Preperation of oil-based polyurethanes for biomedical applications in the absence of solvent and catalyst
Yağ bazlı poliüretanların biyomedikal uygulamalar için çözücü ve katalizör olmadan hazırlanması
- Tez No: 223999
- Danışmanlar: PROF.DR. FATMA SENİHA GÜNER
- Tez Türü: Yüksek Lisans
- Konular: Polimer Bilim ve Teknolojisi, Polymer Science and Technology
- Anahtar Kelimeler: Poliüretan, Trigliserid yag, Kütle polimerizasyonu, Biyopolimerler, Polyurethane, Triglyceride oil, Bulk polymerization, Biopolymers
- Yıl: 2007
- Dil: İngilizce
- Üniversite: İstanbul Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Polimer Bilim ve Teknolojisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 69
Özet
Poliüretanlar biyomateryaller olarak oldukça öneme sahiptirler. Çünki, poliüretanlar biyouyumludurlar ve çok iyi mekanik özelliklere sahiptirler. Kateter, kalp pompası, kısa dönem implant, hastane yatagı, cerrahi kumas ve yara örtüsü olarak kullanılabilirler. Poliüretanlar, genellikle petrolyum bazlı polioller ve izosiyanatlardan katalizör ve çözücü kullanılarak üretilirler. Biyomedikal amaçlarla üretilecek polimerlerin sentezlenmesinde katalizör ve çözücü gibi biyouyumlulugu olumsuz etkileyen maddelerin kullanımı istenmemektedir. Bu nedenle, bu çalısmada medikal amaçlarla kullanılacak yag bazlı poliüretanların kütle polimerizasyonu yöntemi ile katalizörsüz sentezlenmesi amaçlanmıstır. Çalısmada, keten yagı ve gliserinden elde edilen hidroksil gruplarına sahip ara ürün hidroksil kaynagı olarak kullanılmıstır. zosiyanat bileseni olarak ise toluene diizosiyanat ve hegzametilen diisosiyanat kullanılmıstır. Polimerlerin yapıları NMR ve FTIR spektroskopi ile aydınlatılmıstır. Son ürünlerin molekül agırlıklarının belirlenmesinde GPC, termal özelliklerin belirlenmesinde TGA ve DSC kullanılmıstır. Reaksiyonlar hem katalizörlü hem de katalizörsüz gerçeklestirilmis, veriler reaksiyon kinetigi yönünden degerlendirilmistir. Çalısmada polimerizasyon reaksiyonlarının izlenmesi için, yas izosiyanat tayinine alternatif olarak FTIR ile kantitatif analiz yöntemi gelistirilmistir. Tüm verilerin degerlendirilmesi sonucu, biyomedikal amaçlarla kullanılabilecek yag bazlı poliüretanların kütle polimerizasyonu yöntemiyle katalizörsüz üretilebilecegi sonucuna varılmıstır.
Özet (Çeviri)
Polyurethanes have great importance as biomaterials because they are biocompatible and have very good mechanical properties. They can be used as catheters, heart-assist pumps and short term implants, hospital bedding, surgical drapes and wound dressing. Polyurethanes are generally produced from petroleum based polyols and isocyanates in the presence of catalyst using the solvent method. Catalyst and solvent have negative effects for using polymers as biomedical applications. The aim of this thesis is synthesis of oil-based polyurethanes in the absence of catalyst and solvent in order to obtain polymer in medical purity. Oil-based hydroxyl containing material was used as hydroxyl source. Toluene-2.4-diisocyanate and hexamethylene diisocyanate were used as isocyanate component. NMR and FTIR were used for structural characterization of polymers. GPC was used for determination of molecular weight. TGA and DSC were used for investigation of thermal properties. Additionally, the reaction kinetics was investigated by analytic method and FTIR measurements. Reaction kinetic was examined for catalyzed and uncatalyzed reactions. The consumption of raw materials was monitored and the amount of isocyante in reaction mixture was determined by FTIR. After evaluation of the all obtained data, it was reached a conclusion that it is possible to synthesize polyurethanes in the absence of catalyst and solvent for biomedical applications.
Benzer Tezler
- İlaç yüklü pH duyarlı poliüretan filmlerin sentezi ve karakterizasyonu
Synthesis and characterization of drug loaded ph sensitive polyurethane films
FULYA GÜLMEZ
Yüksek Lisans
Türkçe
2019
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. FATMA SENİHA GÜNER
- Polietilen glikol ve Hint yağı temelli şekil hafıza özelliği gösteren poliüretan filmlerin sentezi ve karakterizasyonu
Synthesis and characterization of polyethylene glycol and castor oil based-shape memory polyurethane films
MİREY BONFİL
Yüksek Lisans
Türkçe
2012
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. F. SENİHA GÜNER
- Demir içeren şekil-hafıza özelliğine sahip poliüretan jellerin hazırlanması
Preparation of shape memory polyurethane gels containing iron
BERNA ÖZTÜRK
Yüksek Lisans
Türkçe
2015
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSNÜ ATAKÜL
- Synthesis of bio based polyurethane surface coating materials and characterization
Yüzey kaplaması uygulamalarında kullanılan biyo bazlı poliüretan malzemelerin sentezi ve karakterizasyonu
MERVE METİN
Yüksek Lisans
İngilizce
2016
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. NİLGÜN KIZILCAN
DR. ALPER YEŞİLÇUBUK
- Çevre dostu su bazlı poliüretan nanokompozit verniklerin geliştirilmesi ve film özelliklerinin incelenmesi
Development of eco-friendly water-based polyurethane varnish and investigation of film properties
SONGÜL DUZAN
Yüksek Lisans
Türkçe
2022
Polimer Bilim ve TeknolojisiYalova ÜniversitesiPolimer Malzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ YASEMİN TAMER