Bakırın elektrokimyasal özellikleri üzerine kendiliğinden oluşan silan filmlerinin etkisi
Effects of the self-assembled silane monolayers on the electrochemical properties of copper
- Tez No: 374752
- Danışmanlar: PROF. DR. AYSEL YURT ECE
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2014
- Dil: Türkçe
- Üniversite: Eskişehir Osmangazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Fizikokimya Bilim Dalı
- Sayfa Sayısı: 135
Özet
Silan türevlerinin (3-merkaptopropiltrimetoksisilan, N-2-aminoetil-3-aminopropiltrimetoksisilan, 3-aminopropiltrietoksisilan, Oktadesiltriklorosilan, Oktadesiltrimetoksisilan) kendiliğinden oluşan tek tabakalarının oluşumu ve asidik ortamda bakırın elektrokimyasal davranışları üzerine koruyucu etkisi elektrokimyasal yöntemler (elektrokimyasal kuartz kristal mikroterazi, EQCM ve elektrokimyasal empedans spektroskopisi, EIS) ile incelenmiştir. Her iki yöntemle yapılan ölçümler sonucunda silan çözeltilerinin derişiminin artmasıyla, yüzey filmlerinin koruyucu etkinliğinin arttığı bulunmuştur. Bu durumun silan moleküllerinin bakır yüzeyine adsorpsiyonundan kaynaklandığı ve adsorpsiyonun Langmuir adsorpsiyon izotermine uygun olduğu saptanmıştır. Yüzey analizleri ise taramalı elektron mikroskobu (SEM) yöntemi ile yapılmış ve yüzeyde koruyucu bir film tabakasının oluştuğu sonucuna varılmıştır. Yapı-etki ilişkisini araştırmak amacıyla MNDO yarı-semi empirik hesaplama yöntemi ile kuantum kimyasal hesaplamalar yapılmıştır. Elde edilen parametreler SAM oluşum sürecinde MER-Silan, N-Silan, A-Silan moleküllerinin bakır yüzeyine kimyasal adsorsiyon mekanizması ile adsorplandıklarını, C-Silan ve M-Silan moleküllerinin ise fiziksel adsorpsiyon yoluyla adsorplandıklarını göstermektedir. Oluşan SAM'lerin kalitesinin ve koruyuculuğunun MER-Silan>N-Silan>A-Silan>C-Silan>M-Silan sıralamasını izlediği saptanmıştır. Kuartz kristallerin türünün silan filmleri üzerine etkisini araştırmak amacıyla Cr/Au ve Ti/Au kuartz kristaller, silan yüzey filmleri ile kaplanmış ve aralarındaki fark incelenmiştir. Yüzey filmlerinin koruma yüzdeleri arasındaki farkın, kristalde kullanılan farklı metal çiftlerinin yarattığı farklı kristal rezonans frekanslarından kaynaklanabileceği sonucuna ulaşılmıştır.
Özet (Çeviri)
The formation of self assembled monolayers of silane derivatives (3-mercaptopropyltrimethoxysilane, N-2-aminoethyl-3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, Octadecyltrichlorosilane, Octadecyltrimethoxysilane) and also the effect of monolayers on the electrochemical behaviour of copper in acidic media were investigated by electrochemical methods (electrochemical quartz crystal microbalance, EQCM and electrochemical impedance spectroscopy, EIS). Both of these measurements indicate that the protection efficiencies of silane films increase with increasing of the concentration of silane solutions. This reveals that formation of silane films were mainly due to adsorption of molecules on copper surface. It was found that the adsorption of silane molecules on copper obey Langmuir adsorption isotherm. Surface analysis have been made by scanning electron microscopy (SEM) and that a protective film formed on the metal surface was concluded. The relationship between the protection efficiencies of studied silanes and their molecular structure has been investigated using quantum chemical parameters obtained by MNDO semi-empirical methods. Obtained quantum chemical parameters show that adsorption of MER-Silane, N-Silane, A-Silane molecules have chemical mechanism whereas C-Silane and M-Silane molecules have physical mechanism on copper surface. It was found that the protection efficiencies of the silane molecules follow the order of MER-Silan>N-Silan>A-Silan>C-Silan>M-Silan. Both of the Cr/Au and Ti/Au quartz crystals were coated with silane films and the difference in the properties of monolayers were examined. Obtained results indicate that this difference is due to the different crystal resonant frequencies.
Benzer Tezler
- Synthesis, characterization, and electrochemical properties of mesoporous spinel LiMn2-xMxO4 (M = Mn, Fe, Co, Ni, and Cu) thin films
Mezogözenekli spinel LiMn2-xMxO4 (M = Mn, Fe, Co, Ni, and Cu) ince filmlerin sentezi, karakterizasyonu ve elektrokimyasal özellikleri
IRMAK KARAKAYA DURUKAN
- N-sübstitüe anilin ve N-sübstitüe pirollerin bakır üzerinde elektropolimerizasyonları ve antikorozif özelliklerinin araştırılması
Electropolymerizations of N-substituted anilines and N-substituted pyrroles on copper and investigation of their anticorrosive properties
BERRİN DURAN
- Bakır üzerine nikel-tungsten alaşımlarının elektrokimyasal olarak kaplanması ve elektrokatalitik davranışlarının belirlenmesi
Electordeposition of nickel-tungsten alloys on copper and determination of their electrocatalytic behaviors
YAVUZ SÜRME
Doktora
Türkçe
2011
KimyaNiğde ÜniversitesiKimya Ana Bilim Dalı
DOÇ. DR. ABDULLAH ALİ GÜRTEN
PROF. DR. KADRİYE KAYAKIRILMAZ
- Electrochemical switchable plasmonic surfaces
Elektrokimaysal olarak değiştirilebilen plazmonik yüzeyler
NİHAT SERKAN KARAYALÇIN
Yüksek Lisans
İngilizce
2014
Fizik ve Fizik Mühendisliğiİhsan Doğramacı Bilkent ÜniversitesiMüzik Bilimleri Bölümü
YRD. DOÇ. DR. AYKUTLU DANA
- Sülfürlü ve oksitli bileşiklerden ergimiş tuz elektrolizi ile bakır ve alaşımlarının direkt sentezi
Direct synthesis of copper and copper alloys from sulfide/oxide compounds via molten salt electrolysis
LEVENT KARTAL
Doktora
Türkçe
2019
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. SERVET İBRAHİM TİMUR