Kan varlığında veya yokluğunda kök ucuna yerleştirilen farklı endodontik tamir materyallerinin dentine bağlanma dayanımlarının değerlendirilmesi
Evaluation of the bond strengths to dentine of root-end placed different endodontic repair materials in the presence / absence of blood contamination
- Tez No: 656917
- Danışmanlar: DOÇ. DR. HÜDA MELİKE BAYRAM
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental bonding, Dental materyaller, Kan, Kök kanal dolgu materyalleri, Kök kanal tedavisi, Kök kanalını tıkama, Mikrobiyal kirlilik, Mineral trioksit agregat, Dental bonding, Dental materials, Blood, Root canal filling materials, Root canal therapy, Root canal obturation, Microbial contamination, Mineral trioxide aggregate
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Tokat Gaziosmanpaşa Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Endodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu in vitro çalışmanın amacı; kan kontaminasyonu varlığında veya yokluğunda kök ucuna yerleştirilen MTA Repair HP, RetroMTA ve MTA Flow'un dentine bağlanma dayanımlarının değerlendirilmesidir. Materyal ve Metod: Bu çalışmada tek köklü 90 adet maksiler santral diş kullanıldı. Dişlere endodontik tedavi uygulandıktan sonra kök uçları 3 mm rezeke edildi ve kök ucu kaviteleri hazırlandı. Öncelikle örnekler, kavitelerin kanla kontaminasyonuna göre (+/-) 2 gruba ayrıldı. Daha sonra kök ucu dolgu malzemelerine göre (MTA Repair HP, RetroMTA, MTA Flow) üç alt gruba ayrıldı (n=15) ve bu malzemeler üreticinin talimatları doğrultusunda karıştırılarak kaviteye yerleştirildi. Örnekler 21 gün boyunca 37°C'de %100 nemli ortamda bekletildikten sonra her bir dişin kök ucundan 1 adet olmak üzere 1.0±0.1 mm'lik dilimler elde edildi, üniversal test cihazıyla push-out bağlanma dayanımı testi yapıldı. Başarısızlık tipini değerlendirmek için her dilim stereomikroskop altında incelendi. Veriler, tek yönlü varyans analizi ve Bağımsız Örneklem T Testi kullanılarak analiz edildi. Bulgular: Dentine bağlanma dayanımı, kan kontaminasyonunun varlığından önemli ölçüde olumsuz yönde etkilendi (p<0.05). En yüksek ort. bağlanma dayanımı değeri MTA Flow (-) grubunda, en düşük ort. bağlanma dayanımı değeri ise MTA Repair HP (+) grubunda gözlendi. Hem kanla kontamine olan grupta hem de kanla kontamine olmayan grupta MTA Repair HP en düşük bağlanma dayanımını gösterirken MTA Flow ve RetroMTA arasında anlamlı farklılık bulunamadı. Sonuç: Sonuç olarak kan kontaminasyonunun dentine bağlanma dayanımını azalttığı, materyaller arasında en yüksek bağlanma dayanımını MTA Flow'un, en düşük bağlanma dayanımını MTA Repair HP'nin gösterdiği bulunmuştur.
Özet (Çeviri)
Objective: The aim of this in vitro study is evaluation of bond strength to dentin of root end placed MTA Repair HP, RetroMTA and MTA Flow in the presence or absence of blood contamination. Materials and Methods: In this study, ninety single-rooted maxillary central teeth were used. After endodontic treatment was applied to the teeth, the root end were resected 3 mm and retrograd cavities were prepared. First, samples were divided into (+/-) 2 groups according to the contamination with blood of the cavities. Later, samples was divided into three subgroups (n=15) according to the root end filling materials (MTA Repair HP, RetroMTA, MTA Flow) and these materials were prepared and applied to the cavity according to the manufacturer's instructions. After the samples were kept at 37°C in 100% humid environment for 21 days, 1.0±0.1 mm slices were obtained from the root end of each tooth, and they were subjected to the push-out bond strength test with the universal test device. Each slice was examined under a stereomicroscope to evaluate the failure mode. The data were analyzed using one‑way analysis of variance and Independent Sample T Test. Results: Bond strength to dentin was significantly negatively affected by the presence of blood contamination (p <0.05). The highest average bond strength value was observed in the MTA Flow (-) group and the lowest average bond strenght value was observed in the MTA Repair HP (+) group. No significant difference was found between MTA Flow and RetroMTA while MTA Repair HP showed the lowest bond strength in both the blood contaminated group and the non-blood contaminated group. Conclusion: As a result, it has been found that blood contamination reduces the bond strength to dentin, MTA Flow shows the highest bond strength and MTA Repair HP shows the lowest bond strength among the materials.
Benzer Tezler
- Atherosklerotik kalp hastalıklarında risk faktörleri
Risk factors in the coronary artery disease
MURAT SUHER
- Testosteron dihidrotestosteron ve östrojenin benign prostat hiperplazisindeki etyolojik rolleri
The roles of testosterone, dihydrotestosterone and estradiole on the etiology of benign prostatic hyperplasia
HALUK TOKUÇOĞLU
- Çocuklarda akut stres hiperglisemisinde hormonal değişikliklerin ve kısa süreli prognozun incelenmesi
Başlık çevirisi yok
AYGÜN DİNDAR
Tıpta Uzmanlık
Türkçe
1987
Çocuk Sağlığı ve Hastalıklarıİstanbul ÜniversitesiÇocuk Sağlığı ve Hastalıkları Hemşireliği Ana Bilim Dalı
DOÇ. DR. HÜLYA GÜNÖZ
- Pulmoner hipertansiyon etyopatogenezinde prostasiklin ve lökotrien C4'ün rolü
Possible role of leukotrien C4 and prostacyclin in the development of pulmonary hypertension
ÜLKÜ AYBERK
Tıpta Uzmanlık
Türkçe
1987
Çocuk Sağlığı ve HastalıklarıGazi ÜniversitesiÇocuk Sağlığı ve Hastalıkları Ana Bilim Dalı