Plazma elektrolitik oksidasyon (PEO) işlemi uygulanmış alüminyum alaşımlarının yapıştırma bağlantılarında yapısal ve mekanik özelliklerin incelenmesi

Invastigation of the structural and mechanical features of plasma electrolytic oxidation (PEO) processed aluminium alloys at bonded joints

  1. Tez No: 704337
  2. Yazar: MUHAMMET İKBAL KOTAN
  3. Danışmanlar: PROF. DR. YAŞAR TOTİK
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2021
  8. Dil: Türkçe
  9. Üniversite: Atatürk Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Konstrüksiyon ve İmalat Bilim Dalı
  13. Sayfa Sayısı: 102

Özet

Havacılık ve uzay araçları, ulaşım araçları, biyomedikal ve spor ekipmanları gibi birçok farklı alanda çeşitli bağlantı elemanları kullanılmaktadır. Son zamanlarda yapıştırıcılar alternatif bağlantı yöntemi olarak öne çıkmakta ve birçok yapıştırma işleminde yaygın olarak kullanılmaktadır. Yapıştırıcıların yaygın olarak kullanılması, farklı bilimsel çalışmaların bu alanda yoğunlaşmasına yol açmıştır. Bu amaçla çalışmamızda, Al2024-T3 alaşımı üzerine plazma elektrolitik oksidasyon (PEO) yöntemiyle farklı parametrelerde büyütülen kaplamaların yapıştırma bağlantılarındaki mekanik özelliklerinin incelenmesi amaçlanmıştır. İlk aşamada yapıştırma bağlantılarının oluşturulabilmesi için kalıp üretimi gerçekleştirilmiştir. Daha sonra yüzeylerine ön işlemlerin uygulandığı alüminyum alaşımları üzerinde üç grup olacak şekilde farklı parametrelerde PEO yöntemiyle kaplama işlemi gerçekleştirilmiştir. Kaplama işleminden sonra numunelerin yapıştırma bağlantıları (SLJ) oluşturulmuştur. Kaplamasız ve kaplanmış numunelerin, yapısal ve mekanik analizleri XRD, AFM, SEM, EDS, Scratch(Çizik) testleri ile yapılmıştır. Sonra ki aşamada ise yapıştırma bağlantılarına çekme ve üç nokta eğilme mekanik testleri uygulanmış ve oluşan kırılma yüzeyleri ile birlikte sonuçlar incelenmiştir. Kaplamaların yapısal analizleri sonucunda numunelerde α-Al2O3 ve γ-Al2O3 fazlarının oluştuğu görülmüştür ve bu fazların yoğunluklarının kaplama parametrelerinden azda olsa etkilendiği gözlenmiştir. Kaplama neticesinde yüzeyde porlu bir tabakanın elde edildiği ve yüzey pürüzlülüğünün kaplama parametreleriyle değiştiği gözlenmiştir. Kaplama parametrelerinden frekans, voltaj ve elektrolitik çözeltisinin fazların yoğunluklarına ve yüzey pürüzlülüğünde değişimlere sebep olduğu belirlenmiştir. En porlu yüzey alüminat içerikli elektrolitik çözeltisinde ve 650 V şartlarında kaplanmış Grup 2 kaplamalarda görülmüştür. Mekanik testler sonucunda çekme ve eğilme mukavemeti en yüksek kaplamasız SLJ numunelerde, daha sonra sırasıyla kaplanmış SLJ 2, SLJ 3 ve SLJ 1 numunelerinde elde edilmiştir. Al2024-T3 alaşımına uygulanan kaplama işleminin malzemenin yüzey özelliklerini değiştirdiği gözlenmiştir. Kaplama işleminin yapıştırma bağlantıları üzerinde etkisi ise, kaplamasız SLJ numunelerinin, kaplanmış SLJ 1, SLJ 2 ve SLJ 3 numunelerine göre daha iyi mekanik özellik gösterdiği şeklinde tespit edilmiştir. Bu durum kaplama neticesinde yüzeylerin pürüzlü olması ve bu sebeple yüzeyin hidrofilik özelliğinin azalmasından kaynaklanmaktadır. Ayrıca kırılma yüzeyleri incelendiğinde, buna etken olan en önemli sebepler arasında yapıştırıcının kaplama yüzeyiyle uyumlu bir yapı göstermemesi, pürüzlü yüzeyler arasına iyi nüfuz etmemesi (yerleşmemesi) ve yapıştırıcının uygulama sırasında yeterli akıcılığa sahip olmaması şeklinde ifade edilebilir.

Özet (Çeviri)

Various bonding elements are used in many different areas such as aviation and space vehicles, transportation vehicles, biomedical and sport equipment. Recently, adhesives have come to the forefront as an alternative bonding method and are widely preferred in many bonding processes. Common use of adhesives attracted many others to study on this subject. In this study, it was aimed to investigate the mechanical properties at the bonding joints of coatings that are grown in different parameters on Al2024-T3 alloy by Plasma Electrolytic Oxidation (PEO). At the first stage, mold was produced so that the adhesive connections could be carried out. Then, the coating process was performed by PEO method in different parameters, in three groups, on the materials on which pre-treatment was applied. After the coating process, the adhesive joints (SLJ) of the samples were performed. Structural and mechanical analysis of uncoated and coated samples were performed with XRD, AFM, SEM, EDS and Scratch tests. In the next stage, tensile and three-point bending mechanical tests were applied to the adhesive joints and then appeared fracture surfaces and the results were examined. As a result of the structural analysis of the coatings, it was observed that α-Al2O3 and γ-Al2O3 phases were formed in the samples and the densities of these phases were slightly affected by the coating parameters. As a result of the coating, a porous layer was observed on the surface and the surface roughness changed by depending on the coating parameters. It has been determined that the frequency, voltage and electrolytic solution of the coating parameters cause changes in the densities of the phases and surface roughness. The most porous surface was observed in the electrolytic solution containing aluminate and in Group 2 coatings coated at 650 V conditions. As a result of the mechanical tests the highest tensile and flexural strengths were obtained in the uncoated SLJ samples, that was followed by the coated SLJ 2, SLJ 3 and SLJ 1 samples, respectively.It was observed that the coating process applied to the Al2024-T3 alloy changes the surface properties of the material. The effect of coating on the bounding joints was observed as uncoated SLJ samples had better mechanical properties compare to the coated SLJ 1, SLJ 2 and SLJ 3 samples. This was because of the reduced hydrophilic effect of the rough surfaces which was caused by coating process. Additionally, it could be stated that the most important reasons for this, following the fracture surface examination, are the adhesive did not have a compatible structure with the coating surface, it did not penetrate well between the rough surfaces (not settling), and it did not have sufficient fluidity during application.

Benzer Tezler

  1. Eşit kanal açısal presleme (EKAP) yöntemi kullanılarak Al-Zn-Mg alaşımının mekanik ve yüzey özelliklerinin araştırılması

    Investigation of the mechanical and surface properties of Al-Zn-Mg alloy using the equal channel angular pressing ECAP method

    TAHA ALPER YILMAZ

    Doktora

    Türkçe

    Türkçe

    2022

    Makine MühendisliğiAtatürk Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. YAŞAR TOTİK

    PROF. DR. BÜLENT BOSTAN

  2. Sıcak daldırma yöntemi ile alüminyum kaplanan düşük karbonlu çeliğe uygulanan mikro ark oksidasyon işleminin karakterizasyonu

    Characterization of micro-arc oxidized unalloyed low-carbon steel after hot-dip aluminizing process

    MUSTAFA AÇIKSÖZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. MURAT BAYDOĞAN

  3. Mikro ark oksidasyon işlemi uygulanmış ZA-8 alaşımının yüzey özelliklerinin incelenmesi

    Investigation of surface properties of micro arc oxidized ZA-8 alloy

    BERKAN ÇAMLIBEL

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. MURAT BAYDOĞAN

  4. Plazma elektrolitik oksidasyon yönteminin Al/Al2O3 metal matrisli kompozit malzemelere uygulanması

    Application of plasma electrolytic oxidation method on Al/Al2O3 metal matrix composite materials

    ŞÖHRET MELDA AYDIN

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Makine MühendisliğiEge Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ SERDAR KARAOĞLU

  5. Investigations on reducing friction coefficient of MAO coating fabricated on 7075 Al alloy

    7075 Al alaşımı üzerinde oluşturulan MAO kaplamanın sürtünme katsayısını azaltmaya yönelik araştırmalar

    GİZEM KÜLLÜ

    Yüksek Lisans

    İngilizce

    İngilizce

    2023

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. HÜSEYİN ÇİMENOĞLU

    DR. ÖĞR. ÜYESİ FAİZ MUHAFFEL