Alaşımlı yay çeliklerinin mikroyapı ve mekanik özelliklerine kriyojenik işlemin etkisi

Effect of cryogenic treatment on microstructural and mechanical properties of alloyed spring steels

  1. Tez No: 662063
  2. Yazar: REŞAT CAN ÖZDEN
  3. Danışmanlar: PROF. DR. MUSTAFA ANIK
  4. Tez Türü: Doktora
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2020
  8. Dil: Türkçe
  9. Üniversite: Eskişehir Osmangazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Malzeme Bilim Dalı
  13. Sayfa Sayısı: 87

Özet

Bu çalışmada otomotiv sanayinde yaygın olarak kullanılan orta karbonlu 55Cr3, 51CrV4, 52CrMoV4 yay çeliklerinin mikroyapı ve mekanik özelliklerine, derin kriyojenik işlemin (-196 °C) ve bu işlemi takiben uygulananan temperleme işleminin (500 °C) etkileri incelenmiştir. Bu amaçla çelik numunelerin mikroyapılarının şekilsel ve yapısal analizleri için taramalı elektron mikroskobu (SEM), geçirimli elektron mikroskobu (TEM), elektron geri saçılım kırınımı (EBSD) ve X ışını kırınımı (XRD) yöntemleri kullanılmıştır. Numunelerin kalıntı gerilmeleri de yine XRD yöntemi temel alınarak ölçülmüştür. Martenzit fazı kafes yapısındaki değişimler Rietveld analizi kullanılarak belirlenmiştir. Mekanik özelliklerdeki değişim için numunelerin mikrosertlikleri ölçülmüştür. Aşınma oranlarının tespiti için ball-on disk geometrisi, dinamik tokluk değerlerinin belirlenmesi içinse Charpy testi kullanılmıştır. Numunelere çekme ve dönel eğmeli yorulma testleri de uygulanmıştır. Numunelere uygulanan kriyojenik işlem sonucunda geleneksel ısıl işlem prosesine göre tane irileşmesi etkin şekilde engellenmiş ve %34'lük bir tane incelmesi gözlenmiştir. Oluşan yeni martenzit ve karbür yapıların malzeme matrisi boyunca homojen dağılımı sayesinde kriyojenik işlem görmüş numuneler tokluk kaybına uğramaksızın mukavemet kazanmıştır. İncelenen numuneler içerisinde en fazla alaşım içeren 52CrMoV4 çeliklerinin kriyojenik etkiye daha duyarlı olduğu ve dinamik tokluğun %43,75, statik tokluğun %19,43, yorulma dayanımının ise %51'e varan düzeyde arttığı tespit edilmiştir.

Özet (Çeviri)

In this study, the effects of deep cryogenic process (-196 ° C) and following tempering (500°C) process on microstructure and mechanical properties of medium carbon 55Cr3, 51CrV4, 52CrMoV4 spring steels, which are widely used in automotive industry, were investigated. For this purpose, scanning electron microscope (SEM), transmission electron microscope (TEM), Electron Back Scatter Diffraction (EBSD) and X-ray diffraction (XRD) methods were used for the formal and structural analysis of the microstructure of steel samples. The residual stresses of the samples were also measured based on the XRD method. Changes in martensite lattice structure were determined using Rietveld analysis. In order to determine the changes in mechanical properties, the hardness of the samples was measured using the Vickers microhardness method. Ball-on disc method was used for determination of wear rates and Charpy method for impact toughness. Tensile and rotational bending fatigue tests of the samples were carried out. As a result of the applied cryogenic treatment, grain coarsening was effectively prevented compared to the traditional heat treatment process and a grain refinement of 34% was observed. Thanks to the homogeneous distribution of the newly formed martensite and carbide structures throughout the material matrix, cryogenic treated samples gained strength without losing toughness. It has been reported that 52CrMoV4 steels, which are the most alloyed steel group, are more sensitive to cryogenic effect and have shown improvements up to 43.75% in impact toughness, 19.43% in static toughness and 51% in fatigue strength.

Benzer Tezler

  1. Kriyojenik işlem uygulanmış yay çeliklerinin aşınma özelliklerine alaşım elementlerinin etkisi

    Effects of alloying elements on the wear characteristics of cryogenic treated spring steels

    ERDU DOĞUŞ GÜL

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    Metalurji MühendisliğiEskişehir Osmangazi Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MUSTAFA ANIK

  2. Alaşımsız ve düşük alaşımlı çeliklerde küreselleştirme ısıl işleminin optimizasyonu ve hassas kesme işlemine etkisi

    Optimization of spheroidizing heat treatment in unalloyed and low alloyed steels and its effect on fine blanking process

    AKIN KÜTMEN

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MURAT BAYDOĞAN

  3. Kokil kalıplarda tungsten alaşımlı malzeme kullanımı ile termal yorulma ve aşınma direncinin artırılması

    Improving thermal fatigue and erosion resistance by using tungsten alloy material in permanent molds

    BORA YAY

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Metalurji MühendisliğiEge Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. RASİM İPEK

  4. AISI301 kalite yay çeliğinin ısıl işlem şartlarının mekanik özelliklerine etkisi

    The effect of AISI301 quality spring steel on mechanical properties of heat treatment conditions

    ŞEYDA BULUT

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Metalurji MühendisliğiDumlupınar Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. VELİ UZ

  5. design and manufacturing of a shape memory alloy actuator

    Şekil bellek alaşımlı aktüatör tasarımı ve üretimi

    MUTLU TOPAL

    Yüksek Lisans

    İngilizce

    İngilizce

    1997

    Makine MühendisliğiBoğaziçi Üniversitesi

    PROF. DR. SABRİ ALTINBAŞ