Hibrit plazma ark kaynağı (HPAK)), gaz metal ark kaynağı ((GMAK) ve soğuk metal transfer kaynağı (CMT) yöntemleri ile ARMOX 500T zırh çeliğinin kaynak edilebilirliğinin araştırılması
Investigation of weldability of ARMOX 500T armor steel with hybrid plasma arc welding (HPAW), gas metal arc welding (GMAW) and cold metal transfer welding (CMT) methods
- Tez No: 536393
- Danışmanlar: DR. ÖĞR. ÜYESİ ÖMER SALTUK BÖLÜKBAŞI
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2019
- Dil: Türkçe
- Üniversite: İskenderun Teknik Üniversitesi
- Enstitü: Mühendislik ve Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İleri Metalurji ve Malzeme Teknolojileri Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 130
Özet
Savunma endüstrisinde zırh malzemesi olarak kullanılan ARMOX 500T zırh çeliğinin, Hibrit Plazma Ark Kaynağı (HPAK), Gaz Metal Ark Kaynağı (GMAK) ve Soğuk Metal Transfer Kaynağı (CMT) yöntemleri ile kaynak edilebilirliği araştırılmış ve elde edilen sonuçlar analiz edilerek birbirleri ile kıyaslanmıştır. Kaynak işlemleri robotik sistemli kaynak makineleri ile gerçekleştirilmiştir. Bu tez çalışmasında, ARMOX 500T zırh çeliği birleşim bölgesinde ESAB OK Autrod 16.95 ilave dolgu teli kullanarak farklı kaynak yöntemleri ile birleştirilmesi sonucunda oluşan metalurjik ve mekanik özellikler araştırıldı. Kaynak bölgesi ve kaynaktan etkilenen bölgede (ITAB) oluşan içyapı özelliklerini ve difüzyon durumunu metalografik olarak gözlemlemek için, optik mikroskop ile SEM görüntüleri incelenmiş ve kaynak sonrası oluşan kimyasal dağılımı analiz etmek için EDS analizi yapılmıştır. X-ışını Radyografik Muayene ile kaynak hataları olarak adlandırılan çatlak, gözenek, gaz boşluğu vb. olumsuzluklar test edilmiştir. Kaynak yöntemlerinin mekanik özelliklere etkilerini belirlemek amacı ile kaynaklı numunelere vickers sertlik, çekme, eğme ve çentik darbe testleri uygulanmıştır. Optik mikroskop ve SEM görüntülerinde kaynak difüzyon durumları araştırılmıştır. HPAK ve GMAK kaynak yöntemlerinde ana malzeme ve kaynak metali arasında difüzyon oluşmuştur. CMT kaynak yönteminde ise yeterli difüzyon olmadığı görülmüştür. Bu çalışmada uygulanan kaynak yöntemlerine bağlı olarak oluşan sıcaklığın difüzyon durumlarını etkilediği ve bununda, deneysel olarak birleştirilen malzemenin mekanik özelliklerine tesir ettiği gözlemlenmiştir. Savunma sanayinde kullanılan ARMOX 500T zırh çeliğini her üç kaynak yöntemi ile deneysel olarak birleştirme gerçekleştirilmiştir.
Özet (Çeviri)
ARMOX 500T armor steel, which is used as an armor material in defense industry, was investigated with Hybrid Plasma Arc Welding (HPAW), Gas Metal Arc Welding (GMAW) and Cold Metal Transfer Welding (CMT) methods and the results were analyzed and compared with each other. Welding operations were carried out with robotic system welding machines. In this thesis, metallurgical and mechanical properties of ARMOX 500T armor steel joining together with different welding methods by using ESAB OK Autrod 16.95 additional filler wire were investigated. In order to observe the metallurgical features and diffusion status of the source region and source affected area (ITAB), SEM images were examined by optical microscope and EDS analysis was performed to analyze the chemical distribution after welding. X-ray Radiographic Inspection with welding defects called crack, pore, gas gap etc. negativity has been tested. To determine the effects of welding methods on mechanical properties, vickers hardness, tensile, bending and notch impact tests were applied to the welded samples. Source diffusion conditions on both optical microscope and SEM images were investigated. In HPAW and GMAW welding methods, diffusion has occurred between the main material and the weld metal. There was not enough diffusion in the CMT welding method. In this study, it has been observed that the temperature formed due to the welding methods applied affects the diffusion states and thus the mechanical properties of the experimentally joined material. ARMOX 500T armor steel used in the defense industry was experimentally combined with all three welding methods.
Benzer Tezler
- Ramor 500 zırh çeliğinin farklı ark ergitme kaynak birleştirmelerinin metalurjik ve mekanik özelliklerinin incelenmesi
Study on the effect of different arc welding techniques on the metallurgical and mechanical properties of ramor 500 armour steel
SELÇUK BAYAR
Yüksek Lisans
Türkçe
2019
Metalurji Mühendisliğiİskenderun Teknik Üniversitesiİleri Metalurji ve Malzeme Teknolojileri Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ALİ GÜNEN
- Microstructural and mechanical characterization of duplex stainless steel grade 2205 joined by hybrid plasma and gas metal arc welding
Hibrit plazma ve gaz metal ark kaynağı ile birleştirmiş 2205 dubleks paslanmaz çeliklerinin mikroyapı ve mekanik karakterizasyonu
BURCU TOLUNGÜÇ
Yüksek Lisans
İngilizce
2012
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Bölümü
PROF. DR. CEMİL HAKAN GÜR
PROF. DR. RIZA GÜRBÜZ
- Kinetics and microstructural analysis of fatigue fracture progress in weld joints of duplex stainless steel grade 2205
2205 sınıfı dubleks paslanmaz çelik alaşımı kaynaklı birleştirmelerinde yorulma çatlağı ilerlemesinin kinetik ve iç yapı analizi
KORAY YURTIŞIK
Doktora
İngilizce
2013
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. RIZA GÜRBÜZ
- Investigation of key-hole weldability of line pipe steel grade X70M in terms of fracture toughness
X70M sınıfı boru hattı çeliklerinin anahtar deliği metodu ile kaynaklanabilirliğinin kırılma tokluğu yönünden incelenmesi
MEHMET ÇAĞIRICI
Yüksek Lisans
İngilizce
2017
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. CEMİL HAKAN GÜR
DR. KORAY YURTIŞIK
- An investigation on fatigue crack propagation in gas metal and hybrid plasma-gas metal arc weldments of AA5083-H111
Gaz metal ve hibrit plazma-gaz metal ark yöntemleriyle AA5083-H111 alaşımında yapılan kaynakların yorulma çatlağı ilerlemesi bakımından incelenmesi
KEMAL OKAN
Yüksek Lisans
İngilizce
2015
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. RIZA GÜRBÜZ
DR. KORAY YURTIŞIK