Zirkonyum dioksit alt yapı üzerine uygulanan farklı yüzey işlemlerinin ve tekrarlanan fırınlamanın üst yapı porseleninin bağlanma dayanımına etkisinin in-vitro olarak incelenmesi
In-vitro evaluation of the effect of different surface treatments and repeated firing on their bond strength to two veneer ceramics to zirconia
- Tez No: 303225
- Danışmanlar: PROF. DR. BÜLENT ŞERMET
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2011
- Dil: Türkçe
- Üniversite: İstanbul Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 194
Özet
Amaç:Bu çalışmanın amacı, zirkonyum dioksit alt yapı üzerine uygulanan yüzey işlemlerinin ve tekrarlanan fırınlamanın iki farklı üst yapı seramiğiyle olan bağlanma dayanımlarına etkilerinin araştırılmasıdır.Gereç ve Yöntem:Zirkonyum dioksit alt yapıdan (Kavo Everest ZS blok) elde edilen 120 adet standart örnek (bağlantı yüzeyi 7 mm (çap), 2 mm (yükseklik); metal kalıba sabitlenecek alt kısmı ise 3,2 mm (çap), 7 mm (yükseklik) kademeli silindirik) üç gruba ayrılarak her bir gruba sırasıyla: kumlama, kumlama ve liner uygulaması yapıldı ve kontrol grubuna ise herhangi bir yüzey işlemi uygulanmadı. Elde edilen örneklere üst yapı seramiği (3 mm kalınlığında) iki farklı teknikle (GC Initial Zr-FS ve GC Initial PC) uygulandı. Ayrıca tekrarlanan fırınlama işlemi yapılarak ısı uygulamasının bağlanma dayanımına etkisi değerlendirildi. Makaslama bağlanma dayanımı testi yapılarak değerler (MPa) kaydedildi. Kırılmanın meydana geldiği yüzeylerdeki farklılıklar tarayıcı elektron mikroskobu (SEM) ile değerlendirildi. Çalışmamızın istatistiksel analizi One-way ANOVA ve Tukey testleri kullanıldı.Bulgular:Üst yapı uygulamasında kullanılan farklı teknikler alt yapı-üst yapı bağlantısını büyük oranda etkilemektedir. Presleme tekniğiyle hazırlanan üst yapıların bağlanma dayanımı tabakalama tekniğine göre daha yüksektir. Kumlama ve presleme tekniği (32,23±7,90 MPa) kullanılarak hazırlanan örneklerdeki bağlanma dayanımı, kumlama ve tabakalama tekniğiyle (22,87±8,21 MPa) hazırlananlara göre daha yüksek değerdedir. Ayrıca zirkonya alt yapılar üzerine uygulanan farklı yüzey işlemleri de bağlantıyı önemli ölçüde etkilemektedir. Liner materyalinin uygulanması başarısızlık oranını arttırmaktadır. Kumlama işlemi (32,23±7,90 MPa) ve yüzey uygulamasının yapılmadığı (30,59±8,40 MPa) örneklerin bağlantı dayanımı liner uygulananlara (19,92±5,34 MPa) göre daha yüksektir. Tekrarlanan fırınlama işlemi bağlantıyı arttırmaktadır.
Özet (Çeviri)
Purpose:The aim of this study was to investigate the effect of different surface treatments and repeated firings on their bond strength to two veneer ceramics to zirconia.Materials and Methods:One hundred-twenty standard specimens (base; 7 mm in diameter and 2 mm high and body; 3,2 mm in diameter and 7 mm high) of zirconia framework materials (Kavo Everest ZS blank) received either of the following surface treatments: airborne-particle abrasion, airborne-particle abrasion and coated with the liner application, or unchanged CAD/CAM milled surface. The specimens were veneered (3 mm in thickness) with two types of veneer ceramics: GC Initial Zr-FS and GC Initial PC. In addition the effect of heat treatment was examined. Mean shear bond strength values (MPa) were calculated. Structural differences were analyzed with scanning electron microscopy (SEM). One-way ANOVA and Tukey post hoc tests were used to analyze the data.Results:The type of veneering technique had a significant effect on the core?veneer bond strength. The shear bond strength of pressable veneer ceramics were significantly higher than the layering veneer ceramics. Zirconium oxide copings treated with airborne-particle abrasion and veneered with pressable ceramic (32,23±7,90 MPa) yielded higher shear bond strength values than layering ceramic (22,87±8,21 MPa). Furthermore, different surface treatments had different effects on the core?veneer bond strength according to the zirconia material used. The application of liner material dramatically affected the bond strength and failure mode. The sandblasted (32,23±7,90 MPa) and unchanged milled surfaces (30,59±8,40 MPa) were significantly stronger than the liner application (19,92±5,34 MPa). Repeated firings increased the shear strength.
Benzer Tezler
- Burdur ili mermer sektörünün kurumsal ve ekonomik yapısı
İnstitutional and economic structure of marble sector in burdur
AHMET SARITAŞ
- Üst yapı porselenlerinin zirkonyum esaslı alt yapılar üzerine olan bağlantı dirençlerine farklı soğutma sürelerinin etkisinin incelenmesi
Influence of cooling rate on the shear bond strength of veneering porcelain to zirconia
İBRAHİM EREN YILMAZ
Doktora
Türkçe
2015
Diş HekimliğiSüleyman Demirel ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. DR. HAKKI CENKER KÜÇÜKEŞMEN
- Zirkonyum dioksit alt yapilarda gerçekleştirilen farkli renklendirme işlemlerinin üst yapi porseleniyle olan bağlanti dayanimina etkisi
The effect of different coloring procedures of zirconium oxide cores on the shear bond strengths to veneering porcelain materials
İLKİN TUNCEL
Doktora
Türkçe
2012
Diş HekimliğiSüleyman Demirel ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. ERDAL EROĞLU
- Sıçratma tekniği ile büyütülen zirkonyum dioksit ince filmlerin mikro yapılarının incelenmesi
The investigation of microstructures of zirconium dioxide thin films grown by sputtering technique
BURHAN COŞKUN
Doktora
Türkçe
2013
Fizik ve Fizik MühendisliğiFırat ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. YUSUF ATICI
- Farklı alt yapı ve üst yapı oranlarının tüm seramik sistemlerinde bağ dayanımına etkisinin mekanik yöntemlerle araştırılması
Evaluating the effect of various core and veneer ratio to all ceramic systems bond strength by mechanic methods
CENNET ELÇİN SAĞIRKAYA
Doktora
Türkçe
2010
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. CELAL ARTUNÇ