Sülfürik asit korozyonuna uğramış ince cidarlı çelik tankların burkulma davranışı

Buckling behaviour of sulfuric acid corroded thin-walled cyrindrical steel shells

  1. Tez No: 628964
  2. Yazar: MUHAMMET ÇİNAR
  3. Danışmanlar: DR. ÖĞR. ÜYESİ MAHMUT KILIÇ
  4. Tez Türü: Yüksek Lisans
  5. Konular: İnşaat Mühendisliği, Civil Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2020
  8. Dil: Türkçe
  9. Üniversite: Atatürk Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Yapı Bilim Dalı
  13. Sayfa Sayısı: 105

Özet

Bu araştırma kapsamında sülfürik asit korozyonuna maruz bırakılan ince cidarlı silindirik tankların burkulma davranışı incelenmiş, oluşan burkulma performansı kayıpları Karbon Fiber Takviyeli Polimer (CFRP) ile güçlendirilmek suretiyle geri kazanımı araştırılmıştır. Bu maksatla üç grup silindirik tank modelleri hazırlanmıştır. İlk grup karbon lifli polimer (CFRP) uygulaması yapılmayan silindir numuneleri içerirken, ikinci grup tüm yüzey karbon lifli polimer uygulaması yapılmış numuneleri ve üçüncü grup ise değişken karbon lifli polimer uygulaması yapılan silindirik numuneleri teşkil etmektedir. Deneyler 800x400x0.45 mm boyutlarında 12 adet model ile yapılmıştır. Hazırlanan çözeltiler sızdırmazlıkları sağlanan deney modellerinin içine tam dolu ve 1/2 dolu vaziyette 24 saat sülfürik asit çözeltisine maruz bırakılarak deneyler gerçekleştirilmiştir. 24 saat sonunda çözeltisi boşaltılan silindirik numunelerin ağırlık değişimleri tespit edilerek kütle kayıpları belirlenmiştir. Korozyon sonrası silindir boyunca, silindirin ½ yüksekliğinde ve orta noktasından 10cm'lik kısmına CFRP uygulaması yapılmıştır. CFRP kullanımının maliyetinin fazla olması nedeniyle dayanım kayıplarının en ekonomik yönden geri kazanımı hedeflenmektedir. Hazırlanan model numuneler deney düzeneğine yerleştirilerek sızdırmazlıkları sağlanmıştır. Silindirik tanklar için özel tanzim edilmiş vakumlu sistem deney düzeneği ile test edilen modellere ilişkin veriler toplama ünitesiyle kayıt altına alınmıştır. Deformasyonlar, gerinim ölçerler (strain gauge) ve deformasyon ölçüm cihazları (LVDT) yardımıyla ölçülerek veri toplama cihazı (data logger) yardımıyla bilgisayar ortamına aktarılmıştır. Verilerin toplanmasından sonra ilgili grafikler çizdirilmiştir. Böylelikle asit korozyonuna uğramış bir malzemenin geri kazanımı amaçlanmaktadır. Korozyon etkisine maruz kalan numunelerin CFRP uygulaması yapılarak kaybettikleri dayanımlarını %20-60 oranında geri kazandıkları görülmüştür.

Özet (Çeviri)

In this research, buckling behavior of thin-walled cylindrical tanks exposed to sulfuric acid corrosion was investigated and buckling performance losses were recovered by reinforcing with CFRP. Experiments planned in three groups for this purpose include the first group of without corrosion control samples, and the second group includes full CFRP models and last group variable CFRP application groups. The experiments were carried out with 12 models of 800x 400x0.45 mm dimensions. The prepared solutions were applied to the sealed test models as full and 1/2 filled and exposed to sulfuric acid solution for 24 hours, and the experiments were carried out. The mass losses were determined by determining the weights of the cylindrical samples which were discharged after 24 hours. After the corrosion, CFRP was applied to the cylinder, ½ height of the cylinder and 10cm from its midpoint. Prepared model samples were placed in the test apparatus and sealed. Prepared model samples were placed in the test apparatus and sealed. In the experiments, vacuum was made with the help of the vacuum pump, and data were recorded with the help of load cell. Deformations were measured by strain gauges and LVDT and transferred to the computer by means of a data collection device (datalogger). After data collection, vacuum-displacement plots are plotted. Thus, it is aimed to recover a material that has undergone acid corrosion. It was observed that the samples exposed to corrosion effect recovered their lost strength by CFRP application by 20-60%.

Benzer Tezler

  1. Farklı asitlerle yapılan anodik oksidasyon işlemlerinin 2024 ve 7075 alüminyum alaşımlarının korozyon direncine etkisi

    The effect of anodic oxidation treatments with different acids on the corrosion resistance of 2024 and 7075 aluminum alloys

    YUSUF TOLUNAY KOZAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ CEVAT FAHİR ARISOY

  2. Termik santrallerin döner tip hava ısıtıcılarında kullanılan ısı değiştirici plakalar için emaye kaplama optimizasyonu

    Optimization of enamel coatings on heat exchanger plates used in rotary air preheaters of thermal power plants

    ERDEM GÜNGÖR

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. HÜSEYİN ÇİMENOĞLU

    DOÇ. DR. ERDEM ATAR

  3. Bazı benzoazol türevlerinin sülfürik asit ortamında çeliğin korozyonuna inhibitör etkilerinin kunantum kimyasal incelemesi

    Determination of quantum chemical of inhibition of type 304 stainless steel corrosion in 2M sulfuric acid by some benzoazoles

    FUNDA BAYER

    Yüksek Lisans

    Türkçe

    Türkçe

    2005

    KimyaEskişehir Osmangazi Üniversitesi

    Kimya Ana Bilim Dalı

    PROF.DR. GÖZEN BEREKET

  4. Asi̇tle yikama i̇şlemi̇nde kullanilabi̇lecek i̇nhi̇bi̇törleri̇n i̇ncelenmesi̇

    The investigation of inhibitors that can be used in process of acid leaching

    AYŞE YAVAŞ BAYINDIR

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Kimya MühendisliğiGazi Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. MÜBECCEL ERGUN