AISI 8620 çelik malzemelerin plazma spreyleme yöntemiyle kaplanması ve kaplama arayüzeylerinin karakterizasyonu
Coating of AISI 8620 steel by plasma spraying and characterisation of coating interfaces
- Tez No: 436239
- Danışmanlar: PROF. DR. NİZAMETTİN KAHRAMAN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2016
- Dil: Türkçe
- Üniversite: Karabük Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İmalat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 135
Özet
Bu çalışmada, sementasyon işlemi görmüş AISI 8620 çelik malzemeler kullanılmıştır. Bu malzeme, özellikle inşaat iskelelerinin demir kasnaklarının yapımında kullanılan bir makine parçasıdır. Bu makine parçası çalışma şartlarında maruz kaldığı olumsuz etkenlerden dolayı çapı zaman içerisinde azalmakta ve hurdaya gönderilmektedir. AISI 8620 malzemenin aşınan yüzeyine gerekli ön hazırlıklar yapılarak, farklı kimyasal içeriğe sahip tozlarla, plazma spreyleme yöntemiyle kaplanarak tekrar kullanıma uygun hale getirilmek istenmiştir. Kaplama işlemi gerçekleşmiş numunelerin öncelikle yüzey pürüzlülük ölçümleri gerçekleştirilmiştir. Kaplamaların servis şartlarındaki aşınma dayanımlarını belirlemek için aşınma testi, kaplama tabakası ve arayüzeylerin karakterizasyonu için sertlik testi ve kaplama tabakası-ana malzeme arayüzeydeki yapışma mukavemetini belirlemek için çekme testleri yapılmıştır. Ayrıca kaplama numuneleri üzerinde arayüzey özelliklerini belirlemek için, optik mikroskop ve taramalı elektron mikroskobu (SEM) çalışmaları gerçekleştirilmiştir. Kaplama işlemi gerçekleştirilen numunelerin yüzey pürüzlülük değerleri ile kaplama tozlarının tane boyutlarının yakından ilişkili olduğu belirlenmiştir. Yapılan deneyler sonucunda en düşük yüzey pürüzlülük değeri ve en yüksek aşınma direnci CRC-106 kaplamasında olduğu belirlenmiştir. Sertlik ölçümleri sonucunda; en yüksek değeri 72F-NS kaplamasından ölçülür iken, onu sırasıyla CRC-106, 68F-NS-1 ve AMDRY 962 kaplamaları takip etmektedir. Yapışma mukavemetini belirlemek için yapılan çekme deneyleri sonucunda en yüksek arayüzey bağ dayanımını AMDRY 962 kaplamasında olduğu tespit edilmiştir. Optik mikroskop ve SEM çalışmaları sonucunda kaplama tabakası ve arayüzeyde oksitlerin oluştuğu gözlenmiştir.
Özet (Çeviri)
In this study, carburised AISI 8620 steel was used. This steel is used for making machine parts such as pulleys and construction scaffolding. Diameters of these parts get smaller during their service life because of the negative conditions in working fields and they are sent to scarp. The worn surfaces of AISI 8620 material were prepared before coating and then they were coated by coating plasma spraying method using various powders of different chemical compositions. By doing so, they were made ready for use. Initially, surface roughness values of the coated test specimens were determined. Under service conditions, wear test was done to define the coatings' wear resistance, hardness test was done for the characterisation of coating layer and their interfaces. Tensile test was also carried out to define the adhesion strength of the interface. Also, optical microscopy and SEM tests were done to define their interface properties. It is found out that there is a strong correlation between the surface roughness values of coated test specimens and the grain size of coating powders. The results revealed that CRC-106 coating led to highest wear resistance and lowest surface roughness values. The highest hardness was measured for 72F-NS coating and this is followed by CRC-106, 68F-NS-1 and AMDRY 962 coatings. The highest adhesion strength was seen for AMDRY 962 coating. Finally, the result of optical microscopy and SEM examinations showed the formation of oxides within the coating layer and coating interface.
Benzer Tezler
- İnşaat asansörleri istikamet makaralarında kullanılan farklı çelik malzemelerin aşınmalarının incelenmesi
Examination of the wear of different steel materials used in construction hoists direction rollers
ÜNAL KILINÇ
Yüksek Lisans
Türkçe
2020
Makine MühendisliğiSüleyman Demirel ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ŞEVKİ YILMAZ GÜVEN
- Vites dişli çeliğinin KRTD-bor yöntemi ile borlanması
Boriding of transmission gear steel via CRTD-bor
ALAADDİN CEM OK
Yüksek Lisans
Türkçe
2018
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. GÜLDEM KARTAL ŞİRELİ
- Bor karbür kaplanmış AISI 8620 ve hardox 400 çeliklerinin abrasiv aşınma davranışlarının incelenmesi.
Examination of the abrasive wear behaviour of boron carbide coated AISI 8620 and hardox 400 steels
MEHMET TABUR
Doktora
Türkçe
2008
Makine MühendisliğiGazi ÜniversitesiEndüstriyel Teknoloji Eğitimi Ana Bilim Dalı
PROF. DR. MAHMUT İZCİLER
- Sürtünme kaynağında kırılma davranışının incelenmesi
Fracture analysis of fracture behaviours in friction welding
BAHADIR KARATAŞ
Yüksek Lisans
Türkçe
2010
Makine MühendisliğiCelal Bayar ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. N. SİNAN KÖKSAL
- Katı ortamda bor yayınımı ile sertleştirilen çelik yüzeylerinin kuru kayma halinde sürtünme ve aşınma davranışları
Başlık çevirisi yok
YAVUZ SOYDAN