Üçüncü bileşen şartlarında bor atık katkılı çimentonun özelliklerinin incelenmesi

Investigating the properties of cement with boron wastes under the circumstance of third components

  1. Tez No: 238357
  2. Yazar: MUSTAFA ERSİN AKBULUT
  3. Danışmanlar: YRD. DOÇ. DR. TANER KAVAS
  4. Tez Türü: Yüksek Lisans
  5. Konular: Seramik Mühendisliği, Ceramic Engineering
  6. Anahtar Kelimeler: Portland Çimentosu, Bor atığı, Mikrokalorimetre, SEM, Portland Cement, Boron wastes, Microcalorimeter, SEM
  7. Yıl: 2009
  8. Dil: Türkçe
  9. Üniversite: Afyon Kocatepe Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Seramik Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 99

Özet

Bu çalısmada, Kırka Bor ?sletmelerinde açığa çıkan bor içerikli kil atıklarının üçüncübilesen sartlarında Portland Çimentosuna katkı maddesi olarak kullanılabilirliğiarastırılmıstır. Bu amaçla, Portland Çimentosuna ağırlıkça % 0, 1, 3 ve 5 oranlarındabor atığı ilave edilerek dört faklı reçete hazırlanmıstır. Hazırlanan reçetelere sırasıyla,özgül yüzey alanı (Blaine), priz süresi (Vicat) , hacim genlesmesi (Le-ChatelierHalkası), zeta potansiyeli (ZP), hidratasyon ısısı (Mikrokalorimetre), eğilme ve basmamukavemeti testleri yapılarak mikro yapı (SEM) analizleri incelenmistir. Elde edilenverileri standart (bor atık katkısız) reçete ile karsılastırdığımızda bütün bor atık katkılıreçetelerin hidratasyon özelliklerinin ve priz sürelerinin bor atık katkısının artısınaparalel olarak kötülestiği belirlenmistir. Bununla birlikte aynı numunelerin mukavemetdeğerlerini incelediğimizde % 1 ve 3 oranlarında bor atık katkılı reçetelerin standartreçetenin mukavemet değerlerini yakaladığı görülmüstür. Bor atık katkılı reçetelerarasından en iyi mukavemet sonucunu veren % 3 oranında bor atık katkılı reçeteyeüçüncü bilesen olarak % 0.1, 0.3, 0.5, ve 0.7 oranlarında organik katkı (pektin) ilaveedilerek olumsuz hidratasyon özellikleri iyilestirilmeye çalısılmıstır. Bu amaçla dörtfarklı pektin katkılı reçete hazırlanarak deneyler tekrarlanmıstır. Deney sonuçlarına görepektin katkısının artmasına paralel olarak tüm reçetelerin hidratasyon sürelerininkısaldığı, fakat mukavemet değerlerinin düstüğü belirlenmistir.Sonuç olarak % 3 oranında bor atık katkısı ve % 0.1 oranında pektin katkısı ile TS EN196-1 standartında belirlenmis mukavemet değerine ve TS EN 196-3 standartındabelirlenmis priz süresi değer aralığına ulasıldığı saptanmıstır.

Özet (Çeviri)

In this study, the usability of clay waste including boron, which is supplied from KırkaBoron Companies, as an additive material for Portland Cement in case of thirdcomponent has been investigated. So, four different receipts were prepared by addingboron waste in ratios of 0%, 1%, 3%, and 5% by weight respectively to Portland cementcomposition. Specific surface area, outlet time, the volume expansion, zeta potential,heat of hydration, bending and suppression tests and SEM analysis were performed tothe samples in order to determine the physical properties and microstructure. Afterwardsthe datas obtained from characterization workout were compared to the blank sample(having no boron waste) and as a result, the deterioration of hydration of all samplesbelonging to four different receipts depending on the increasing amount of boron wasteadditive was comeout. On the other hand, it was clarified that the strength values ofsamples having boron waste in ratios of 1 % and 3% were nearly same as the blankones. For further step of the study, as a third component pectin (organic additive) wasput in the receipt having boron waste in ratio 3% which acquired the best strengthvalues, in ratios of 0.1%, 0.3%, 0.5%, 0.7% by weight respectively just to amelioratethe hydration properties. For this purpose four different receipts incorporating pectinwere prepared and the experiments were carried up again. According to the results ofexperiments, as the amount of pectin additive was gone up hydration times of allsamples were shortened but strength values were decreased.Finally as a conclusion it was determined that the sample having boron waste in ratio of3% and pectin additive in ratio of 0.1% was appropriate to the standart TS EN 196-1 interms of strength values and to the TS EN 196-3 in terms of hydration time values.

Benzer Tezler

  1. Special resin additives for polyurethane

    Poliüretan için özel reçine katkı maddeleri

    GÖRKEM ÜLKÜ

    Doktora

    İngilizce

    İngilizce

    2023

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    DOÇ. DR. NESRİN KÖKEN

  2. Treatability of aircraft deicing fluids (ADFs) by high-rate anaerobic systems: An investigation on biogas potential and energy recovery

    Havalimanlarında ortaya çıkan buz çözücü sıvıların yüksek-hızlı anaerobik sistemlerde arıtılabilirliği: Biyogaz potansiyeli ve enerji geri kazanımının araştırılması

    GİZEM ENGİZ

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Çevre Mühendisliğiİstanbul Teknik Üniversitesi

    Çevre Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ÇİĞDEM GÖMEÇ

  3. Effect of pre-concentration technique on the extraction of volatile compounds in beef and changes in quality parameters under dynamic storage conditions

    Çiğ etten uçucu bileşenlerin ekstraksiyonunda ön konsantrasyon tekniğinin etkisi ve dinamik muhafaza şartları altında kalite parametrelerinin değişimi

    AYLİN MET ÖZYURT

    Doktora

    İngilizce

    İngilizce

    2018

    Gıda Mühendisliğiİstanbul Teknik Üniversitesi

    Gıda Mühendisliği Ana Bilim Dalı

    DOÇ. DR. NEŞE ŞAHİN YEŞİLÇUBUK

  4. Experimental investigation of steam-alkali flooding with borax using Batı Raman oil

    Batı Raman petrolü kullanılarak buhar- alkali (borax) solüsyon enjeksiyonunun deneysel incelenmesi

    WILDAN HASHIM NOORI NOORI

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Petrol ve Doğal Gaz Mühendisliğiİstanbul Teknik Üniversitesi

    Petrol ve Doğal Gaz Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MURAT ÇINAR