Mekanokimyasal yöntemle demir silisyum bileşiğinin üretilmesi ve radar absorpsiyon malzemesi olarak kullanılabilirliği
Production of iron silicide by mechanochemical method and usability as radar absorbtion material
- Tez No: 354202
- Danışmanlar: PROF. DR. METİN GÜRÜ
- Tez Türü: Doktora
- Konular: Kimya Mühendisliği, Savunma ve Savunma Teknolojileri, Chemical Engineering, Defense and Defense Technologies
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2013
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 113
Özet
Radar absorpsiyon malzemeleri (RAM); radar tarafından gönderilen elektromanyetik dalganın bir kısmını soğurarak malzemenin radarda tespitini güçleştiren malzemelerdir. Ülkemizde maalesef RAM üretimi yapılamadığı için yurt dışından ithal edilmesi gerekmektedir. RAM vb. stratejik öneme sahip ürünleri ülkemizde üretirsek hem kendi silahlı kuvvetlerimizde istediğimiz yerde ve zamanda kullanabilmesi hem de diğer ülkelere bu malzemelerin satışının yapılabilmesi mümkün olacaktır. RAM olarak kullanılabileceği değerlendirilen demir silisyumun üretilmesine bu yüzden karar verilmiştir. Bu doktora çalışmasında da; yüksek enerji çarpımlı öğütücü ile yapılan mekanokimyasal teknik kullanılarak demir silisyumun üretilmesi, üretilen malzemenin uygun bağlayıcı ile karıştırılarak yüksek sıcaklığa dayanıklı hale getirilmesi ve radar absorpsiyon malzemesi olarak kullanılabilirliğinin araştırılması amaçlanmıştır. Demir silisyum (Fe3Si) üretim koşullarının optimize edilmesi için parametrik çalışma yapılmıştır. Parametrik çalışmada en önemli parametre olan silisyum miktarı ilk önce optimize edilmiş ve %17 olarak belirlenmiştir. Daha sonra sırasıyla en uygun çalkalama süresi, sinterleşme sıcaklığı ve süresinin belirlenmesi için deneysel çalışma yapılmıştır. Yapılan çalışmalar sonucunda çalkalama süresi 1000 dakika, sinterleme sıcaklığı 12000C ve sinterleme süresi de 2 saat olarak optimize edilmiştir. Fe3Si üretilebilmesiyle RAM için en önemli kısım olan manyetik ışınları soğurma özelliğine sahip pigment üretimi sağlanmıştır. Üretilen pigmentin boya haline getirilebilmesinde yüksek sıcaklık dayanımı da amaçlandığı için silikon esaslı bağlayıcının kullanılmasına karar verilmiştir. Hazırlanan boya hem 18-40 GHz aralığında yaklaşık -16 dB absorpsiyon yaptığı hem de 5700C'a kadar özelliklerini koruduğu için yüksek sıcaklığa dayanıklı RAM olarak kullanılabileceği değerlendirilmiştir.
Özet (Çeviri)
Radar absorption material (RAM); absorbs a portion of electromagnetic waves transmitted by radar and make it difficult to be detected by radar. Unfortunately, in our country (Turkey), RAM cannot be produced and have to be imported from other countries. If RAM etc. other strategic materials will be produced in our country, we want to be able to use in Turkish Armed Forces with no limitation for place or time and can sale RAM to other countries. Therefore, the production of strategic materials such as RAM, is very important for our country. Because of these reasons, synthesis of iron silicon, which can be used as RAM, was decided. The aims of this thesis are; to produce iron silicide by mechanochemical method by using high energy mill, to mix by proper binder to produce high temperature resistant RAM and research to availability as RAM. Parametric study was performed to optimize production conditions of Iron silicon (Fe3Si). In parametric study, silicon percent is the most important parameter so firstly it was optimized and was found as %17. After that, milling time, annealing temperature and annealing time was optimized respectively. Optimum milling time, annealing temperature and annealing time was identified as 1000 minute, 12000C and 2 hours respectively. The most important portion of RAM is pigment, which absorbs the magnetic waves, was completed by production of Fe3Si. Usage of silicon based resin was decided to produce high temperature resistant paint from produced pigment. Produced paint absorbs -16 dB at 18-40 frequency bands as well as resistant to 5700C, so it was evaluated as high temperature resistant RAM.
Benzer Tezler
- Mekanokimyasal yöntemle radar absorplayıcı madde sentezlenmesi için reaktör tasarımı ve katkılarla absorplayıcı malzemenin geliştirilmesi
Design reactor for synthesis of radar absorption material by mechanochemical method and development of absorbing material by additives
ALİ RIZA AKTAŞ
Doktora
Türkçe
2013
Kimya MühendisliğiGazi ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. METİN GÜRÜ
- Bazı metal sülfidlerin mekanokimyasal yöntemle çözündürülmesi
Dissolution of some metal sulphides by mechanochemical processing
GÖKHAN UÇAR
Doktora
Türkçe
2010
Maden Mühendisliği ve MadencilikSelçuk ÜniversitesiMaden Mühendisliği Ana Bilim Dalı
DOÇ. DR. SALİH AYDOĞAN
- Mekanokimyasal sentez yöntemiyle BaTa2O6 üretimi, Fe giderimi, lüminesans ve termodinamik özellikler
BaTa2O6 production by mechanochemical synthesis, Fe removal, luminescence and thermodynamic properties
MUSTAFA İLHAN
Doktora
Türkçe
2013
Metalurji MühendisliğiYıldız Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. CEMALETTİN YAMAN
PROF. DR. AYHAN MERGEN
- Metal/ametal katkılı ZnO nano taneciklerin sentezleri, fotokatalitik aktivitedeki ve boya duyarlı güneş hücrelerindeki performansları
Synthesis of metal/nonmetal doped ZnO nanoparticles, their performances in photocatalytic activity and in dye sensitized solar cells
MOHAMMAD SUTAIF
- Farklı oranlarda alüminyum-bor oksit-karbon karışımlarından mekanokimyasal yöntem ile oda sıcaklığında Al2O3-B4C kompozit sentezi ve karakterizasyonu
Synthesis and characterization of Al2O3-B4C composites at room temperature by mechanochemical method from aluminum-boron oxide-carbon mixtures at different ratios
ÜMİT KOÇ
Yüksek Lisans
Türkçe
2018
Metalurji MühendisliğiDumlupınar ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. REMZİ GÖREN
DR. ÖĞR. ÜYESİ HEDİYE AYDIN