Comparsion of shear bond strength and microleakage of ceramic flash-free orthodontic brackets
Seramik parlamayan ortodontik bareketlerin mikrosızıntısının ve makaslama bağlanma dayanımının karşılaştırması
- Tez No: 527365
- Danışmanlar: PROF. DR. İLTER UZEL
- Tez Türü: Yüksek Lisans
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental bonding, Dental porselen, Dental stres analizi, Dental sızma, Ortodonti, Ortodontik aygıtlar, Ortodontik braketler, Dental bonding, Dental porcelain, Dental stress analysis, Dental leakage, Orthodontics, Orthodontic appliances, Orthodontic brackets
- Yıl: 2018
- Dil: İngilizce
- Üniversite: İstanbul Yeni Yüzyıl Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Ortodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Özet Bu çalışmanın amacı şunlardır: termal çevrimden sonra kendi kendinidağlayan bir primer (SEP) kullanarak bağlanan seramik APC ortodontikbraketlerin bağlanma dayanımını laboratuvarda saptamak ve ortodontikbraketler arasında termal çevrimi takip eden mikro sızıntıyı değerlendirmek. Malzemeler ve Yöntem: Altmış adet önceden çıkartılmış zarar görmemiş, insana ait küçük azı dişi (N=60, her bir grup n = 20) rastgele üç test grubundan birine bölündü. Buçalışmada kullanılan braketler, kontrol grubu için Berraklığı İleri Seramiklerdahil olmak üzere 3M Unitek, iki çalışma grubu için APC ParlamayanYapışkan Kaplı İleti Seramik ve APC Artı Yapışkan Kaplı İleri Seramik idi.Braketler dişlere yapıştırıldıktan sonra numuneler 5000 çevrim için 5 Co ila 55Co arasında termal olarak çevrildiler. Tüm numuneler, her bir numune içinmakaslama bağlanma dayanımını (SBS) ve mikro sızıntıyı ölçmek için InstronUniversal test makinesi kullanılarak braket çıkartma işlemine tabi tutuldular. Her bir grubun makaslama bağlanma dayanımı ve mikro sızıntısı t-test p<0.05kullanılarak istatistiksel olarak karşılaştırıldı. Test Sonuçları: Berraklığı İleri Seramik braket grubunun ortalama makaslamabağlanma dayanımı, APC Parlamayan (11.6885) ve APC Artı (12.0995) braketgrubu ile karşılaştırıldığında önemli ölçüde yüksek ortalama makaslamabağlanma dayanımına (16.4350) sahiptir (p=0.00 , p=0.00 sırasıyla).Mikro sızıntı, her iki yapışkan ara yüzler için oklüzal taraflarda gözlemlenen ilekarşılaştırıldığında tüm gruplarda dişeti tarafında daha yüksektir. Diş minesineyapışkan ara yüzler yapışkan braket ara yüzlerine göre daha fazla mikro sızıntıgöstermişlerdir. Diğer taraftan kendi kendini dağlayan primer sistemi ilebağlanan braketler dişeti tarafının diş minesine yapışkan ara yüzde önemliölçüde daha yüksek mikro sızıntı göstermiştir. Sonuçlar: %37 fosforik asitli jel ile bağlanan Berraklığı İleri Seramikbraketler, termal çevrimden sonra kendi kendini dağlayan primer sistemi ilebağlanan Seramik APC parlamayan ve Seramik APC Artı braketlere göre dahayüksek SBS ve daha az mikro sızıntı göstermişlerdir.
Özet (Çeviri)
Abstract The aim of this study are: to determine in vitro bond strength of ceramic APCorthodontic brackets when bonded using a self-etching primer (SEP) afterThermo-cycling, and to assess Microleakage following Thermo-cycling underorthodontic brackets. Materials and Method: Sixty previously extracted intact human premolar teeth (N =60, n = 20 pergroup) were randomly allocated to one of three test groups. The brackets usedin this study were 3M Unitek, include Clarity Advanced Ceramic for thecontrol group, APC Flash-free Adhesive-coated Advanced Ceramic and APCPlus Adhesive-coated Advanced Ceramic for the two study group. Afterbrackets were bonded to teeth, specimens were thermocycled between 5 Co to 55 Co for 5000 cycles. All specimens were subjected to bracket removalusing the Instron Universal testing machine to measure shear bond strength(SBS) and Microleakage for each sample.The shear bond strength, and microleakage of each group were statisticallycompared using t-test p<0.05. Results: The mean shear bond strength of Clarity Advanced Ceramic bracketgroup had significantly higher mean shear bond strength value (16.4350) whencompared with APC Flash-free (11.6885) and APC Plus (12.0995) bracketgroup (p=0.00 , p=0.00 respectively).The microleakage is higher at gingival sides in all groups compared with thoseobserved in occlusal sides for both adhesive interfaces. Enamel-adhesiveinterfaces exhibited more microleakage than did the adhesive-bracketinterfaces. Also, brackets bonded with self-etching primer system showedsignificantly higher microleakage at the enamel-adhesive interface of the gingival side. Conclusions: Clarity Advanced Ceramic brackets bonded with 37 %phosphoric acid gel showed higher SBS and less microleakage than CeramicAPC flash-free and Ceramic APC Plus bonded with self-etching primer systemafter Thermo-cycling
Benzer Tezler
- Adeziv kaplı seramik braketler ile geleneksel seramik braketlerin mikrosızıntı açısından karşılaştırılması: Bir mikro bilgisayarlı tomografi çalışması
Comparison of microleakage under adhesive precoated ceramic brackets and conventional ceramic brackets: A microcomputed tomography study
GÖKAY ÜSTDAL
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiHatay Mustafa Kemal ÜniversitesiOrtodonti Ana Bilim Dalı
DR. ÖĞR. ÜYESİ EYÜP BURAK KÜÇÜK
- Ortodontik metal ve seramik braketlerin yapıştırılmasında kullanılan primersiz tek adımlık sistemin mikrosızıntı ve bağlanma dayanımlarının farklı adeziv sistemleri ile in vitro olarak karşılaştırılması
In vitro comparison of microleakage and bond strength of one-step sysyem without primer used in bonding of orthodontic metal and ceramic brackets with different adhesive systems
HANDAN BAYAR BİLEN
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiPamukkale ÜniversitesiOrtodonti Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SERPİL ÇOKAKOĞLU
- Cam iyonomer içerikli farklı yapıdaki biyoaktif restoratif materyallerin süt dişlerindeki mikrosızıntı ve bağlanma kuvvetlerinin karşılaştırılması
Comparison of microleakage and shear bond strength of different bioactive restorative materials contained glass ionomer in primary teeth
İNCİ ÇİL
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiSivas Cumhuriyet ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
PROF. DR. ARİFE KAPTAN
- Er-yag lazer kullanılarak hazırlanan çürükten etkilenmiş dentinde farklı self-adeziv kompozitlerin bağlantılarının ve mikrosızıntılarının karşılaştırılması
A comparison of the different self-adhesive composites' shear bond strength and microleakage on caries affected dentin with using er-yag laser
MAKBULE TUĞBA TUNÇDEMİR
Doktora
İngilizce
2015
Diş HekimliğiSelçuk ÜniversitesiRestoratif Diş Tedavisi ve Endodonti Ana Bilim Dalı
PROF. DR. BORA ÖZTÜRK
- Geleneksel ve tam dijital iş akışı ile gerçekleştirilmiş endirekt braketleme yöntemlerinin, mikrosızıntı ve sıyırma kuvveti dayanım parametreleri açısından karşılaştırılması
Comparison of indirect bonding methods performed with conventional and fully digital workflows in terms of microleakage and shear bond strength parameters
SELAHATTİN CEM ÜNSAL
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş Hekimliğiİstanbul ÜniversitesiOrtodonti Ana Bilim Dalı
DOÇ. DR. MUHSİN ÇİFTER