Polipropilen lifli, hava sürükleyici katkılı ve yöresel hafif agregalarla üretilen yüksek dayanımlı betonların yüksek sıcaklıklar altında bazı fiziksel ve mekanik özelliklerinin incelenmesi

The investigation of some physical and mechanical properties of high strength concrete produced with polypropylene fiber, air entraining agent and regional lightweight aggregates at elevated temperatures

PDF İndir

  1. Tez No: 232791
  2. Yazar: SERBÜLENT YAŞAR
  3. Danışmanlar: YRD. DOÇ. DR. İBRAHİM TÜRKMEN
  4. Tez Türü: Yüksek Lisans
  5. Konular: İnşaat Mühendisliği, Civil Engineering
  6. Anahtar Kelimeler: Pomza agregası, genleştirilmiş perlit agregası, polipropilen lif, hava sürükleyici katkı, yüksek sıcaklık, dayanım, kılcal geçirimlilik katsayısı, Pumice aggregate, expanded perlite aggregate, polypropylene fiber, air entraining agent, high temperatures, strength, capillary coefficient
  7. Yıl: 2008
  8. Dil: Türkçe
  9. Üniversite: Atatürk Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 170

Özet

Ince agrega (0-2 mm) yerine ağırlıkça %25, %50, %75 ve %100 oranlarında genleştirilmiş perlit agregası (GPA) ve pomza agregası (PA), beton hacminin %0,15, %0,25, %0,35 ve %0,50 oranlarında polipropilen lif (PPF) ve hacimce %4, %6 hava sürüklenmiş beton (HSB) ile toplam olarak 16 grup betonun yüksek sıcaklık (100, 200, 300, 400, 500, 600 ve 700ºC) öncesi ve sonrası, basınç dayanımı, birim ağırlık ve kılcal geçirimlilik özellikleri incelenerek analiz edilmiştir. Beton numunelerde çimento dozajı 500 kg/m3 olarak alınmış ve bütün numunelerde çimento yerine ağırlıkça %7 silis dumanı (SD) kullanılmıştır. Tüm beton numuneleri üretildikten sonra 1 gün nemli ortamda bekletilmiş ve daha sonra 27 gün boyunca 23±1ºC kirece doygun suda kür edilmiştir. Numuneler, 28 günlük kür sonunda 100, 200, 300, 400, 500, 600 ve 700ºC gibi 7 farklı sıcaklıkta üç saat bekletilmiş ve daha sonra laboratuar ortamında kendi kendine soğumaları sağlanmıştır. Yalnızca kontrol numuneleri yüksek sıcaklık sonrasında havada ve suda olmak üzere iki farklı soğuma şekline maruz bırakılmıştır. Kontrol grubu dışındaki bütün örnekler havada soğutulmuştur. Karışımlarda ince agrega yerine %25, %50, %75 ve %100 PA ve GPA kullanıldığında basınç dayanımları, kuru birim ağırlık değerleri hem yüksek sıcaklık öncesi ve hem de sonrasında azalmıştır. Ancak basınç dayanımlarındaki azalmaların PA, EPA, PPF ve hava bo?luklu numunelerde kontrol numunelerine oranla bütün sıcaklıklarda daha düşük olduğu tespit edilmiştir. Kontrol numuneleriyle diğer numuneler arasındaki farkın 300ºC sıcaklıktan sonra sıcaklığın artmasıyla azaldığı belirlenmiştir ve 600ºC`den sonra kontrol numuneleriyle diğer numuneler arasında belirgin bir farkın olmadığı tespit edilmiştir. Artan sıcaklıklarla birlikte kuru birim ağırlıklarda azalma meydana gelmiştir. Numunelerin kılcal geçirimlilik katsayısı maruz kalınan sıcaklık paralelinde artmıştır. Hava sürükleyici katkı, betonun kılcal geçirimliliğine bütün sıcaklık seviyelerinde olumlu etkide bulunmuştur. PPF`li gruplarda ise dalgalı bir seyir göstermiştir.2008, 154 sayfa

Özet (Çeviri)

Totally 16 groups of concrete produced by replacing expanded perlite aggregate (EPA), pumice aggregate (PA) with fine aggregate (0-2 mm) with the ratios of 25%, 50%, 75% and 100% in weight, by using polypropylene fiber (PPF) with the ratios of 0,15%, 0,25%, 0,35%, and 0,50% of concrete and by adding air entraining agent (AE) with the ratios of 4% and 6% in volume, were analyzed before and after high temperature effects (100, 200, 300, 400, 500, 600 and 700ºC) by examining compressive strength, dry unit weight and capillary permeability properties. Dosage was chosen as 500 kg/m3 and silica fume (SF) was used with the ratio of 7% instead of cement in all concrete mix groups. All of the concrete specimens were kept in humid environmental conditions, and then cured in lime saturated water 23+1ºC for 27 days. After curing, specimens were kept at 7 different temperatures as 100, 200, 300, 400, 500, 600 and 700ºC for three hours, and then cooled to room temperature in laboratory conditions. Only control group specimens were exposed two different cooling regimes, in air and in water. Except control group all specimens are cooled in air. Compressive strength and dry unit weight values are decreased in specimens, which EPA and PA replaced with fine aggregate with the ratios of 25%, 50%, 75% and 100%, both before and after high temperature effects. But the reductions in compressive strength were determined less at all temperatures according to control specimens. It was determined that, the difference between control specimens and other groups decrease with the increase of heat and it was observed that there was not a pronounced difference between control specimens and other groups after 600ºC. With the increasing of the temperatures dry unit weights decreased. The maximum reductions due to the PA and EPA were at 100% of their replacement of sand. The capillarity coefficient of samples increased with the increasing of the exposed temperature. AE improved the capillarity coefficient of samples at all level of high temperature. Capillarity coefficient of samples due to the PPF was fluctuated.2008, 154 pages

Benzer Tezler

  1. Tez No

    232362

    Yüksek sıcaklık etkisinden hasar görmüş lifli, hava sürükleyici katkılı ve perlit agregalı betonların dayanım özellikleri ve GFRP ile onarımı ve güçlendirilmesi

    Strength properties of concretes with fiber, entrained air and expanded perlite aggregates after exposure to high temperatures and confinement with GFRP

    OZAN SEÇER

    Yüksek Lisans

    Türkçe

    Türkçe

    2008

    İnşaat MühendisliğiAtatürk Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. İBRAHİM TÜRKMEN

  2. Tez No

    532163

    Kolemanit atığı ve silis dumanı katkılı metakaolin tabanlı geopolimer harcın mekanik ve durabilite özelliklerinin incelenmesi

    Investigation of colemanite waste and silica fume on the mechanical and durability properties of metakaolin based geopolymer mortar

    YURDAKUL AYGÖRMEZ

    Doktora

    Türkçe

    Türkçe

    2018

    İnşaat MühendisliğiYıldız Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ORHAN CANPOLAT

  3. Tez No

    647409

    Polimer-modifiye çimento esaslı hibrit lifli hafif kompozit geliştirilmesi

    Development of polymer-modified cement-based hybrid fiber reinforced lightweight composite

    CEREN DUYAL

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    İnşaat MühendisliğiDokuz Eylül Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. KAMİLE TOSUN FELEKOĞLU

  4. Tez No

    855419

    Yüksek sıcaklığa maruz kalan çimento esaslı lifli kompozitlerin temel mühendislik özellikleri

    Fundamental engineering properties of cement-based fiber-reinforced composites exposed to high temperature

    MUHAMMED YUSUF GÖZKESER

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    İnşaat MühendisliğiBatman Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DR. SERHAT DEMİRHAN

  5. Tez No

    151593

    Polipropilen lifli betonların mekanik özelliklerinin incelenmesi

    Investigation of mechanical properties of polyropylene fiber concrete

    GÖKHAN ALKAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2004

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF.DR. CANAN TAŞDEMİR

Geri Dön