SiC takviyeli CoCrFeNi yüksek entropili kompozitin üretilmesi ve aşınma özelliklerinin incelenmesi
Production of SiC reinforced CoCrFeNi high entropy composite and investigation of wear characteristics
- Tez No: 521252
- Danışmanlar: DOÇ. DR. HAKAN GAŞAN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Yüksek Entropili Alaşım, Kompozit Malzemeler, Mekanik Alaşımlama, Spark Plazma Sinterleme, CoCrFeNi-SiC, High Entropy Alloy, Composite Material, Mechanical Alloying, Spark Plasma Sintering, CoCrFeNi-SiC
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Eskişehir Osmangazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Nanobilim ve Nanoteknoloji Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 86
Özet
Yüksek entropi alaşımları yeni keşfedilen metal alaşımları sınıfından olup yüksek mukavemet, yüksek sertlik, iyi korozyon direnci gibi mekanik özellikleri nedeniyle birçok araştırmacının dikkatini çekmektedir. Çalışmada metal matris olarak yüksek entropili alaşım kullanılmış, ilave edilen pekiştirici ile aşınma direncinin iyileştirilmesi ve böylelikle yüksek aşınma direncine sahip yüksek entropili kompozit malzemenin üretilmesi hedeflenmiştir. Bu çalışmada Kobalt (Co), Krom (Cr), Demir(Fe), Nikel (Ni) elementleri eşmolar oranlarda mekanik alaşımlama cihazında alaşımlandırılmıştır. Yüzey merkezli kübik (YMK) yapıya sahip yüksek entropili alaşıma ağırlıkça %1, %3, %5 oranlarında nanoboyutta Silisyum Karbür (SiC) takviye bileşeni ilave edilerek mekanik alaşımlama cihazında homojen karışımları sağlanmıştır. Hazırlanan toz karışımları spark plazma sinterleme cihazı (SPS) ile sinterlenmiş ve sinterlenen numunelere karakterizasyon çalışmaları taramalı elektron mikroskobu (SEM), X-ışınları difraksiyon cihazı (XRD), optik mikroskop, aşınma ve sertlik cihazları kullanılarak yapılmıştır. Ağırlıkça %1, %3 ve %5 oranlarında nanoboyutta SiC takviye bileşeni ilavesi yapılan CoCrFeNi yüksek entropili metal matrisin ağırlıkça %1 ve %3 SiC takviye fazı ilaveleri ile aşınma direncinde metal matrise kıyasla önemli ölçüde değişiklik olmayarak aşınma direncini olumlu yönde etkilemediği, %5 SiC takviye fazı ilavesi ile aşınma direncinde metal matrise oranla artış olduğu tespit edilmiştir. Üretilen CoCrFeNi yüksek entropili matrisin sertlik değerlerine oranla ağırlıkça %1, %3 ve %5 oranlarında SiC takviye fazı ilavesi ile üretilen kompozit malzemelerin sertlik değerlerinin daha yüksek değerlere sahip olduğu sonucuna varılmıştır.
Özet (Çeviri)
High entropy alloys are a newly discovered class of metal alloys and attract many researchers due to their mechanical properties such as high strength, high hardness and good corrosion resistance. In this study, high entropy alloy was used as metal matrix and it was aimed to improve wear resistance with added reinforcement and in this way to produce high entropy composite material with high wear resistance. In this study, Cobalt (Co), Chromium (Cr), Iron (Fe), Nickel (Ni) elements were alloyed in the mechanical alloying at equimolar ratios. The high entropy alloy which face centered cubic (FCC) structure was obtained by adding 1%, 3%, 5% by weight of nanostructured Silicon Carbide (SiC) reinforce to the homogeneous mixture in the mechanical alloying. The prepared powder mixtures were sintered by spark plasma sintering (SPS). The sintered samples were characterized samples by scanning electron microscopy (SEM), X-ray diffraction (XRD), optical microscope, wear and microhardness devices. The CoCrFeNi that high entropy metal matrix reinforced with 1%, 3% and 5% (%w.) of nanostructured SiC component, has been found that the wear resistance with 1% and 3% by weight of SiC reinforcing phase is not significantly changed compared to metal matrices, the wear resistance of samples were not positively effected, and the wear resistance was increased in the metal matrix by addition of 5% SiC reinforcing phase. It has been concluded that the hardness values of composite materials produced by the addition of SiC reinforcing phase at 1%, 3% and 5% by weight compared to the hardness values of the produced CoCrFeNi high entropy matrix have higher values.
Benzer Tezler
- Sic takviyeli etial 21 esaslı kompozit malzemelerin basınçlı infiltrasyon yöntemi ile üretimi ve özelliklerinin incelenmesi
Production and characteristic analysis of sic-reinforced etial 21 based composite materials by pressure infiltration method
SERKAN ATEŞ
Doktora
Türkçe
2011
Makine MühendisliğiKırıkkale ÜniversitesiMakine Ana Bilim Dalı
PROF. DR. İBRAHİM UZUN
DOÇ. DR. RECEP ÇALIN
- Melt infiltration squeeze casting of sic reinforced functionally graded metal matrix composite processing and characterization
Sıc takviyeli fonksiyonel kademeli metal matris kompozitin eriyik sızma sıkıştırma dökümü ile proses ve karakterizasyonu
ERALP TATLIŞEN
Yüksek Lisans
İngilizce
2024
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ALİ KALKANLI
- SİC takviyeli magnezyum kompozit malzemelerin üretimi ve yüksek sıcaklık özelliklerinin incelenmesi
Production of SİC reinforced magnesium composite materials and investigation of high temperature properties
ALİ MALAK
Yüksek Lisans
Türkçe
2022
Metalurji MühendisliğiMersin ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. HÜSEYİN ŞEVİK
- Değişik oranlarda SiC içeren aluminyum matrisli kompozitlerin birleştirilmesi
Başlık çevirisi yok
ÇİSEM ENGİN
Yüksek Lisans
Türkçe
2007
Metalurji MühendisliğiYıldız Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. AHMET KARAASLAN
- SiC takviyeli alüminyum matriks kompozit üretimi ve mekanik özelliklerinin incelenmesi
Fabrication of SiC reinforced aluminum matrix composite and investigation of its mechanical properties
SERAP KARAKOÇ
Yüksek Lisans
Türkçe
2023
Metalurji MühendisliğiSakarya Uygulamalı Bilimler ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ADEM DEMİR