Elektrokimyasal polimerizasyon yöntemiyle alüminyum üzerinde sentezlenen poli(N-metil pirol) ve poli(N-metil pirol)/bor nitrür kompozitinin korozyon koruma davranışlarının incelenmesi

Investigation of corrosion protection behaviors of poly(N-methyl pyrrole) and poly(N-methyl pyrrole)/boron nitride composite synthesized on aluminum by electrochemical polymerization method

PDF İndir

  1. Tez No: 716304
  2. Yazar: NİMET CEREN GÜVEN
  3. Danışmanlar: DOÇ. DR. HATİCE ÖZKAZANÇ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Polimer Bilim ve Teknolojisi, Polymer Science and Technology
  6. Anahtar Kelimeler: Alüminyum, Bor Nitrür, Karışım Elektroliti, Korozyon, Poli(N-Metil Pirol), Aluminum, Boron Nitride, Mixture Electrolyte, Corrosion, Poly (N-methyl Pyrrole)
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: Kocaeli Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Polimer Bilim ve Teknolojisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 59

Özet

Bu çalışmada, endüstriyel öneme sahip alüminyum-1050 (Al-1050) yüzeyine okzalik asit (OXA) ve dodesil benzen sülfonik asit (DBSA) karışım elektrolitinde galvanostatik yöntem ile poli(N-metil pirol) (PNMPy) ve PNMPy/BN kompozit filmleri kaplandı. Kaplamaların yapısal ve morfolojik karakterizasyon çalışmaları Fourier Dönüşümlü Kızılötesi (FT-IR) Spektroskopisi, Taramalı Elektron Mikroskobu (SEM), X-ışınları kırınımı (XRD) ve Atomik Kuvvet Mikroskobu (AFM) analizleri ile gerçekleştirildi. Kaplamaların korozyon koruma davranışları 0,1 M H2SO4 içerisinde gerçekleştirilen Tafel polarizasyonu ve elektrokimyasal empedans spektroskopisi (EIS) ile, kaplamaların aşınma dirençleri ise tuz püskürtme testi yapılarak incelendi. DBSA-OXA karışım elektrolitinin kullanılması, kaplamaların homojenliğini ve yapışkanlığını belirgin şekilde arttırdı. Bor nitrür nanopartikülleri polimer filminin ortalama kalınlığını 28 μm'den 20 μm'e düşürdü. Aynı zamanda katkılamayla PNMPy'nin yüzey pürüzlülüğü 121 nm'den 95 nm'ye düştü. EIS analizleri, PNMPy filminin Al-1050'nin yük transfer direncini (Rct) yaklaşık 172 kat, PNMPy/BN kompozit filminin ise yaklaşık 238 kat arttırdığını gösterdi. PNMPy/BN filminin korozyon verimliliğinin % 98,57 olduğu belirlendi. Korozif ortam içerisinde bulunan her iki kaplamanın da, 6. günün sonunda bile Al-1050 yüzeyinden ayrılmadığı ve en iyi korumayı PNMPy/BN kompozit kaplamasının sağladığı belirlendi.

Özet (Çeviri)

In this study, the surface of aluminum-1050 (Al-1050), which has industrial importance, was covered with poly(N-methylpyrrole)/boron nitride (PNMPy/BN) composite film in a mixture electrolyte of oxalic acid (OXA) and dodecylbenzene sulfonic acid (DBSA) by the galvanostatic method. Fourier Transform Infrared (FT-IR) Spectroscopy, Scanning Electron Microscopy (SEM), X-ray diffraction analysis (XRD) and Atomic Force Microscopy (AFM) techniques were used for the characterization and morphology of the film. The corrosion protection behaviors of the coatings were investigated by Tafel polarization and electrochemical impedance spectroscopy (EIS) performed in 0.1 M H2SO4, and the abrasion resistance of the coatings by salt spray test. The DBSA-OXA mixing electrolyte markedly increased the homogeneity and adhesiveness of the coatings. Boron nitride nanoparticles reduced the average thickness of the polymer film from 28 μm to 20 μm. At the same time, the surface roughness of PNMPy by doping decreased from 121 nm to 95 nm. EIS analyzes showed that PNMPy and PNMPy/BN composite films increased the charge transfer resistance (Rct) of Al-1050 around 172 and 238 times, respectively. The corrosion efficiency of the PNMPy/BN film was determined to be 98.57%. It was observed that coatings in the corrosive environment did not separate from the Al-1050 surface even at the end of the 6th day, and the PNMPy/BN composite film provided the best protection.

Benzer Tezler

  1. Tez No

    398003

    Chemical deintercalation and stability investigation of nanosized C/Li2MnSiO4 cathode material with different electrolytes

    C/Li2MnSiO4 katot malzemesinin kimyasal deinterkalasyonu ve farklı elektrolitler ile kararlılığının incelenmesi

    EKİN EŞEN

    Yüksek Lisans

    İngilizce

    İngilizce

    2015

    Mühendislik Bilimleriİstanbul Teknik Üniversitesi

    Nanobilim ve Nanomühendislik Ana Bilim Dalı

    PROF. DR. FİGEN KADIRGAN

  2. Tez No

    558450

    A highly selective and reusable colorimetric and turn-on fluorescent chemosensor based on rhodamine tethered aldehyde functional microspheres for the detection of Cu2+ and Hg2+ ions

    Cu2+ ve Hg2+ 'nın deteksiyonu için yüksek seçicilik gösteren rodamin tutturulmuş aldehit fonksiyonlu mikroküre esaslı kolorimetrik ve floresans 'turn on' tekrar kullanılabilir kemosensörlerin hazırlanması

    PINAR ÖZMEN

    Yüksek Lisans

    İngilizce

    İngilizce

    2019

    Kimyaİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    DOÇ. DR. BÜNYAMİN KARAGÖZ

  3. Tez No

    101382

    N-substituye karbazollerin endüstriyel metallerin korozyonunu önlemedeki etkileri

    Corrosion inhibition effect of N-substituted carbazole on the corrosion of some industrial metals

    SADIK ÖZTÜRK

    Yüksek Lisans

    Türkçe

    Türkçe

    2001

    Kimyaİstanbul Teknik Üniversitesi

    PROF.DR. A. SEZAİ SARAÇ

    Y.DOÇ.DR. ESMA SEZER

  4. Tez No

    55895

    Akrilonitrilin kimyasal ve elektrokimyasal yöntemle polimerizasyonu

    Başlık çevirisi yok

    GÜLBEYAZ ÖZGÜR

    Yüksek Lisans

    Türkçe

    Türkçe

    1996

    Kimyaİstanbul Teknik Üniversitesi

    PROF.DR. A. SEZAİ SARAÇ

  5. Tez No

    356997

    2-aminobenzo[c]sinnolin içeren polimer ve kopolimerlerin üretimi ve karakterizasyonu

    Production and characterization of 2 aminobenzo[c]cinnolines containing polymer and copolymers

    SABRİYE ŞİMŞEK

    Yüksek Lisans

    Türkçe

    Türkçe

    2014

    Kimya MühendisliğiSelçuk Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. AHMET GÜLCE

Geri Dön