Hidroksiapatit esaslı/perlit hibrit biyoseramik kompozit kaplamaların hidrotermal yöntem ile uygulanması ve karakterizasyonu
Application and characterization of hydroxyapatite based / perlite hybrid bioceramic composite coatings by hydrothermal method
- Tez No: 648537
- Danışmanlar: PROF. DR. MEHTAP MURATOĞLU
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2020
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 90
Özet
Bu çalışmada, titanyum alaşımı üzerine hidrotermal yöntem kullanılarak hidroksiapatit-perlit ve hidroksiapatit-perlit-kitosan kaplanması hedeflenmektedir. Yüzeyi temizlenmiş Ti6Al4V alaşımları A ve B grubu olarak sınıflandırılmıştır. Kalsiyum kaynağı olarak CaNO3 ve fosfor kaynağı olarak P2O5 kullanılarak, hidrotermal yöntem ile hidroksiapatit(HAP) sentezlenmiştir. Genleştirilmiş perlit(GP) ağırlıkça %5-10-15 oranlarında arttırılıp, %5 kitosan takviye edilerek 15 ml lik solüsyon hazırlanmştır. Daha sonra iki solüsyon birbiriyle karıştırılmıştır. Titanyum alaşımı, solüsyon ile termo kaba konulup, hidrotermal cihaza 12 saat 180oC'de kaplanmak üzere yerleştirilmiştir. Kaplanmış numuneler kaplama sonrası sıcaklık ve süre açısından kademeli olarak sinterleme ısıl işlemine tabi tutulmuştur. Elde edilen kaplamalar ringer çözeltide 1, 10 ve 15 gün bekletilerek in vitro davranışları gözlenmiştir. Titanyum alaşımı üzerinde biriktirilen HAP/GP kaplamların, taramalı elektron mikroskobu (SEM), enerji yayılımlı X-ışını analizi (EDX), X-ışını kırınım analizi (XRD), fourier dönüşümlü kızılötesi spektroskopisi (FTIR) analizleri ve kaplama kalınlığı değerleri ölçülüp karşılaştırılmıştır. Sonuç olarak SEM analizinde gözenekli yapılar gözlemlenmiştir. Buda osteointegrasyonu arttırmaktadır. Ayrıca ön ısıl işlemli numunelerin kaplama kalınlığında daha iyi sonuçlar verdiği gözlemlenmiştir. EDX analizlerinde yüzeyde Ca, P, Al, Si, Ti ve O gözlemlenmiştir. XRD analizi kaplamalarımızın hidroksiapatit olduğunu göstermiştir. FTIR analizinde ise bulunan pikler literatürle benzerlik göstermektedir.
Özet (Çeviri)
In this study, it is aimed to cover hydroxyapatite-perlite and hydroxyapatite-perlite-chitosan on the titanium alloy by using hydrothermal method. Ti6Al4V alloys with surface cleaned are classified as A and B group. Hydroxyapatite (HAP) was synthesized by hydrothermal method using CaNO3 as calcium source and P2O5 as phosphorus source. Expanded perlite (GP) was increased by 5-10-15% by weight, and a 15 ml solution was prepared by reinforcing 5% chitosan. The two solutions were then mixed together. The titanium alloy was placed in the thermo container with the solution and placed on the hydrothermal device to be coated at 180oC for 12 hours. Coated samples were subjected to gradually sintering heat treatment in terms of temperature and time after coating. The obtained coatings were kept in ringer's solution for 1, 10 and 15 days and their in vitro behavior was observed. HAP / GP coatings deposited on titanium alloy, scanning electron microscopy (SEM), energy diffuse X-ray analysis (EDX), X-ray diffraction analysis (XRD), fourier transform infrared spectroscopy (FTIR) analysis and coating thickness values were measured and compared. As a result, porous structures were observed in SEM analysis. This increases osteointegration. In addition, it has been observed that pre-heat treated samples give better results in coating thickness. In EDX analysis, Ca, P, Al, Si, Ti and O were observed on the surface. XRD analysis showed that our coatings are hydroxyapatite. The peaks found in the FTIR analysis are similar to the literature.
Benzer Tezler
- Hidroksiapatit esaslı zeolit/biyocam hibrit kompozit malzamenin hidrotermal yöntemle insan dişi üzerine kaplanması
Coating of hydroxyapatite based zeolite / bioglass hybrid composite material on human female by hydrothermal method
BÜŞRA ÖNCE
Yüksek Lisans
Türkçe
2021
Metalurji MühendisliğiFırat ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MEHTAP MURATOĞLU
- Hidroksiapatit esaslı seramik malzemelerin kristal yapı ve mikroyapılarının incelenmesi
Investigation of the crystal structure and microstructure of hydroxyapatite based ceramic materials
DİLEK BAĞCI
Yüksek Lisans
Türkçe
2017
Fizik ve Fizik MühendisliğiFırat ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. CENGİZ TATAR
- Hidroksiapatit esaslı biyoseramik malzemelerin karakterizasyonu
Characteriziation of hydroxyapatite based bioceramic materials
CEVRİYE KALKANDELEN
Doktora
Türkçe
2016
Biyomühendislikİstanbul ÜniversitesiBiyomedikal Mühendisliği Ana Bilim Dalı
PROF. DR. AYDIN AKAN
PROF. DR. FAİK NÜZHET OKTAR
- Hidroksiapatit esaslı doku iskelelerinin geliştirilmesi ve katakterizasyonu
Development and characterization of hydroxyapatite-based scaffolds
SÜMEYYE GÜLEÇ
Yüksek Lisans
Türkçe
2023
BiyoteknolojiSelçuk ÜniversitesiBiyoteknoloji Ana Bilim Dalı
DOÇ. DR. GÜLSÜM AYDIN
DOÇ. DR. AYŞE KALEMTAŞ
- Hidroksiapatit esaslı kemik grefti-trombosittten zengin plazma kombinasyonunun tavşan maksillasında oluşturulan deneysel kemik defektlerinde kemik rejenerasyonu üzerine etkilerinin histolojik açıdan değerlendirilmesi
Histological evaluation of bone regeneration of the surgically created defects in rabbit maxilla using hydroxyapatite bone graft- platelet-rich plasma combination
CANER ATALAY
Doktora
Türkçe
2011
Diş Hekimliğiİstanbul ÜniversitesiPeriodontoloji Ana Bilim Dalı
PROF. DR. KORKUD DEMİREL