Cam bilya partikül ile takviye edilmiş PA66'nın işlenebilirliği ve mekanik özelliklerinin belirlenmesi

Processability and mechanical properties of PA66 reinforced with glass ball particles

  1. Tez No: 676103
  2. Yazar: GONCA USLU
  3. Danışmanlar: DR. ÖĞR. ÜYESİ NAFİZ YAŞAR
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2021
  8. Dil: Türkçe
  9. Üniversite: Karabük Üniversitesi
  10. Enstitü: Lisansüstü Eğitim Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 65

Özet

Bu çalışmada, farklı oranlarda cam bilya (CB) takviye edilerek üretilen poliamid 66 (PA66) malzemelerde CB katkısının mekanik özelliklere ve delinebilirliğe etkisinin incelenmesi amaçlanmıştır. Bu doğrultuda, mekanik özellikler için çekme mukavemeti, elastiklik modülü, sertlik, kopmadaki uzama ve darbe mukavemeti ölçümleri gerçekleştirilmiştir. Ayrıca, delme yöntemiyle gerçekleştirilen işlenebilirlik deneylerinde itme kuvveti ve yüzey pürüzlülüğü işleme çıktıları değerlendirilmiştir. Delme deneylerinde, iki farklı matkap kalitesi (kaplamasız ve kaplamalı) ile ilerleme miktarı ve kesme hızının üçer farklı seviyeleri kullanılmıştır. Mekanik testler sonucunda, CB takviyesinin çekme mukavemeti, darbe mukavemeti ve kopmadaki uzama oranını düşürdüğü, sertlik ve elastiklik modülünü ise artırdığı gözlemlenmiştir. En yüksek çekme mukavemeti, darbe mukavemeti ve kopmadaki uzama oranı CB takviye edilmemiş PA66 ile elde edilirken, en yüksek sertlik değeri ve elastiklik modülü %30 CB takviyeli PA66 ile elde edilmiştir. Delme deneyleri sonucunda ise kaplamalı matkap ile elde edilen itme kuvveti (Fz) değerleri, kaplamasız matkap ile elde edilen değerlere göre daha düşük çıkmıştır. Diğer taraftan, artan CB oranına bağlı olarak Fz deeğrinin arttığı gözlemlenmiştir. En düşük Fz değeri kaplamalı matkap ile %10 CB takviyeli PA66 ile elde edilmiştir. En yüksek Fz değeri ise kaplamasız matkap ile %30 CB takviyeli PA66 ile elde edilmiştir. Yüzey pürüzlülüğü (Ra) açısından yapılan değerlendirmede artan CB takviye oranının Ra değerini artırdığı, aynı CB takviye oranlarında yapılan kıyaslamalarda ise kaplamalı matkap ile elde edilen Ra değerleri, kaplamasıza göre daha düşük çıkmıştır. En düşük Ra değeri %10 CB takviyeli PA66'nın kaplamalı matkap ile delinmesinde, en yüksek Ra değeri ise %30 CB takviyeli PA66'nın kaplamasız matkap ile delme işleminde ortaya çıkmıştır. Bu sonuçlara göre, CB takviyesinin Fz ve Ra değerlerini artırdığı, kesici takım kaplamasına bağlı olarak düşüş dergilediğini söylemek mümkündür. Ayrıca artan ilerleme miktarına bağlı olarak Fz ve Ra değerlerinde artış olduğu görülmüştür. Kesme hızının artışlarında Fz ve Ra değerlerinde azalma olduğu, ancak kesme hızının 80 m/dak'dan 120 m/dak'ya artışlarında Ra değerlerinin arttığı tespit edilmiştir.

Özet (Çeviri)

In this study, it was aimed to investigate the effect of glass ball (GB) additive on mechanical properties and punctureability of polyamide 66 (PA66) materials produced by reinforcing GB at different rates. In this direction, tensile strength, modulus of elasticity, hardness, elongation at break and impact strength were measured for mechanical properties. In addition, the thrust force and surface roughness machining outputs were evaluated in the machinability tests performed with the drilling method. In drilling experiments, two different drill qualities (uncoated and coated) and three different levels of feed rate and cutting speed were used. As a result of the mechanical tests, it was observed that GB reinforcement decreased the tensile strength, impact strength and elongation at break, while increasing the stiffness and modulus of elasticity. The highest tensile strength, impact strength and elongation at break were obtained with PA66 without GB reinforcement, while the highest hardness value and modulus of elasticity were obtained with 30% GB reinforced PA66. As a result of the drilling experiments, the thrust force (Fz) values obtained with the coated drill were lower than the values obtained with the uncoated drill. On the other hand, it was noticed that the Fz value rose depending on the increasing GB ratio. The lowest Fz value was obtained with coated drill and 10% GB reinforced PA66. The highest Fz value was obtained with uncoated drill and 30% GB reinforced PA66. In the evaluation made in terms of surface roughness (Ra), increasing the GB reinforcement ratio increased the Ra value, and in the comparisons made at the same GB reinforcement ratios, the Ra values obtained with the coated drill were lower than the uncoated drill. The lowest Ra value was observed when drilling 10% GB reinforced PA66 with a coated drill, and the highest Ra value was found in drilling with an uncoated drill of 30% GB reinforced PA66. According to these results, it is possible to say that GB reinforcement increases the Fz and Ra values and journals decrease depending on the cutting tool coating. In addition, it was observed that the Fz and Ra values increased depending on the increasing feed rate. It was determined that there was a decrease in Fz and Ra values with increasing cutting speed, but Ra values increased with increasing cutting speed from 80 m/min to 120 m/min.

Benzer Tezler

  1. Cam bilya ve silisyum partikül ile takviye edilmiş polipropilen kompozit malzemenin işlenebilirliğinin araştırılması

    Invesgatigating machinability of glass sphere and silicon particle reinforced polypropylene composite material

    MUSTAFA DÜNDAR

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Mühendislik BilimleriSakarya Üniversitesi

    İmalat Mühendisliği Ana Bilim Dalı

    PROF. DR. SALİM ASLANLAR

  2. Süperkritik karbondioksit ortamında sentezlenen fluroakrilat kopolimerden süper-hidrofobik, süper-oleofobik yüzey ve sıvı bilya eldesi ve uygulamaları

    Formation of superhydrophobic and superoleofophobic surfaces from fluoroacrylate copolymers in supercritical carbon dioxide medium and liquid marble and aplications

    UĞUR CENGİZ

    Doktora

    Türkçe

    Türkçe

    2012

    Kimya MühendisliğiGebze Yüksek Teknoloji Enstitüsü

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. H. YILDIRIM ERBİL

  3. Bazı metal sülfidlerin mekanokimyasal yöntemle çözündürülmesi

    Dissolution of some metal sulphides by mechanochemical processing

    GÖKHAN UÇAR

    Doktora

    Türkçe

    Türkçe

    2010

    Maden Mühendisliği ve MadencilikSelçuk Üniversitesi

    Maden Mühendisliği Ana Bilim Dalı

    DOÇ. DR. SALİH AYDOĞAN

  4. Noise and friction characteristics of polymer ball bearings

    Bilyalı polimer yatakların gürültü ve sürtünme karakteristikleri

    ALİYYE KARA

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Makine Mühendisliğiİstanbul Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ VEDAT TEMİZ