Zamana bağlı olarak kompozit malzemelerin darbe davranışına soğuk ortamın etkisi

The effect of cold environment on impact behavior of composite material depending on time

  1. Tez No: 475156
  2. Yazar: ALİ YASİN CANER
  3. Danışmanlar: DOÇ. DR. ÜMRAN ESENDEMİR
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Cam elyaf takviyeli kompozit malzeme, darbe davranışı, zamana ve sıcaklığa bağlı darbe davranışı, düşük hızlı darbe, tabaka kalınlığı, Glass fiber reinforced material, impact behavior, time and temperature dependent impact behavior, low velocity impact, plate thickness
  7. Yıl: 2016
  8. Dil: Türkçe
  9. Üniversite: Süleyman Demirel Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 89

Özet

Farklı hızlarda kısa süre içinde, bir malzeme ve yapı üzerine anlık dış kuvvetin yarattığı etkiye darbe adı verilir. Darbe kompozit malzemeler üzerinde bir veya birden çok hasar modu oluşturabilir. Hasar modları; delaminasyon, fiber kırılması, matriks çatlağı, fiber –matriks ara yüzey hasarı ve delinme şeklinde görülebilir. Bu hasar modlarına bağlı olarak darbe davranışı kuvvet‐çökme eğrileri, absorbe edilen enerji‐zaman eğrileri, darbe enerjisi‐kuvvet eğrileri, darbe enerjisi‐ çökme eğrileri yardımlarıyla da gözlemlenebilir. Bu tez çalışmasında ASTM standartalarına göre mekanik özellikleri belirlenen tek yönlü cam elyaf takviyeli epoksi kompozit plakaların artan darbe enerjisi altında darbe davranışları oda sıcaklığı, soğuk ortam ve yarı zamanlı soğuk ortam olmak üzere 6 ay süreyle 3 farklı ortam sıcaklık şartlarında ele alınarak incelenmiştir. Kompozit plakalar 100 mm x 100 mm boyutlarında, 8 ve 16 tabakalı, 2 mm ve 4mm kalınlıklarda tabakalar imal ettirilmiştir. Soğuk ortamın darbe davranışları üzerindeki etkisi zamana bağlı olarak incelenmiştir. Darbe testleri Instron‐Dynatup 9350 HV darbe test cihazı ile yapılmıştır. Deney numuneleri oda sıcaklığı, soğuk ortam, yarı zamanlı soğuk ortam ve 20J, 30J, 40J, 50J, 60J darbe enerjileri koşulları altında test edildi. Bu çalışma sonucunda, 8 tabakalı numuneler için üç farklı çevre şartlarında ve 20J'lük darbe enerjisi altında kapalı eğri elde edilirken diğer darbe enerjileri seviyeleri ve üç ortam şart için açık eğri oluşmuştur. 16 tabakalı numuneler için ise tüm darbe enerjileri ve her üç ortam şartları için kapalı eğri oluşmuştur.

Özet (Çeviri)

The effect on a material or a structure created by an external force within a short time with different speeds is called impact. The impact might create damage modes on composite materials once or more. Damage modes can appear as delamination, fiber breakage, matrix cracking, fiber‐matrix interface damage and perforation. According to these damage modes, impact behaviour can be also observed with the help of forcedeflection curves, absorded energy‐time curves, , impact energy‐force curves and impact energy‐ deflection curves. In this study, the impact behaviour under increasing impact energies of unidirectional fiber glass reinforced epoxy composite plates determined mechanical properties according to ASTM standarts have been examined for a period of 6 months under cold environment conditions, half cold environment conditions and room temperature conditions. Composite plates have been manufactured as in the size of 100mmx100mm, 2 mm and 4 mm different thickness of 8 and 16 layers. The effect of the cold environment on impact bahavior has been studied as function of time. An instrumented drop weight impact testing machine '' Instron‐ Dynatup 9350 HV'' was used for the impact tests. The samples have been tested under cold, half cold and room temperature conditions for the cold atmosphere condition, half cold atmosphere condition and room temperature and 20J, 30J, 40J, 50J, 60J impact energy conditions. As a result, while a closed curve was obtained the three different environmental conditions and under 20J impact energy, the open curves were obtained for other impact energy levels and the three different environmental conditions. Closed curves were obtained for the samples with 16 layers at all environmental and impact energy conditions.

Benzer Tezler

  1. Uçak kompozit yapılarında erozyon direncinin incelenmesi

    Investigation of erosion resistance in aircraft composite structures

    ORHAN BAYDIR

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Havacılık ve Uzay MühendisliğiEskişehir Osmangazi Üniversitesi

    Havacılık Bilimi ve Teknolojileri Ana Bilim Dalı

    DOÇ. DR. SELİM GÜRGEN

  2. Investigation and comparison of dynamic and mechanical properties of poly-lactic acid and glass fiber reinforced poly-lactic acid

    Poli-laktik asit ve cam elyaf katkılı poli-laktik asit'in dinamik ve mekanik özelliklerinin incelenmesi ve karşılaştırılması

    ASLINUR ÖZBOYACI

    Yüksek Lisans

    İngilizce

    İngilizce

    2021

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    DOÇ. DR. MOHAMMADREZA NOFAR

  3. Investigation of the cutting performances of the diamond tools used in the natural stone industry

    Doğal taş sanayisinde kullanılan elmaslı kesicilerin kesim performansının incelenmesi

    BERRAK BULUT

    Doktora

    İngilizce

    İngilizce

    2021

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MURAT BAYDOĞAN

  4. Generation and measurement of mixed voltages, investigation on electrical discharge phenomena, and electric field analysis

    Karma gerilimlerin üretimi ve ölçümü, elektriksel boşalma olayının araştırılması ve elektrik alan analizi

    MEHMET MURAT İSPİRLİ

    Doktora

    İngilizce

    İngilizce

    2022

    Elektrik ve Elektronik Mühendisliğiİstanbul Teknik Üniversitesi

    Elektrik Mühendisliği Ana Bilim Dalı

    PROF. DR. ÖZCAN KALENDERLİ

  5. Darbe tesiri altındaki kompozit levhanın sonlu elemanlar yöntemi ile simülasyonu

    Finite element method with simulation of a composite board under impact effect

    FERHAT SANLI

    Yüksek Lisans

    Türkçe

    Türkçe

    2008

    Makine MühendisliğiMarmara Üniversitesi

    Makine Eğitimi Ana Bilim Dalı

    PROF. DR. NİHAT AKKUŞ

    YRD. DOÇ. DR. MUSTAFA GÜRLER