Yüzey çatlaklı hibrit kompozitlerin mekanik özelliklerinin araştırılması
Research of mechanical properties of hybrid composites with surface cracks
- Tez No: 629814
- Danışmanlar: DR. ÖĞR. ÜYESİ LÜTFİYE DAHİL
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Hibrit kompozit, Cam elyaf, Karbon Elyaf, Yüzey Çatlağı, Hybrid Composite, Glass Fiber, Carbon Fiber, Surface Crac
- Yıl: 2020
- Dil: Türkçe
- Üniversite: İstanbul Aydın Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Makine Mühendisliği Bilim Dalı
- Sayfa Sayısı: 76
Özet
Hızla gelişen teknoloji ve üstün malzeme arayışı sebebiyle son yıllarda kullanılmakta olan en önemli malzemelerden biri kompozittir. Kompozit, iki ya da daha fazla farklı malzemenin makro seviyede birleşmesiyle, ortaya yeni bir malzeme çıkarma amacıyla üretilen malzemedir. Kompozit malzemelerin çok tercih edilmesinin nedeni, ihtiyaca göre matris ve takviye bileşenlerinin belirlenebilmesidir. Kompozit malzemeler, otomotiv, savunma ve uzay sanayi, havacılık ve spor malzemeleri gibi alanlarda sıklıkla kullanılmaktadır. Bu çalışmada, vakum infüzyon yöntemi ile 8, 10 ve 12 tabakalı olmak üzere değişik kalınlıklarda 3 adet cam – karbon elyaf takviyeli hibrit kompozit plaklar üretilmiştir. Bu plaklardan standartlara uygun bir şekilde yakma, charpy ve çekme deneyi numuneleri elde edilmiştir. Kompozit malzemelerde yüzey çatlağının etkisini araştırmak için çekme deneyi numunelerinin yarısına yüzey çatlağı açılmıştır. Ardından numunelerin fiber hacim oranlarını, kırılma enerjisi, tokluğu ve mekanik özelliklerini belirlemek için numuneler üzerine yakma, charpy ve çekme testi uygulanmıştır. Uygulanan testlerin sonucunda tabaka sayısı arttıkça yük dayanımının, darbe enerjisinin ve tokluğunun arttığı, yüzey çatlağının yük dayanımını önemli ölçüde düşürdüğü ve özellikle yüzey çatlaklı numunelerde kırılmanın çatlak bölgesinde meydana geldiği gözlemlenmiştir. Aynı zamanda charpy testi sonucunda numunelerde matris hasarı ve fiber kopması, çekme testi sonucunda ise fiber kopması ve yüksek oranda delaminasyon gözlemlenmiştir.
Özet (Çeviri)
Because of the fast technology development and superior materials research, composites have become one of the most commonly used materials in recent years. Composite is a result of two or more material's macro level combination, to gain a new material. The reason of preferability of composites is the ability of choosing matrix and reinforcement phases according to the need. Composite materials are commonly used in automotive, defence, space, aviation and sports materials industry. In this study, 8, 10 and 12 layered, glass – carbon fiber reinforced, hybrid composite plaques were produced with vacuum infusion technique. Burning, charpy and tension test samples were obtained from the plaques according to the standarts. Half of the tension test samples were with surface cracks to research the affect of the cracks. Then, to determine fiber volüme ratios, fracture energies, toughnesses and mechanical properties of the samples, burning, charpy and tension tests were performed. Results of the tests showed that as the number of layers increased, durability, impact energy and toughness were increased, surface cracks significantly lowered the durabilty of the samples and fracturing occured in the surface crack area. At the same time, matrix failure and fiber fracture were detected at the charpy test results and fiber fracture and delamination were detected at the tension test results.
Benzer Tezler
- Yüzey çatlaklı ve çatlaksız ±55° filaman sarım cnt takviyeli ctp kompozit boruların mekanik özelliklerinin ve iç basınç etkisi altındaki yorulma davranışının araştırılması
Investigation of mechanical properties and fatigue behavior under internal pressure effect of the ±55° fi̇lament wi̇ndi̇ng cnt reinforced ctp composite pi̇pe wi̇th and wi̇thout surface crack
MUSTAFA TAŞYÜREK
Doktora
Türkçe
2014
Mühendislik BilimleriSelçuk ÜniversitesiMakine Eğitimi Ana Bilim Dalı
PROF. DR. NECMETTİN TARAKÇIOĞLU
- Yüzey çatlaklı filaman sarım CTP kompozit boruların korozif ortamda yorulma davranışı
Corrosion fatigue behavior of filament wound pipes with surface crack
ÖMER SİNAN ŞAHİN
Doktora
Türkçe
2004
Makine MühendisliğiSelçuk ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF.DR. AHMET AVCI
- Yüzey çatlaklı filaman sarım CTP boruların iç basınç altında yorulma davranışı
Fatigue behaviour of filament would GRP pipe with surface crack under internal pressure
AHMET SAMANCI
Doktora
Türkçe
2004
Makine MühendisliğiSelçuk ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ.DR. NECMETTİN TARAKÇIOĞLU
- Yüzey çatlaklı kompozit malzemelerde yorulma çatlak büyümesi ve tabaka ayrılması
Surface crack propagation of composite plates with axial fatique
İBRAHİM ALDENİZ
Yüksek Lisans
Türkçe
1992
Makine MühendisliğiSelçuk ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. AHMET AVCI
- Yüzey çatlaklı cam takviyeli plastiklerde gerilmeli korozyon
Stress corrosion of glass reinforced plastic with surface crack
AHMET AKDEMİR