Alev sprey pı̇rolı̇z yöntemı̇ ı̇le çekı̇rdek/kabuk yapısındakı̇ mgal2o4/al2o3 kompozı̇t tozlarının sentezlenmesı̇
Synthesis of core-shell mgal2o4/al2o3 composite powders via flame spray pyrolysis
- Tez No: 677038
- Danışmanlar: DR. ÖĞR. ÜYESİ İSMAİL ÖZGÜR ÖZER
- Tez Türü: Yüksek Lisans
- Konular: Seramik Mühendisliği, Ceramic Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Eskişehir Teknik Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 83
Özet
Bu tezin temel amacı şeffaf MgAl2O4 seramiklerin mikroyapı kontrolüne önemli katkı sağlayacak, sinterleme aktivitesi yüksek MgAl2O4/Al2O3 çekirdek kabuk yapıda kompozit tozların alev sprey pirolizi ile sentezidir. İlk olarak MgAl2O4 tozlarının sentezi için gerekli başlangıç kimyasalının kompozisyonu ve reaktör süreç parametreleri belirlenmiştir. Bu çalışmalarda oksit tozlarının alev sprey pirolizi ile sentezi için kullanılan nem hassasiyetleri düşük ve görece maliyet etkin oksitlerden“trane”kompleksi hazırlama metodu kullanılmıştır. Ancak, oksitlerden başlanarak elde edilen“trane”komplekslerinin faz saflığı eldesini zorlaştırdığı ortaya konmuştur. İstenilen faz saflığında ve stokiyometride tozların eldesi için direkt çöktürme ile“trane”kompleksi hazırlama metodunu birleştiren hibrit bir yöntem kullanılmıştır. Stokiyometri ve faz analizleri x-ışınları kırınımı (XRD) metodu ile gerçekleştirilmiştir. Partikül boyut kontrolü, sentez süresince askıda kalma süresini ve alev sıcaklığını etkileyen süreç parametrelerine karşı çalışılmıştır. XRD deseni üzerinden Scherer denklemi ile ölçülen en yüksek birincil partikül boyutu 17 nanometre, Zetasizer ile ölçülen (elektro-foretik hareket prensibine dayalı çalışan) en yüksek aglomere boyutu ise 180 nanometre değerindedir. Çekirdek partiküllerinin kaplanması, alüminyum klorür buharının reaktör içine N2 gazı ile torus halkası vasıtasıyla beslenmesi ve reaktörde yanma sonucu meydana gelen su buharıyla reaksiyona sokulması ile çalışılmıştır. Çekirdek partikülleri üzerindeki kaplama varlığı geçirimli elektron mikroskobu (TEM) analizleri ile araştırılmıştır. Sentezlenen MgAl2O4 tozları optik geçirim sağlayacak yüksek yoğunluğa sinterlenmiştir.
Özet (Çeviri)
The main objective of this thesis is the synthesis of composite powders in the form of MgA2O4/Al2O3 core/shell structure that are high in sintering activity and will improve microstructure significantly, by using flame spray pyrolysis method. Firstly, the precursor compositions and process parameters were determined which are required to achieve phase pure MgAl2O4 powders. In these studies, relatively low moisture sensitive and cost effective“trane”complex precursors are used to obtain oxide phases. However, it was showed that a widely used“trane”complex method for the synthesis of oxide powders via pyrolysis makes it difficult to obtain phase purity. A new hybrid method was proposed to achieve highly pure MgAl2O4 powders powders with controlled stoichiometry. Stoichiometry and phase analyzes were carried out by x-ray diffraction (XRD) method. Particle size control has been studied at different process parameters that affect the residence time of particles in the flame. The largest primary particle size measured with XRD-based Scherer formula was 17 nm, and the maximum aggregate size measured with Zetasizer was recorded as 180 nm. The coating of the core particles was studied by carrying AlCl3 vapor to the reactor with the N2 gas, feeding it into the reactor through the Torus ring and reacting it with the water vapor which is the combustion product in the reactor. The presence of the coating on the core particles were studied by transmission electron microscopy (TEM). Magnesium spinel powders were able to sintered to high densities that can provide optical transmission.
Benzer Tezler
- Production of Ce and Cu doped nano-TiO2 by flame spray pyrolysis method and evaluation of their photo-catalytic activities
Alev sprey piroliz yöntemi ile Ce ve Cu katkılı nano-TiO2 üretimi ve fotokatalitik aktivitelerinin değerlendirilmesi
ASLI KADER ONAY
Yüksek Lisans
İngilizce
2021
Kimya MühendisliğiAtılım ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. NESRİN EKİNCİ MACHIN
- Production of MgO catalyzor nano particles by flame sprey pyrolyses method
Alev sprey piroliz yöntemi ile MgO katalizör nanopartiküllerin üretimi
BERKAN ÖZTÜRK
Yüksek Lisans
İngilizce
2013
Mühendislik BilimleriDokuz Eylül ÜniversitesiMaden Mühendisliği Ana Bilim Dalı
PROF. DR. TURAN BATAR
- Modeling and optimization of nanoparticle production by flame spray pyrolysis method
Alev sprey piroliz yöntemi ile nanopartikül üretimininmodellenmesi ve optimizasyonu
MUSTAFİ ALHALEEB
Doktora
İngilizce
2021
Kimya MühendisliğiAtılım ÜniversitesiMühendislik Sistemlerinin Modellenmesi ve Tasarımı Ana Bilim Dalı
DOÇ. DR. NESRİN EKİNCİ MACHIN
- Alev sprey piroliz yöntemiyle katalizör üretimi ve metanın katalitik yanmasında etkinliğinin araştırılması
Synthesis of catalysts by flame spray pyrolyis and investigation of their activity on catalytic combustion of methane
SİBEL ŞANLTÜRK
Yüksek Lisans
Türkçe
2013
Bilim ve TeknolojiKocaeli ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. NESRİN EKİNCİ MACHIN
- Süperkritik su atmosferinde formaldehitin katalitik gazlaştırılması
Catalytic gasification of formaldehyde in supercritical water atmosphere
GÖKHAN YAŞAR
Yüksek Lisans
Türkçe
2016
Kimya MühendisliğiCumhuriyet ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. AYTEN ATEŞ
DOÇ. DR. NESRİN MACHIN