L-TZF membranların mekanik özelliklerinin geliştirilmesi, degradasyon süresinin azaltılması: ın-vıtro çalışma
Improvement of mechanical properties of L-TZF membranes, reducing degradation time: İn-vitro study
- Tez No: 700316
- Danışmanlar: PROF. DR. ALPER AKTAŞ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: L-TZF, degradasyon, fiziksel dayanıklılık, Genipin, Ankaferd, Ankaferd kanama durdurucu, Trombositten zengin fibrin, L-PRF, degradation, mechanical strength, Genipin, Ankaferd, Ankaferd bloodStopper, Physical endurance, Platelet rich fibrin
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Hacettepe Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Ağız, Diş ve Çene Cerrahisi Ana Bilim Dalı
- Bilim Dalı: Ağız, Diş, Çene Hastalıkları ve Cerrahisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada L-TZF'nin fibrin fiberleri arasındaki çapraz bağlantıların arttırılması, bu sayede fiziksel dayanımının arttırılması ve degradasyon hızının düşürülmesi için doğal bir çapraz bağlantı ajanı olan Genipin ve Ankaferd kanama durdurucu ajan kullanılmıştır. 25 hastadan ikişer tüp kan alındıktan sonra santrifüj cihazı ile (3000 devir/dakika) 10 dakika santrifüj edilmiştir. Elde edilen L-TZF'ler PRF Box kullanılarak membran haline getirilmiştir. Birincisi Genipin, ikincisi Ankaferd ve üçüncüsü de kontrol grubu olmak üzere üç grup oluşturulmuştur. Her grupta 4 ml'lik solüsyon bulunmaktadır; ilk grubun solüsyonunda %1'lik genipin çözeltisi, İkinci grupta %10'luk Ankaferd çözeltisi, son olarak kontrol grubunda ise sadece %70 oranında ethanol içeren solüsyon bulunmaktadır. Hazırlanan bu solüsyonlarda örnekler 48 saat boyunca bekletilmiştir. Membranların 15 tanesi degradasyon testi için 500 l %0.01 oranında tripsin içeren solüsyonda 3 gün daha 37C'de bekletilmiştir. 3.günün sonundaki kütle değişimi üzerinden degradasyon miktarı hesaplanmıştır. 18 örnek çekme testinde kullanılmıştır, ZwickRoell Mekanik Test makinesı kullanılarak 20 dk/mm hızla membranlara çekme kuvveti uygulanmış, membranların Emod, Fmaks. , Fkopma, Membranlardaki uzaman yüzdesi ölçülmüştür. 9 örnekte UV-Spektrofotometrik inceleme altında çapraz bağlantı miktarı ölçülmüştür. 3 örnek Taramalı Elektron Mikroskobunda incelenmiş, x10k ve x25k büyütmede görüntüler alınmıştır. Grupların kütle kaybı ortalamaları karşılaştırıldığında Genipin ve ankaferd'in istatistiksel olarak anlamlı derecede (p<0.005) L-TZF'nin degradasyonunu azalttığı tespit edilmiştir. Yapılan mekanik test sonucunda da genipin ve Ankaferd gruplarında kontrol grubuna göre istatistiksel olarak anlamı (p<0.005) derecede artış izlenmiştir. Membranlarda meydana gelen çapraz bağlanma miktarları incelendiğinde Ankaferd grubunda %90,4 Genipin grubunda ise %47.08 olarak bulunmuştur. Gruplar arası farkın istatistiksel olarak anlamlı derecede farklı (p<0.005) olduğu, her iki materyalin de çapraz bağlantı miktarını arttırdığı tespit edilmiştir. Genipin ve Ankaferd grubunun Taramalı Elektron Mikroskobu altında alınan görüntülerinde her iki materyalin de fibrin fiberleri arası çapraz bağlantı miktarını arttırdığı tespit edilmiştir. Çalışmanın sonucunda genipin ve Ankaferd materyalinin L-TZF membranın fibrin fiberleri arasında çapraz bağ kurarak fiziksel bağı arttırdığını ve bunun sonucunda da materyalin fiziksel dayanımını arttırarak degradasyon hızını düşürdüğü tespit edilmiştir.
Özet (Çeviri)
In this study, Genipin and Ankaferd Blood Stopper (ABS), which are natural crosslinking agents, were used to increase the crosslinking between fibrin fibers of L-PRF, thereby increasing its physical strength and reducing the degradation rate. After collecting two tubes of blood from 25 patients, it was centrifuged for 10 minutes with a centrifuge device (3000 rpm). The obtained L-PRFs were turned into membranes using the PRF Box. Three groups were established, the first Genipin, the second ABS, and the third control group. Each group contains 4 ml of solution; The solution of the first group contains 1% genipin solution, the second group contains 10% Ankaferd solution, and lastly, the solution containing only 70% ethanol in the control group. Samples were kept in these prepared solutions for 48 hours. For the degradation test, 15 of the membranes were kept in 500 µl of 0.01% trypsin solution for 3 more days at 37°C. The amount of degradation was calculated over the mass change at the end of the 3rd day. 18 samples were used in the tensile test, tensile force was applied to the membranes at a speed of 20 min/mm using the ZwickRoell Mechanical Testing machine; Emod, Fmaks., Fkopma, percent of elongation in the membranes was measured. The amount of crosslinking was measured in 9 samples under UV-Spectrophotometric examination. 3 samples were examined under a Scanning Electron Microscope and images were taken at x10k and x25kk magnifications. When the mass loss averages of the groups were compared, it was determined that Genipin and ABS reduced the degradation of L-PRF statistically significantly (p<0.005). According to the result of the mechanical test, a statistically significant (p<0.005) increase was observed in the genipin and ABS groups compared to the control group. When the amount of crosslinking occurred in the membranes was examined, it was found as 90.4% increase in cross linking in the ABS group and 47.08% increase in the Genipin group. It was determined that the difference between the groups was statistically significantly different (p<0.005), and both materials increased the amount of crosslinking. In the images taken under Scanning Electron Microscopy of Genipin and ABS groups, it was determined that both materials increased the amount of crosslinking between fibrin fibers. To conclude, it was determined that genipin and ABS material increased the physical bond by establishing a cross-link between the fibrin fibers of the L-PRF membrane, and as a result, it decreased the degradation rate by increasing the physical strength of the material.
Benzer Tezler
- Periodontitisin trombositten zengin fibrinin mekanik, yapısal ve biyolojik özelliklerine etkisi
The effect of periodontitis on the mechanical, structural, and biological properties of platelet-rich fibrin
SARVAR IBRAHIMLI
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiKırıkkale ÜniversitesiPeriodontoloji Ana Bilim Dalı
DOÇ. DR. MELTEM HENDEK
- Hidroksiapatit trombositten zengin fibrinin (HA-TZF) gingiva kaynaklı mezenkimal kök hücreler ve yara iyileşmesi üzerine etkililiğinin değerlendirilmesi
Evaluation of the effectiveness of hydroxyapatite platelet-rich fibrin (HA-PRF) on gingiva-derived mesenchymal stem cells and wound healing
İZZET MELİH GÜRKAN
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiEskişehir Osmangazi ÜniversitesiPeriodontoloji Ana Bilim Dalı
PROF. DR. HAKAN ÖZDEMİR
DOÇ. DR. SEÇİL ÇALIŞKAN
- Nanotitanyum trombositten zengin fibrinin gingiva kaynaklı mezenkimal kök hücreler ve yara iyileşmesi üzerine etkinliğinin değerlendirilmesi
Evaluation of the Effectiveness of Nanotitanium Platelet-Rich Fibrin on Gingiva-Derived Mesenchymal Stem Cells and Wound Healing
AHMET SELÇUK ALKAYA
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiEskişehir Osmangazi ÜniversitesiPeriodontoloji Ana Bilim Dalı
PROF. DR. HAKAN ÖZDEMİR
DOÇ. DR. SEÇİL ÇALIŞKAN
- Lökosit ve trombositten zengin fibrin uygulamasının serbest dişeti grefti verici bölge iyileşmesi üzerine etkilerinin değerlendirilmesi
Evaluation of the effect of leukocyte and platelet rich fibrin on wound healing of palatal donor sites after free gingival grafting procedures
SERAP GÜLSEVER
Doktora
Türkçe
2014
Diş HekimliğiBaşkent ÜniversitesiAğız, Diş ve Çene Cerrahisi Ana Bilim Dalı
PROF. DR. İBRAHİM SİNA UÇKAN
- Periimplanter beş duvarlı kemik defektlerinin iyileşmesinde t-TZF ve l-TZF uygulamalarının in vivo olarak histomorfometrik incelenmesi
Histomorphometric examination of t-PRF and l-PRF in vivo applications in the healing of periimplanter fivewall bone defects
ARTHUR BOZACIOĞLU
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş Hekimliğiİstanbul ÜniversitesiAğız, Diş ve Çene Cerrahisi Ana Bilim Dalı
PROF. DR. HAKKI TANYERİ