Mekanik alasımlama yöntemi ile niyobyum ilaveli cualni sekil hafızalı alasımların üretimi karakterizasyonu ve asınma performanslarının incelenmesi
The investigate of characterization and wear performance of niobium add in cualni shape memory alloy produced with mechanical alloying method
- Tez No: 561655
- Danışmanlar: PROF. DR. DURSUN ÖZYÜREK
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: ġekil hafızalı alaĢım, aĢınma performansı, toz metalurjisi, mekanik alaĢımlama, Cu-Al-Ni
- Yıl: 2019
- Dil: Türkçe
- Üniversite: Karabük Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 110
Özet
Bu çalıĢmada, Cu14Al4Ni alaĢımının farklı miktarlarda Nb ilave edilerek, Nb miktarının aĢınma davranıĢı üzerine etkileri incelenmiĢtir. ÇalıĢmanın ilk aĢamasında, mekanik alaĢımlama ile üretilen Cu14Al4Ni alaĢımında, farklı mekanik alaĢımlama sürelerinin alaĢımın toz boyutu üzerindeki etkisi araĢtırılmıĢtır. Üretilen alaĢım tozları, soğuk pres ile Ģekillendirilerek sinterlenmiĢtir. Sinterlenen alaĢımlar 900 °C 1 saat ısıl iĢlem yapıldıktan sonra suda hızlı soğutulmuĢtur. Üretilen Cu14Al4Ni alaĢımları yoğunluk, sertlik, toz boyut analizi ve aĢınma testleri yapılmıĢtır. Ayrıca üretilen alaĢımların, termal analizleri; (DTA/DSC), x-ıĢını kırınımı (XRD) ve mikroyapı incelemeleri (SEM+EDS) yapılmıĢtır. Krakterizasyon çalıĢmaları tamamlandıktan sonra pin-on-disk tipi aĢınma cihazında, aĢınma testleri yapılmıĢtır.AĢınma testlerinde üç farklı yük, beĢ farklı kayma mesafesi ve 1 ms-1 kayma hızı test edilmiĢtir. ÇalıĢmanın ikinci aĢamasında ise, Cu14Al4Ni alaĢımına farklı miktarlarda Nb ilave edilerek, yeni alaĢım sistemeleri elde edilmiĢtir. Üretilen alaĢım tozları soğuk preslendikten sonra iki saat sinterlenmiĢtir. Sinterleme iv iĢleminden sonra alaĢımlar 900 °C 1 saat süre ısıl iĢlem uygulanarak suda hızlı soğutulmuĢtur. Yapılan çalıĢmalar sonucunda Cu14Al4Ni alaĢımlarında mekanik alaĢımlama süresi arttıkça toz boyutunun azaldığı belirlenmiĢtir. Yük miktarındaki artıĢ kütle kaybını atırmaktadır. Kütle kaybı Nb ilavesi arttıkça azaldığı görülmüĢtür. AĢınma oranlarıda artan Nb oranı ile azalma göstermiĢtir.
Özet (Çeviri)
In this study, Cu14Al4Ni alloy, one of the shape memory alloys, was produced by mechanical alloying at different times and the abrasion performances were investigated. In the first stage of the study, the effect of different mechanical alloying times on the powder size of the alloy was determined in Cu14Al4Ni alloy produced by mechanical alloying. The alloy powders produced were sintered by forming with cold press. The sintered alloys were cooled rapidly at 900 ° C after 1 hour of heat treatment. Cu14Al4Ni alloys produced density, hardness, powder size analysis and abrasion tests were performed. Alloys produced were also analyzed by thermal analysis (DTA/DSC), x-ray diffraction (XRD) and microstructure studies (SEM+EDS). After the completion of the crackerization studies, wear tests were carried out on the pin-on-disc type wear device. As a result of the studies, it was determined that the powder size decreases with increasing mechanical alloying time in Cu14Al4Ni alloys. vi In the second stage of the study, mechanical alloying (MA) time was determined as 7.5 hours. New alloy systems were obtained by adding different amounts of Nb to Cu14Al4Ni alloy. The alloy powders were sintered for two hours after cold pressing. After sintering, the alloy was cooled rapidly by heat treatment with 900 °C for 1 hour. The increase in load amount increases the mass loss. It was observed that mass loss decreased as Nb addition increased. Wear rates also decreased with increasing Nb ratio. Key Word : Shape memory alloys, mechanical alloying, wear behavior, powder metallurgy, Cu-Al-Ni. Science Code : 701.3.019
Benzer Tezler
- Toz metalurjisi ile üretilmiş Ti-xNB alaşımlarının yüzey özelliklerinin borlama yöntemi ile geliştirilmesi
Improvement of surface properties of Ti-xNB alloys produced by powder metallurgy with boriding
BATUHAN SORUŞBAY
Yüksek Lisans
Türkçe
2023
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU
ÖĞR. GÖR. FAİZ MUHAFFEL
- Mechanochemical synthesis and characterization investigations of some refractory metal silicides
Bazı refrakter metal silisitlerin mekanokimyasal yöntemle sentezlenmesi ve karakterizasyonu
DİDEM OVALI DÖNDAŞ
Doktora
İngilizce
2018
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA LUTFİ ÖVEÇOĞLU
- Biyomedikal uygulamalar için üretilen alaşımların yüzey özelliklerinin geliştirilmesi
Development of the surface properties of alloys that produced for biomedical applications
ÖZGE ÖZEN
Yüksek Lisans
Türkçe
2019
Metalurji MühendisliğiDokuz Eylül ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ESRA DOKUMACI
- Ti-nb esaslı alaşımların implant uygulamaları için gözenekli üretim ve biyoaktif kaplama ile özelliklerinin geliştirilmesi
Improving the properties of ti-nb based alloys with porous production and bioactive coating for implant applications
EREN YILMAZ
Doktora
Türkçe
2019
Metalurji MühendisliğiSakarya Uygulamalı Bilimler ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. FEHİM FINDIK
PROF. DR. HAMİT ÖZKAN GÜLSOY
- Inconel 718 süper alaşımının nitrürlenmesi
Nitriding of inconel 718 superalloy
TUNCAY TURAN
Yüksek Lisans
Türkçe
2013
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU