İleri teknoloji metalik kaplama tozlarının üretilmesi ve kaplanabilirliğinin araştırılması
The production and coating of advanced technology metallic coating powder
- Tez No: 614412
- Danışmanlar: PROF. DR. HALİS ÇELİK
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Toz Metalurjisi, Gaz Atomizasyonu, Nikel, Kaplama, HVOF, Powder Metallurgy, Gas Atomization, Nickel, Plating, HVOF
- Yıl: 2019
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Teknolojileri Ana Bilim Dalı
- Bilim Dalı: Üretim Metalurjisi Bilim Dalı
- Sayfa Sayısı: 106
Özet
Bu tez çalışmasının amacı; Nikel esaslı saf yüzey kaplama tozlarının üretilmesi ve üretilen Nikel esaslı tozların kaplanabilirliğini araştırmaktır. Nikel esaslı tozlar (Ni, Si, B, Cr, Fe, C) toz üretim yöntemlerinden gaz atomizasyon yöntemi kullanılarak düşey gaz atomizasyon ünitesinde 1650-1700 ºC sıcaklıkta, 22-30 bar arası basınçta üretimi gerçekleştirilmiştir. Üretilen tozların genelinin küresel yapıda olduğu görüldü. Yapılan toz boyut analizi incelenmesi sonucu ortalama toz boyutunun 90-120 µm arasında olduğu anlaşılmıştır. Optimum şartlarda üretilen tozların mikroyapıları hakkında bilgi sahibi olmak için Taramalı Elektron Mikroskobu (SEM), EDX, X-Işını (XRD) incelemeleri yapılmıştır. Üretimi gerçekleştirilen Nikel esaslı tozlar; 1 numaralı toz (Ni1Si0,8B2P), 2 numaralı toz (Ni2Si1,8B10Cr2Fe0,6C), 3 numaralı toz (Ni3Si2,8B17Cr4Fe0,8C)'dur. Bu üç farklı Nikel esaslı toz termal sprey kaplama yöntemlerinden Yüksek Hızlı Oksi Yakıt (HVOF) yöntemi kullanılarak Manganlı altlık malzeme yüzeyine kaplama yapılmış olup, üretilen Nikel esaslı tozların kaplanabilirliği incelenmiştir. Aynı zamanda bir diğer amaç aşınmaya, korozyona, ısıya karşı dayanımını ve oksitlenmeye karşı direnci artırmaktır. Parametre olarak sabit kaplama parametreleri kullanılmıştır. Yapılan kaplamaların mikro yapıları hakkında bilgi sahibi olmak için Taramalı Elektron Mikroskobu (SEM), EDX, X-Işını (XRD) incelemeleri yapılmıştır. Yapılan kaplamaların sertliğini öğrenmek için kesit yüzeylerinden mikro sertlik ölçümü yapılmıştır. Yapılan incelemeler sonucu 1 numaralı toz ile yapılan kaplamanın ortalama sertliği 440 HV'dir. 2 numaralı toz ile yapılan kaplamanın ortalama sertliği 520 HV'dir. 3 numaralı toz ile yapılan kaplamanın çok ince olduğu görülmüştür.
Özet (Çeviri)
The aim of this thesis is to study the production of pure surface nickel-based powders and to investigate the coating ability of nickel-based powders. Nickel-based powders (Ni, Si, B, Cr, Fe, C) were produced in the vertical gas atomization unit at 1650-1700 ºC temperature and 22-30 bar pressure using gas atomization method. It was observed that the produced powders were generally spherical. The dust size analysis revealed that the average dust size was between 90-120 µm. Scanning Electron Microscopy (SEM), EDX, X-Ray (XRD) investigations were performed to obtain information about the microstructures of powders produced under optimum conditions. Nickel based powders that were produced are as follows: No. 1 powder (Ni1Si0,8B2P), No. 2 powder (Ni2Si1,8B10Cr2Fe0,6C), No. 3 powder (Ni3Si2,8B17Cr4Fe0.8C). Using the, High Velocity Oxygen Fuel (HVOF) thermal spray coating method, the nickel-based powders were applied to the surface of Manganese based material and the coating ability of the Nickel based powders was examined. In addition, another purpose of this paper is to identify any increases in endurance against abrasion, corrosion, and to provide heat resistance and resistance to oxidation. Constant coating parameters were used as parameters. Investigations of Scanning Electron Microscopy (SEM), EDX, X-Ray (XRD) were used to get information about the microstructures of the coatings. In order to learn the hardness of the coatings, micro hardness measurements were employed on the cross-sectional surfaces. As a result of the researches, the average hardness of the coating made with powder No. 1 is 440 HV and the average hardness of the coating made with powder No. 2 is 520 HV but the coating that made with powder No.3 seen very thin.
Benzer Tezler
- Kendiliğinden ilerleyen yüksek sıcaklık sentezi ile üretilen AlCoxCrFeNi yüksek entropili alaşım sistemindeki kobalt oranın değişiminin incelenmesi
Examination of reducing cobalt ratio in AlCoxCrFeNi high entropy alloy system manufactured by self-propagating high temperature synthesis method
MELİH YETİŞ
Yüksek Lisans
Türkçe
2020
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. CEVAT BORA DERİN
DR. ÖĞR. ÜYESİ GÜL İPEK SELİMOĞLU
- Development and characterization of high entropy (HfTiZrMn/Cr)B2 based ceramics
Yüksek entropi (HfTiZrMn/Cr)B2 bazlı seramiklerin geliştirilmesi ve karakterizasyonu
İLAYDA SÜZER
Yüksek Lisans
İngilizce
2022
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. DUYGU AĞAOĞULLARI
- Ultrasonik sprey piroliz tekniğiyle küresel gümüş nano-partiküllerinin üretimi
Production of spherical silver nano-particles by ultrasonic spray pyrolysis technique
ELİF YAZICI
Yüksek Lisans
Türkçe
2009
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. SEBAHATTİN GÜRMEN
- Fabrication of vanadium and niobium borides via milling-assisted solid state synthesis methods and sintering techniques
Vanadyum ve niyobyum borürlerin öğütme destekli katı hal sentezleme yöntemleri ve sinterleme teknikleri ile üretimi
ÖZGE BALCI
Doktora
İngilizce
2015
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Bölümü
PROF. DR. İSMAİL DUMAN
- Bakır/gümüş/çinko oksit (CuAg/ZnO) partiküllerinin ultrasonik sprey piroliz yöntemiyle üretimi
Production of CuAg/ZnO nanocomposite particles by ultrasonic sprey pyrolysis
TOLGA ÇAKMAK
Yüksek Lisans
Türkçe
2016
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. SEBAHATTİN GÜRMEN