Fren disklerine uygulanan kaplamaların frenleme performansına etkisinin deneysel incelenmesi

An experimental investigation on the braking performance of coated brake discs/rotors

  1. Tez No: 233139
  2. Yazar: ABDULLAH DEMİR
  3. Danışmanlar: PROF. DR. İBRAHİM KILIÇASLAN
  4. Tez Türü: Doktora
  5. Konular: Teknik Eğitim, Technical Education
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2009
  8. Dil: Türkçe
  9. Üniversite: Kocaeli Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 154

Özet

Bu çalışmada 5 adet 2001 model Toyota Corolla'nın orijinal ön fren diski kullanıldı. Bu disklerden 4 tanesi; metalik (Metco 19E ve 18C), sermet ve seramik ile kaplandı. İki disk, sırası ile 1'er mm kalınlığında alevle püskürtme ve ergitme yöntemi kullanılarak Metco 19E ve Metco 18C metalik tozlarla kaplandı. Diğer iki diske de NiCr arabağlayıcı kaplandıktan sonra; birincisinde plazma sprey yöntemiyle Al2O3-TiO2, diğerine de HVOF (Yüksek Hızlı Oksijen Yakıtıyla Püskürtme) yöntemiyle Cr3C2-NiCr kaplandı. Çalışmada yapılan tüm kaplamalardan ve orijinal diskten alınan numuneler standart metalografik incelemeye tabii tutuldu. Ayrıca orijinal ve kaplanmış diskler Link Engineering Company test laboratuarında (Detroit, USA) tam ölçekli atalet dinamometresi ile SAE'nin J2522 fren etkinlik testine alındı. Tüm testlerde; frenleme sayısı, çevrim zamanı, frenleme başlangıç hızı, bırakma hızı, frenleme süresi, frenleme ivmesi, frenleme torku, uygulama basıncı, sürtünme katsayısı, diskin sıcaklığı, iç ve dış balata sıcaklığı gibi parametreler toplam 276 frenleme ile kaydedildi. Her bir diskin toplam test süresi yaklaşık 41.400 saniye tutmuştur. Bu sürenin ortalama 39.600 saniyesi diskin rejim haline getirilmesi için harcanmıştır. Geri kalan ortalama 1770 saniye de etkin frenleme testine harcanmıştır. Bu parametrelere ek olarak bazı test bölümlerinde ise koniklik, frenleme tork değişimi ve disk kalınlık değişimi de ölçülmüştür. Ayrıca testler başlamadan önce ve testler tamamlandıktan sonra disk ve balataların aşınma oranları hem boyutsal hem de kütlesel olarak tespit edilmiştir. Daha sonra tüm diskler SAE J2334 test standardına göre hızlandırılmış korozyon testine tabii tutulmuştur. Yapılan tüm testlerde; kaplamalı diskler hem korozyon direnci hem de sürtünme katsayısı (seramik disk hariç) açısından orijinal diskten daha iyi performans göstermiştir.

Özet (Çeviri)

In this study five front brake rotors of the car, 2001 model Toyota Corolla, has been used. Four of these has been coated with metallic (Metco 19E and 18C), sermet and ceramics by using various coating methods. Two rotors have been coated respectively with Metco 18C and Metco 19E metallic powder at 1 mm thickness using flame spray and melting method. After the other two rotors were coated with NiCr layer; by using plasma spray method, the first one has been coated with Al2O3-TiO2 and the second one has been coated with Cr3C2-NiC using HVOF method. Samples taken from all coatings made in this study and OEM rotor have been subjected to metallographic investigation. Furthermore, OEM discs and coated discs have been subjected to J2522 global brake effectiveness test of SAE with full-scale inertia dynamometer in Link Testing Laboratory (Detroit, USA). In all tests; parameters as braking number, cycle time, brake speed, release speed, stop time, deceleration, braking torque, pad actuator pressure, coefficient of friction, rotor temperature, and inpad/outpad temperature have been saved for 276 brakings. While total test time of each disc was 41400 s, averagely 1770 seconds of this time was determined as effective braking time. In addition to these parameters, in some test sections, coning, brake torque variation and disc thickness variation were also measured. Furthermore, before and after tests, abrasion rate of rotors and pads were measured in ?mm? and ?g?. Additionally, all rotors were subjected to cosmetic corrosion test according to SAE J2334 test standards. In all tests; coated rotors showed higher performance than OEM rotor in respect of corrosion resistance and coefficient of friction (except of ceramics disc).

Benzer Tezler

  1. Ağır ticari araçlarda kullanılan fren disklerinin sürtünme ve aşınma özelliklerinin incelenmesi

    Examination of the friction and wear properties of brake discs used in heavy commercial vehi̇cles

    EMİN EMRE GÖKTEPE

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Metalurji MühendisliğiSakarya Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MEHMET UYSAL

  2. Termal sprey kaplamalı fren diskleri için çevreye uyumlu balata geliştirilmesi

    Development of environmentally compatible pads for thermal spray coated brake discs

    OZAN DEMİRDALMIŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Metalurji MühendisliğiSakarya Uygulamalı Bilimler Üniversitesi

    İmalat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. EKREM ALTUNCU

  3. Fren disklerinde plazma sprey alümina esaslı kaplamaların uygulanabilirliği ve kaplamalı disk- balata arası sürtünme davranışının incelenmesi

    The applicability of plasma spray alumina based coatings in brake discs and investigation of coated disc-pad friction behavior

    ZEKERİYA KOLBASAR

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    Metalurji MühendisliğiSakarya Uygulamalı Bilimler Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ EKREM ALTUNCU

  4. Farklı seramik parçacıkların AISI 304 östenitik paslanmaz çelik üzerine elektrokimyasal yöntem ile kaplanabilirliğinin araştırılması

    Investigation of electrochemical coating of different ceramic particles on AISI 304 austenitic stainless steel

    GİZEM TUGÇE GÜNGÖR

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Makine MühendisliğiFırat Üniversitesi

    Makine Mühendisliği Teknolojileri Ana Bilim Dalı

    DOÇ. DR. FARUK KARACA

    DR. ÖĞR. ÜYESİ SALİH CİHANGİR

  5. İzotrop yarım düzleme oturan ortotrop tabakanın sürekli temas problemi

    Continuous contact problem of an orthotropic layer resting on an isotropic half plane

    MİNE GÜL OKTAY

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    İnşaat MühendisliğiBayburt Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ERDAL ÖNER