Sol-jel ve katıhal reaksiyon yöntemleri ile üretilen, Co ve CoFe2O4 katkılı polikristal YBCO-123 süperiletkeninin yapısal, elektrik ve mekanik özelliklerinin karakterizasyonu

The characterization of structural, electric and mechanical properties of Co and CoFe2O4 doped polycrystal YBCO-123 superconductors produced by sol-gel and solid state reaction methods

  1. Tez No: 548128
  2. Yazar: ABDULRHMAN RAJAB ALI NEFROW
  3. Danışmanlar: PROF. DR. ÖZGÜR ÖZTÜRK
  4. Tez Türü: Doktora
  5. Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2019
  8. Dil: Türkçe
  9. Üniversite: Kastamonu Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Fizik Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 116

Özet

Bu çalışmada, YBa2Cu3-x(Co)xO7-δ ve YBa2Cu3-x(CoFe2O4)xO7-δ süperiletken numuneleri katıhal reaksiyonu ve sol-jel yöntemleri kullanılarak üretilmiştir (x = 0, 0.05, 0.10 ve 0.20). Numunelerin hazırlanmasında; katıhal reaksiyon yöntemi için oksit bazlı bileşikler, sol-jel yönteminde asetat bazlı bileşikler kullanılmıştır. Tüm numuneler üretim aşamasında, 930 °C'de 24 saat tavlamanın ardından 5 saat süreyle 500°C'de oksijen ortamında bekletilmiştir. Üretilen numunelerin yapısal özelliklerinin belirlenebilmesi için X-ışınları kırınım (XRD) desenleri, taramalı elektron mikroskobu (SEM) görüntüleri, enerji dağılım spektroskopi (EDS) verileri analiz edilmiştir. Bunun yanı sıra, elektriksel ve mekanik özelliklerin tespiti için sıcaklığa bağlı direnç (R-T) ve Vickers mikrosertlik ölçümleri gerçekleştirilmiştir. XRD sonuçlarında numunenin ortorombik yapıda olduğu sonucuna ulaşılırken elektriksel ölçüm sonuçlarında tüm numunelerin süperiletken özellik gösterdiği görülmüştür. Her iki yöntemle üretilen numuneler için de katkılama işlemi süperiletken kritik sıcaklık değerini düşürmüştür. Ayrıca Vickers mikrosertlik değerlerinde meydana gelen değişimler incelenmiştir. Mikrosertlik analizleri sonucunda Co katkılı numunelerin mikrosetlik davranışlarında değişim olmazken, CoFe2O4 katkılı numunelerin sertlik davranışlarının değiştiği görülmüştür. Katkısız numune TÇBE davranışı gösterirken CoFe2O4 katkılı numunelerde ÇBE davranışı gözlenmiştir.

Özet (Çeviri)

In this study, YBa2Cu3-x(Co)xO7-δ and YBa2Cu3-x(CoFe2O4)xO7-δ superconductor samples were produced by using solid state reaction and sol-gel methods (x= 0, 0.05, 0.10 ve 0.20). In the preparation of the samples; oxide based compounds were used for the solid state reaction method, while acetate based compounds were used in the sol-gel method. All samples were sintered at 930 °C for 24 hours and 5 hours at 500 °C in oxygen atmosphere. X-ray diffraction (XRD) patterns, scanning electron microscopy (SEM) images, energy distribution spectroscopy (EDS) data were analyzed in order to determine the structural properties of the produced samples. In addition, temperature-dependent resistance (R-T) and Vickers microhardness measurements were performed to determine electrical and mechanical properties. XRD results showed that the sample was orthorhombic, and all samples showed superconductive properties in electrical measurement results. For the samples produced by both methods, the doping process reduced the superconducting critical temperature value. In addition, changes in Vickers microhardness values were investigated in detailed. As a result of the microhardness analysis, it was seen that while the microhardness behavior of the Co doped samples did not change, the hardness behaviors of the CoFe2O4 doped samples was changed. While the microhardness behavior of undoped sample was RISE, CoFe2O4 doped samples exhibited ISE behavior.

Benzer Tezler

  1. Synthesis and characterization of strontium aluminate based nanophospors

    Nano boyutta stronsiyum aluminat esaslı fosfor sentezi ve karakterizasyonu

    MEHMET DURMUŞ ÇALIŞIR

    Yüksek Lisans

    İngilizce

    İngilizce

    2014

    Mühendislik Bilimleriİstanbul Teknik Üniversitesi

    Nanobilim ve Nanomühendislik Ana Bilim Dalı

    YRD. DOÇ. DR. NURİ SOLAK

  2. Formation of SrTiO3[TiO2] ceramic composites at low temperatures

    Düşük sıcaklıklarda SrTiO3[TiO2] seramik kompozitlerin oluşumu

    ESİN KARATAŞ

    Yüksek Lisans

    İngilizce

    İngilizce

    2021

    Seramik Mühendisliğiİzmir Yüksek Teknoloji Enstitüsü

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. ÇEKDAR VAKIF AHMETOĞLU

    DR. ÖĞR. ÜYESİ UMUT ADEM

  3. BaO-CeO2-SrO üçlü oksit sisteminde faz dengelerinin deneysel incelenmesi

    Experimental phase studies in the BaO-SrO-CeO2 oxide system

    HANİFİ ERAY KORKMAZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ NURİ SOLAK

  4. LaCaMnO nanotellerin ve nanoparçacıkların sol-jel yöntemi ile elde edilmesi ve özelliklerinin incelenmesi

    Production of LaCaMnO nanowires and nanoparticles by sol-gel method and their properties

    VEDAT YAĞMUR

    Yüksek Lisans

    Türkçe

    Türkçe

    2008

    Fizik ve Fizik Mühendisliğiİnönü Üniversitesi

    Katıhal Fiziği Ana Bilim Dalı

    DOÇ. DR. FUNDA ERSOY ATALAY

  5. Investigation of infrared phosphorescence properties of chromium doped lanthanum gallogermanate phosphors sythesized by sol-gel method

    Sol-gel yöntemi ile sentezlenen krom katkılı lantan galogermanat fosforlarının kızılötesi fosforesans özelliklerinin incelenmesi

    BURCU CAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2020

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ NURİ SOLAK