Geri Dön

Metakrilamit'in mono ve dikarboksilik asitlerle hidrojellerinin hazırlanması ve şişme davranışlarının araştırılması

Preparation of hydrogels of methacrylamid with mono and dicarbocsilic acids and investigation of the swelling behavior

  1. Tez No: 284293
  2. Yazar: ALAADDİN KILIÇ
  3. Danışmanlar: YRD. DOÇ. DR. RAMAZAN COŞKUN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya, Chemistry
  6. Anahtar Kelimeler: Poli(metakrilamit-ko-krotonik asit), poli(metakrilamit-ko-maleik asit), hidrojeller, metilenbisakrilamit, Poly( methacrylamid-co-crotonic acid), Poly(methacrylamid-co-maleic acid), hydorgels, methylenbisacrylamide
  7. Yıl: 2010
  8. Dil: Türkçe
  9. Üniversite: Bozok Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Bölümü
  12. Bilim Dalı: Kimya Ana Bilim Dalı
  13. Sayfa Sayısı: 112

Özet

Bu çalışmada, potasyum persülfat (KPS) başlatıcısı ve metilenbisakrilamit (MBAAm) çapraz bağlayıcısı kullanılarak radikalik kopolimerizasyonla metakrilamitin (MAAm), mono(krotonik asit,CrA) ve dikarboksilik (maleik asit, MAA) asitlerle hidrojelleri hazırlandı ve hazırlanan hidrojellerin şişme davranışları incelendi. Şişme oranına; monomer oranının, başlatıcı ve çapraz bağlayıcı derişiminin ve polimerizasyon sıcaklığının etkileri araştırıldı. MAAm/CrA hidrojelinde, 85/15 MAAm/CrA ( mol/mol), molce %2 KPS, molce %1 MBAAm ve 55oC'ta hazırlanan hidrojellerin maksimum (% 480) şiştiği gözlendi. MAAm/MAA hidrojelinde, 75/25 MAAm/MAA (mol/mol), molce %1 KPS, molce %1 MBAAm ve 55 oC'ta hazırlanan hidrojellerin maksimum (% 1100) şiştiği gözlendi. Optimum şartlarda hazırlanan hidrojellerin SEM analizinde yüzey morfolojisinin; monomer oranı, başlatıcı ve çapraz bağlayıcı derişimine bağlı olarak değiştiği gözlendi. Optimum hidrojellerin şişme davranışına ortam pH'nın, ortam sıcaklığının, ortam elektrolit derişiminin ve türünün etkileri araştırıldı. Her iki hidrojelinde pH=7'de maksimum şişme gösterdiği gözlendi. Her iki hidrojelin şişme davranışlarının ortam sıcaklığı, ortam elektrolit derişimi ve türüne bağlı olarak değiştiği gözlendi. Optimum jellerin oda sıcaklığında damıtık suda şişme kinetiği çalışmaları sonucunda MAAm/CrA jelinin Fick tipi, MAAm/MAA jelinin Nonfickian tipi difüzyon gösterdiği gözlendi.Sentezlenen jellerin karakterizasyonunda; TGA, ATR-FTIR ve SEM tekniği kullanıldı.

Özet (Çeviri)

In this study, by using potassium persulfate (KPS) initiator, methylenbisacrylamide (MBAAm) crosslinking, methacrylamid?s (MAAm) mono (crotonik acid, CrA) and dicarboxylic (maleic acid, MAA) acids hydrogels were prepared with radical copolymerization and the prepared hydrogels? swelling behaviors were investigated. The effects of ratio of monomer, initiator and crosslinker concentration and polymerization temperature to swelling ratio were investigated. In MAAm/CrA hydrogel, maximum (480%) swelling was observed with the hydrogels prepared with 85/15 MAAm/ CrA (mole/mole), KPS mole ratio % 2, MBAAm mole ratio 1% and at the heat of 55oC. In MAAm/MAA hydrogel, maximum (1100%) swelling was observed with the hydrogels prepared with 75/25 MAAm/MAA (mole/mole), KPS mole ratio 1%, MBAAm mole ratio 1% and at the heat of 55o C. In SEM analysis, it was observed that the surface morphology of the hydrogels, prepared under optimum conditions, changed depending on the monomer ratio, initiator and crosslinker concentration. The effects of pH and temperature of the environment, electrolyte concentration and type of environment to swelling behavior of the optimum hydrogels were investigated.At level of pH =7 maximum swelling was observed in both of the hydrogels. It was observed that swelling behavior of both of the hydrogelschanged according to the temperature, electrolyte concentration and type of the environment. As a result of experimental studies, optimum gel swelling kinetics in distilled water at room temperature MAAm/CrA gel Fick type, MAAm/MAA gel Nonfickian type diffusion was observed.TGA,FTIR and SEM techniques were used while characterizing the structure of the synthesized gels.

Benzer Tezler

  1. Termal duyarlı polimerlerin davranışlarına uç grupların ve çeşitli polimerik blokların etkisinin incelenmesi

    Investigation of the effect of the end groups and various polymeric blocks on the behaviour of thermal sensitive polymers

    SERZEN İLBOĞA

    Doktora

    Türkçe

    Türkçe

    2014

    KimyaFırat Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. MEHMET COŞKUN

  2. Katı faz zenginleştirmeli akışa enjeksiyonlu FAAS ile Pb, Ag ve Au tayini

    Determination of Pb, Ag and Au with solid phase precontrantion by flow injection FAAS

    TESLİMA DAŞBAŞI

    Doktora

    Türkçe

    Türkçe

    2013

    KimyaErciyes Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. AHMET ÜLGEN

  3. İnsan plasenta ve endotel hücre hatları ile 3b kriyojel ortak kültür sisteminin oluşturulması ve etkinliğinin araştırılması

    Construction of a 3d cryogel co-culture system using human placental and endothelial cell lines and investigating its efficiency

    MERVE DEMİR

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    BiyolojiHacettepe Üniversitesi

    Biyoloji Ana Bilim Dalı

    DOÇ. DR. AYSUN KILIÇ SÜLOĞLU

  4. Üç boyutlu biyobasım yönteminde denizel kaynaklı biyomürekkep kullanılarak karaciğer doku mühendisliği uygulamaları için ko-kültür yapılarının oluşturulması

    Construction of co-culture structures for liver tissue engineering applications by using marine-derived bioink in three-dimensional bioprinting method

    ELİF BALIKÇI

    Doktora

    Türkçe

    Türkçe

    2024

    BiyomühendislikSağlık Bilimleri Üniversitesi

    Doku Mühendisliği Anabilim Dalı

    PROF. DR. ERKAN TÜRKER BARAN

  5. İzokumarin türevli polimer sentezi ve karakterizasyonu

    Synthesis and characterization of isocoumarin derivative polymer

    HALİL İBRAHİM AVCI

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Polimer Bilim ve TeknolojisiAdıyaman Üniversitesi

    Kimya Ana Bilim Dalı

    DOÇ. DR. ADNAN KURT

    PROF. DR. MURAT KOCA