Manyezit filtre tozu ile kordiyerit seramik üretimi ve reaksiyon kinetiğinin incelenmesi

Production of the cordierite ceramic with magnesite filter powder and analysis of the reaction kinetics

  1. Tez No: 496633
  2. Yazar: ŞULE KILINÇ
  3. Danışmanlar: PROF. DR. AYŞEGÜL AŞKIN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Seramik Mühendisliği, Chemical Engineering, Ceramic Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2018
  8. Dil: Türkçe
  9. Üniversite: Eskişehir Osmangazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Temel İşlemler ve Termodinamik Bilim Dalı
  13. Sayfa Sayısı: 82

Özet

Bu çalışmanın amacı, doğal ve atık magnezitin kordiyerit oluşumunda başlangıç hammaddesi olarak kullanılabilirliğini araştırmak ve kordiyerit oluşum reaksiyonunu kinetik olarak incelemektir. İlk olarak ham manyezit kordiyerit hammadde bileşiminde kullanılmış (CM), ikinci olarak ise ham manyezit yerine manyezit filtre tozu kullanılarak (CMF) iki farklı kordiyerit malzeme hazırlanmıştır. Farklı ısıtma hızları (1,5, 2 ve 3 °C/dk) ve farklı sıcaklıklarda (1250, 1300 ve 1325 °C) sinterlenen örneklerin bulk yoğunluk, % su emme, % gözeneklilik değerleri ile tane boyutları belirlenmitştir. Kordiyerit malzemelerdeki fiziksel ve kimyasal farklılıkların belirlenmesi amacıyla XRD, SEM, DSC/TG analizleri yapılmış, Rietveld analizi ile de kantitatif analiz gerçekleştirilmiştir. Kordiyerit malzemenin oluşumunda tane boyutu ve sinterleme sıcaklık parametreleri bilimsel açıdan öneme sahiptir. Tane boyutu azaldıkça malzemede bulk yoğukluk, % su emme ve % gözeneklilik azalmaktadır. Sinterleme sıcaklığı arttıkça malzeme oluşumunda ikincil fazların varlığı azalmaktadır. 1250 °C'de CMF ve CM kordiyeritlerde XRD analizi sonucunda α-kordiyerit, kristobalit, kuvars ve forsterit ortak fazları bulunarak manyezit filtre tozunun kordiyerit seramiklerde başlangıç hammadde olarak kullanılabildiği görülmüştür. Rietveld analizi sonucu ile 1250 °C ve 3 °C/dk sinterleme hızında CM'de % 53, CMF'de % 61 oranında ve 1325 °C'de % 61 oranında α-kordiyerit fazı gözlenmiştir. En yüksek β-kordiyerit faz miktarı ise % 70 oranında 1,5 °C/dk sinterleme hızında 1300 °C'de gözlenmiştir. Manyezit filtre tozu kullanılarak üretilen kordiyeritte 1145 °C'de faz oluşumunu tamamladığı gözlenmiş, reaksiyonun gerçekleşmesi için gerekli aktivasyon enerjileri ise KAS yöntemi ile 112,41 kJ/mol, FWO yöntemi ile 118,63 kJ/mol hesaplanmıştır.

Özet (Çeviri)

Primary purpose of this study is to research both usability of natural and waste materials as starting raw materials on formation of cordierite and reaction kinetics of cordierite formation. At first, raw magnesite was used in cordierite raw materials composition (CM), secondly instead of raw magnesite magnesite filter powder was used in cordierite raw materials composition (CMF) and two different cordierite sampling material were prepared. Bulk density, % water absorption, % porosity, particle size were determined by using different heating rate (1,5, 2 and 3 °C/min) and sintering temperature (1250, 1300 and 1325 °C). XRD, SEM, DSC/TG and Rietveld analyzes for quantitative analyzes were performed in an attempt to determine physical and chemical differences of cordierite materials formation. In the formation of the cordierite, particle size and sintering parameters are site of special scientific interest. As long as decreasing particle size, bulk density, % water absorption and % porosity decrease. According as sintering temperature increases, secondary phases decrease in cordierite materials. As a result of XRD analysis at 1250 °C in CMF and CM cordierite, α-cordierite, cristobalite, quartz and forsiterite were determined, it is observed that magnesite filter powder can be used as starting raw materials. With Rietveld analysis results high quantitiy of α-cordierite was determined % 53 in CM and % 61 in CMF at 1250 °C, % 61 in CMF at 1325 °C. Maximum β-kordiyerit phase quantity was observed % 70 at 1300 °C, 1,5 °C/min. As a consequence in magnesite filter cordierite produced by using dust, it is observed the phase completed at its formation 1145 °C and the activation energy required for the reaction to occur is calculated 112,41 kJ/mol with KAS method, 118,63 kJ/mol with FWO method.

Benzer Tezler

  1. Kümaş elektro-filtre manyezit tozu artıklarından magnezyum bileşikleri (MgO, Mg(OH)2, MgCl2, MgB2) üretimi

    Production of magnesium compounds (MgO, Mg(OH)2, MgCl2, MgB2) from Kümaş electro-filter magnesite dust waste

    NECMETTİN ERDOĞAN

    Doktora

    Türkçe

    Türkçe

    2002

    Maden Mühendisliği ve MadencilikEskişehir Osmangazi Üniversitesi

    Maden Mühendisliği Ana Bilim Dalı

    PROF. DR. MUAMMER KAYA

  2. Atık elektro filtre manyezit tozlarının çözünme davranışının optimizasyonu ve geri kullanılabilirliğinin belirlenmesi

    The Optimization of dissolution behaviour of electrofilter magnesite dust waste and determination of its recyclebility

    GÖZDE AYVAZOĞLUYÜKSEL

    Yüksek Lisans

    Türkçe

    Türkçe

    2011

    Maden Mühendisliği ve MadencilikEskişehir Osmangazi Üniversitesi

    Maden Mühendisliği Ana Bilim Dalı

    PROF. DR. HALDUN KURAMA

  3. Sprey atomizasyon destekli indüktif plazma yöntemiyle oksit ve oksit-dışı nanopartikül üretimi

    Production of oxide and non-oxide nanoparticles via the method of spray atomization assisted inductive plasma

    ABDULLAH SELİM PARLAKYİĞİT

    Doktora

    Türkçe

    Türkçe

    2019

    Makine Mühendisliğiİstanbul Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. CELALETDİN ERGUN

  4. Manyezitin sülfürik asit çözeltilerindeki çözünürlüğü

    Başlık çevirisi yok

    AHMET EKMEKYAPAR

    Doktora

    Türkçe

    Türkçe

    1989

    KimyaAtatürk Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. M. MUHTAR KOCAKERİM