
Türkçe
2017
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. HAKAN NURİ ATAHAN
- Sentetik C-S-H bileşiklerinin kendiliğinden yerleşen betonların taze ve sertleşmiş özelliklerine etkisi
Effect of synthetic C-S-H compounds on fresh and hardened properties of self compacting concrete
MUSTAFA OĞUZ SAF
Yüksek Lisans
Türkçe
2015
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. ÜNAL ANIL DOĞAN
- Properties of self-compacting concretes made with cold bonded fly ash lightweight aggregates
Soğuk bağlama yöntemi ile elde edilen uçucu kül hafif agregalı kendiliğinden yerleşen betonların özellikleri
HATİCE ÖZNUR ÖZ
Doktora
İngilizce
2014
İnşaat MühendisliğiGaziantep Üniversitesiİnşaat Mühendisliği Bölümü
DOÇ. DR. MEHMET GESOĞLU
- Effect of particle packing on properties of heavyweight and sef-compacting concrete mortar
Doldurma yoğunluğunun kendiliğinden yerleşen ağır beton harcı üzerine etkileri
ALPER ORHUN ERÜZ
Yüksek Lisans
İngilizce
2021
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA HULUSİ ÖZKUL
- Properties of self-compacting concretes prepared with recycled aggregate
Geri kazanılmış agregalarla hazırlanan kendiliğinden yerleşen betonların özellikleri
ZEYNEP ALĞIN
Doktora
İngilizce
2015
İnşaat MühendisliğiGaziantep Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. ERHAN GÜNEYİSİ