Çelik dökümlerin tamir bakım kaynakları ve ultrasonik muayenesi
Repair weldings and ultrasonic testing of steel castings
- Tez No: 315143
- Danışmanlar: YRD. DOÇ. DR. MEMDUH KURTULMUŞ
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Teknik Eğitim, Metallurgical Engineering, Technical Education
- Anahtar Kelimeler: Onarım, Tozaltı kaynağı, Ultrasonik test, Çelik döküm, Repair, Submerged arc welding, Ultrasonic test, steel casting
- Yıl: 2012
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Büyük maliyetlerle hazırlanan çok amaçlı konstrüksiyonların birçok işlevibyapması sırasında; dinamik, statik yüklere ve korozyona karşı uzun süre dayanması istenir. Buna mukabil zamanla oluşabilecek anormal zorlanmalar sonucunda bir takım hasarlar meydana gelebilmektedir. Bu hasarları gidermek için en etkili ve en ekonomik yöntem kaynaklı tamirattır.Bu tez çalışmasında; 4 adet St 52 plakalar kullanılmış, bu plakalar V kaynak ağzı açılarak Tozaltı kaynak yöntemi ile birleştirilmiştir. Birleştirilen plakalar 4 eşit parçaya ayrılmıştır. Bu parçalara uygulanan ultrasonik ve radyografik muayeneler sonucunda malzeme kalınlığının % 70, % 80 ve %100'ü kadar oyuklar açılmıştır. Gazaltı (MAG), Özlü tel ve Elektrik Ark kaynağı olmak üzere üç farklı kaynak yöntemi kullanılarak açılan oyuklar doldurulmuştur. Kaynaklar soğuk (ön tavsız)olarak yapılmıştır. Her parçaya iki defa tamir uygulanmıştır. Tamir öncesi ve sonrası gerekli ölçümlemeler yapılmıştır. Her tamir işlemi sonunda parçalardan çekme deneyi, metalografik inceleme ve sertlik deneyi için numuneler alınmıştır. Parçalara uygulanan tamirler sonucunda meydana gelen distorsiyon miktarları, çekme dayanımı ve sertlik gibi mekanik özellikler tespit edilmiş ve metalografik incelemeleri yapılmıştır.Hazırladığımız bu tezle ve yaptığımız deneysel çalışmalar sonucunda, çeliklerin tamir bakım kaynaklarında, Gazaltı(MAG), Özlü tel ve Elektrik Ark kaynak yöntemlerinden hangisini kullanırsak kullanalım tamir sonrası malzemelerin mekanik özelliklerinde herhangi bir değişiklik olmadığı belirlenmiştir. Ayrıca parçalara açılan oyuk miktarlarına ve soğuk (ön tavsız) uygulanan kaynak yöntemlerine bağlı olarak malzemelerde oluşan açısal distorsiyonların farklılık gösterdiği tespit edilmiştir.
Özet (Çeviri)
Steel castings and weldments are examined with nondestructive test methods. Ultrasonic test method is usually is applied to steel castings and weldments to detect internal defects. The castings and weldments which containe internal defects can repaired by welding operations.In this study repair welding effects on cast steel weldments were investigated. 20 mm thick St 52 steel plates were butt welded with the submerged arc welding (SAW) process. The weldments were ultrasonically examined. Although the weldments were defect free, repair welding was applied to them. The welds were cut 60-80 % and then welded. Repair weldings were done with shielded Metal Arc Welding (SMAW), Flux Cored Arc Welding (FCAW) and Gas Metal Arc Welding(MAG) welding processes. The repair welds were done without preheating. After each repair welding the workpiece was ultrasonically examined. Then the angular distortion of the workpiece was measured.Two successive repair welding operation was applied to each workpiece. Samples were cut from the weldments for tensile testing, hardness testing and metallographic examination.From the experiments the following results were drived:1) The least angular distortion was obtained with the MAG method.2) SMAW repair welding caused the highest distortion.3) All repair welding methods gave the same machanical properties.
Benzer Tezler
- Darbeli elektromanyetik alanlar ile osteojenik indüksiyon (teorik, deneysel ve klinik çalışma)
Başlık çevirisi yok
ARSLAN BORA
Tıpta Uzmanlık
Türkçe
1982
Ortopedi ve TravmatolojiEge ÜniversitesiOrtopedi ve Travmatoloji Ana Bilim Dalı
PROF. DR. MERİH EROĞLU
- Türkiye'nin ekonomik gelişmesinde tarımın parasal sorunları ve tarımsal kredi uygulaması
Başlık çevirisi yok
AHMET CEMAL SİVASLIGİL
- Assessment of degradation mechanism and stability of a cut slope in jointed and sheared limestone along Anakara-Eskişehir E90 highway
Ankara-Eskişehir E90 karayolu üzerindeki çatlaklı ve makaslanmış kireçtaşında açılan şevin duraylılık ve degradasyon mekanizmasının belirlenmesi
BURAK ÖZTEKİN
Yüksek Lisans
İngilizce
2004
Jeoloji MühendisliğiOrta Doğu Teknik ÜniversitesiJeoloji Mühendisliği Ana Bilim Dalı
DOÇ.DR. TAMER TOPAL
- Yığma yapılarda taşıyıcı tuğla duvarların hasır donatılı horasan harcı ile güçlendirilmesinin deneysel olarak incelenmesi
Experimental investigation of the strengthening of masonry walls with steel mesh reinforcement horasan mortar in masonry structures
VOLKAN ÖZTAŞ
Doktora
Türkçe
2024
İnşaat Mühendisliğiİstanbul Teknik ÜniversitesiMimarlık Ana Bilim Dalı
PROF. DR. NECDET TORUNBALCI