Cam matriks seramik-dentin bağlantı dayanıklılığına baicaleinin etkisi
Effect of baicalein on glass matrix ceramic-dentin bonding strength
- Tez No: 707138
- Danışmanlar: PROF. DR. ASLI SEÇİLMİŞ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Baicalein, Dental bonding, Dental protezler, Dental stres analizi, Dentin, Dimetil sülfoksit, Matriks metalloproteinazlar, Baicalein, Dental bonding, Dental prosthesis, Dental stress analysis, Dentin, Dimethyl sulfoxide, Matrix metalloproteinases
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Gaziantep Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Adeziv bağlantının uzun dönem başarısını artırmak amacıyla matriks metalloproteinaz inhibitörleri kullanarak biyodegradasyonunun önüne geçme fikri güncel bir araştırma konusudur. Bu in vitro çalışmanın amacı matriks metalloproteinaz inhibitörü kullanımının seramik-dentin mikroçekme bağlantı kuvveti üzerine etkisini değerlendirmektir. On altı adet insan mandibular 20 yaş dişinin okluzal minesi prepare edildi ve cam matriks seramik (Celtra Duo) kullanılarak overleyler elde edildi. Dişler 4 gruba ayrıldı. Kontrol grubunda ön işlem uygulanmaksızın total etch, dual cure rezin siman (Variolink N) ile simante edildi. Dimetilsülfoksit ve baicalein grubunda asitleme işleminden sonra çözeltiler uygulandı ve simantasyon, üreticinin talimatları doğrultusunda yapıldı. Baicalein + Ultrasonik aktivasyon grubunda asitleme sonrası baicalein çözeltisi uygulandı, 10 sn ultrasonik aktivasyon yapıldı ve simanın diğer bileşenlerinin baicalein çözeltisiyle aynı penetrasyon derinliğine ulaşması için her aşamada 10 sn ultrasonik aktivasyon yapıldı. Örnekler 5000 devir termal yaşlandırmaya tabi tutuldu. Örnekler kesilerek mikrobar elde edildi ve mikroçekme testi yapıldı. Bağlantı yüzeyi ve ön işlem uygulanmış okluzal yüzey taramalı elektron mikroskobunda görüntülendi. Verilerin normal dağılıma uygunluğu Shaphiro wilk testi ile test edildi normal dağılmayan özelliklerin ikiden fazla bağımsız grupta karşılaştırılmasında ise Kruskal Wallis ve Dunn çoklu karşılaştırma testleri kullanıldı (P<0.05). Kontrol grubu bağlantı dayanıklılığı değerleri diğer üç gruba oranla anlamlı derecede yüksek bulundu. Çalışma sonucunda % 0.1'lik dimetilsülfoksit ve 12.5 μmol/L'lik baicalein çözeltilerinin cam matriks seramik ile dentinin; total etch, dual cure rezin siman (Variolink N) ile simantasyonunda kullanımı önerilmemiştir. Cam matriks seramik-dentin bağlantı dayanıklılığını artırmak için farklı rezin simanlar ve farklı baicalein dozlarıyla daha fazla çalışmaya ihtiyaç duyulmaktadır.
Özet (Çeviri)
In order to increase the long-term success of the adhesive bond, the idea of preventing biodegradation by using matrix metalloproteinase inhibitors is a current research topic. The aim of this in vitro study was to evaluate the effect of matrix metalloproteinase inhibitor use on the ceramic-dentin microtensile bond strength. The occlusal enamel of sixteen human mandibular wisdom teeth was prepared and overlays were obtained using glass matrix ceramic (Celtra Duo). Teeth were divided into 4 groups. In the control group, was cemented with total etch, dual cure resin cement (Variolink N) without pretreatment. In the dimethyl sulfoxide and baicalein group, solutions were applied after etching and cementation was done according to the manufacturer's instructions. In the Baicalein + Ultrasonic activation group, after etching, baicalein solution was applied, ultrasonic activation was performed for 10 seconds and ultrasonic activation was performed for 10 seconds at each stage so that the other components of the cement reached the same penetration depth with the baicalein solution. The samples were subjected to 5000 cycles of thermal aging. Microbar was obtained by cutting the samples and micro-tensile test was performed. The junctional surface and pretreated occlusal surface were visualized in a scanning electron microscope. The conformity of the data to the normal distribution was tested with the Shaphiro Wilk test, and the Kruskal Wallis and Dunn multiple comparison tests were used to compare the non- normally distributed features in more than two independent groups (P<0.05). Connection strength values of the control group were found to be significantly higher than the other three groups. As a result of the study, the use of 0.1% dimethylsulfoxide and 12.5 μmol/L baicalein solutions in glass matrix ceramic and dentin; total etch, dual cure resin cement (Variolink N) cementation was not recommended. More studies are needed with different resin cements and different baicalein doses to increase the durability of the glass matrix ceramic-dentine joint .
Benzer Tezler
- Cam ve plastik seraların sonbahar domates üretimi yönünden karşılaştırılması
Başlık çevirisi yok
ERGUN DURAN
- Ağızlık açma mekanizmalarının tasarımı
Başlık çevirisi yok
RECEP EREN
Yüksek Lisans
Türkçe
1987
Tekstil ve Tekstil MühendisliğiUludağ ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
DOÇ. DR. HALİL R. ALPAY
- Ege bölgesi keçi liflerinin bazı önemli fiziksel, kimyasal özellikleri ve değerlendirme imkanları
Başlık çevirisi yok
NİLÜFER ERDEM
Doktora
Türkçe
1985
Tekstil ve Tekstil MühendisliğiEge ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
PROF. DR. GÜLSEREN YAZICIOĞLU
- Bentonitlerde değişebilir katyonların katman yapısına etkilerinin x-ışınları kırınım yöntemi ile incelenmesi
Başlık çevirisi yok
İLHAN AKSOY
Doktora
Türkçe
1986
Fizik ve Fizik Mühendisliğiİnönü ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. NİZAMETTİN ARMAĞAN
- An Experimental and analytical investigation of cam follower jump phenomenon
Başlık çevirisi yok
ŞÖLEN ŞEN
Yüksek Lisans
İngilizce
1987
Makine MühendisliğiOrta Doğu Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. MEHMET ÇALIŞKAN