Sol-jel yöntemi ile borosiloksan (SİBOC) jel eldesi, karakterizasyonu ve seramik oluşumu çalışmaları
Borosiloksan (SİBOC) gel synthesis by sol-gel method, characterization and ceramic formation investigation
- Tez No: 337988
- Danışmanlar: DOÇ. DR. BİRSEN ŞENGÜL OKSAL
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2013
- Dil: Türkçe
- Üniversite: Akdeniz Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 101
Özet
Bu çalışmada, sol-jel yöntemi ile silisyum bor oksikarbür (SiBOC) polimer jeller ve hidroborasyon reaksiyonu ile organoborosiloksan polimerleri sentezlenmiştir. Elde edilen polimerlerin inert atmosferde pirolizi ile SiBOC seramikleri elde edilmiştir. Farklı parametreler kullanarak sentezlenen ve literatürde yer almayan polimerler ve seramik tozların yapısı, termal özellikleri ve kristallenme davranışları Fourier Transform Infrared Spektroskopisi (FT-IR), Termogravimetrik Analiz (TGA) ve X-Işını Kırınımı (XRD) tekniği ile incelenmiştir. SiBOC polimer başlatıcı jel eldesinde farklı silanlar, farklı bor bileşikleri (bor kaynağı) ve değişen B/Si mol oranları kullanılmıştır. Reaksiyon esnasında gliserin ilavesinin ve reaksiyon sonunda ultrasonik ve mikro dalga uygulamasının, polimerlerin jelleşme zamanı, seramik tozlarının yapısı ve bozunma sıcaklığına etkisi incelenmiştir. Ayrıca, organoborosiloksan polimer eldesinde kullanılan siloksan yapısının ve siloksan/boran mol oranının seramik tozların yapısı ve bozunma sıcaklığına etkisi incelenmiştir. Sonuç olarak, organik gruplardaki dallanmanın azalmasının, yapıdaki bor oranının artmasının, bor kaynağı olarak trietilborat (TEB) kullanılmasının, gliserin ilavesinin ve ultrasonik ve mikrodalga uygulamasının jelleşme süresini kısaltıcı etmenler olduğu gözlenmiştir. XRD analizi sonucu, tüm seramik tozlarda 1400°C?de ß-SiC kristal oluşumunun gözlenmesi, termal açıdan kararlı amorf SiBOC seramiklerin elde edildiğini göstermiştir.
Özet (Çeviri)
In this study, silicon boron oksikarbür (SiBOC) precursor polymer gels were synthesized by sol-gel method and organoborosiloksan polymers were synthesized by hydroboration reaction. SiBOC ceramics were obtained by the pyrolysis of this polymers in an inert atmosphere. Polymers and ceramic powders that have not been in the literature were synthesized using different parameters. Structure, thermal properties and crystallization behavior of them were investigated by Fourier Transform Infrared Spectroscopy (FT-IR), Thermogravimetric Analysis (TGA), and X-Ray Diffraction (XRD) technique. To obtain SiBOC precursor polymer gels, different silanes, boron compounds and B/Si molar ratio were used. The effect of addition of glycerine during the reaction and ultrasonic and microwave application at the end of the reaction to the polymer gelation times and decomposition temperature of ceramic powders were investigated. In addition, structure of the used siloxane to produce the organoborosiloxane polymers and siloxane/borane molar ratio were investigated in terms of the effect to the structure and the decomposition temperature of ceramic powders. As a conclusion, the decrease in branching of the organic groups, the increase of the percentage of boron in the structure, the use of triethylborate (TEB) as boron sources, the addition of glycerin and the application of ultrasonic and microwave reduced the gelation time (tgel). XRD analysis results show that, ß-SiC crystal were observed in the all ceramic powders at 1400°C and amorphous SiBOC ceramics with stability at high temperatures were obtained.
Benzer Tezler
- Sol-jel yöntemi ile hazırlanan TB ve ZN katkılı YBCO-123 ve YBCO-358 süperiletkenlerinin incelenmesi
The investigation of TB and ZN doped YBCO-123 and YBCO-358 superconductors produced by sol-gel route
GÜLNUR GÜDÜCÜ
Doktora
Türkçe
2022
Metalurji MühendisliğiKastamonu ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. ÖZGÜR ÖZTÜRK
PROF. DR. SERAP SAFRAN
- Sol-jel yöntemi ile Na2O-B2O3-P2O5-SiO2-CaO biyoaktif camlarının üretimi
Produciton of Na2O-B2O3-P2O5-SiO2-CaO bioactive glasses by sol-gel method
CEM KESGİN
Doktora
Türkçe
2021
BiyomühendislikYıldız Teknik ÜniversitesiBiyomühendislik Ana Bilim Dalı
PROF. DR. SEVİL YÜCEL
- Sol-jel yöntemi ile elde edilen nano boyutlu çapraz bağlayıcı ürün eldesi ve kumaşa aplikasyonu
Obtaining a nano-sized crosslinking chemical by sol-gel technique and its application to fabric
ELİF YAŞAR
Yüksek Lisans
Türkçe
2013
Tekstil ve Tekstil MühendisliğiDokuz Eylül ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
PROF. DR. AYSUN AKŞİT
- Sol-jel yöntemi ile hazırlanmış katkılı ZrO2 ile galvaniz kaplamaların karşılaştırılması
Comparison of galvanized coatings with additive ZrO2 prepared by sol-gel method
MERT CAN EMRE
Yüksek Lisans
Türkçe
2021
Mühendislik BilimleriAkdeniz ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. İBRAHİM HALİL MUTLU
- Sol-jel yöntemi ile üretilmiş alümina-bovine hidroksiapatit (BHA) kompozitlerinin özellikleri ve karakterizasyonu
Properties and characterization of alumina-bovine hydroxyapatite (BHA) composites produced by sol-gel method
AZADE YELTEN
Yüksek Lisans
Türkçe
2010
Metalurji Mühendisliğiİstanbul ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. SUAT YILMAZ