Tufal ve düşük tenörlü hematit cevherlerinden sünger demir üretiminde redükleyici olarak soma bölgesi linyit kömürünün kullanılması
Using soma region lignite coal as reducer in production sponge iron from scale and low-grade hematite ores
- Tez No: 733679
- Danışmanlar: DOÇ. DR. MUSTAFA BOYRAZLI
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Sünger Demir, Linyit Kömürü, Soma Bölgesi, Hadde Tufali, Hematit, Mekanik Öğütme, Sponge Iron, Lignite Coal, Soma Region, Rolling Scale, Hematite, Mechanical Grinding
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Üretim Metalurjisi Bilim Dalı
- Sayfa Sayısı: 63
Özet
Bu çalışmada, yerli hammaddeler kullanılarak demir oksitlerin redüksiyonu incelenmiştir. Bu amaçla, %25 tufal, %75 hematit ve toplam malzemenin %40'ı kadar linyit ilave edilerek hazırlanan harmanın mekanik aktivasyon işlemi uygulanmadan hazırlanan peletlerin farklı sıcaklıklarda süreye bağlı olarak yapılan hesaplamada reaksiyonların aktivasyon enerjisinin, ürün tabakasından difüzyon yolu ile kontrol edilmesi durumunda 75,43 kJ/mol olduğu, reaksiyon yüzeyde kimyasal reaksiyon ile kontrol edilmesi durumunda ise 64,10 kJ/mol olduğu anlaşılmıştır. %40 linyit miktarı sabit tutularak karışıma yine %25, 50 ve %75 oranında tufal ilavesi yapılmış ve 60 dakika yüksek enerjili bir değirmende peletleme öncesi öğütme işlemi gerçekleştirilmiştir. Bu deneylerde, sıcaklık, 800, 900 ve 1000oC olarak seçilmiş süre ise 5, 10, 15, 30, 60 ve 120 dakika olarak belirlenmiştir. Yapılan tüm redüksiyon deneylerinde vüstit ilavesi artarken, redüksiyon derecesinde bir düşüş olduğu görülmüştür. Deneysel çalışmalarda en yüksek redüksiyon derecesi %25 tufal, %75 hematit ve toplam miktarın %40'ı kadar ilave edilen redükleyicinin (linyit) 60 dakika süre ile yüksek enerjili bir değirmende öğütüldükten sonra hazırlanan peletlerin 1000oC sıcaklıkta 120 dakika redüksiyona tabi tutulmaları sonucu %98,25 olarak elde edilmiştir.
Özet (Çeviri)
In this study, the reduction of iron oxides using domestic raw materials was investigated. For this purpose, in the calculation made depending on the time at different temperatures of the pellets prepared without applying the mechanical activation process of the blend prepared by adding 25% scale, 75% hematite and 40% lignite of the total material, it has understood that if the activation energy of the reactions is controlled by diffusion from the product layer the activation energy is 73.46 kJ/mol and if the reaction is controlled by chemical reaction on the surface it is 64.10 kJ/mol. By keeping the 40% lignite content constant, 25%, 50% and 75% scale was added to the mixture, and grinding was carried out in a high-energy mill for 60 minutes before pelletizing. In these experiments, the temperature was chosen as 800, 900 and 1000°C, and the time was determined as 5, 10, 15, 30, 60 and 120 minutes. In all reduction experiments, it was observed that while the addition of wustite increased, there was a decrease in the degree of reduction. In experimental studies, the highest reduction degree is 25% scale, 75% hematite and 40% of the total amount of reducer (lignite) is grinded in a high energy mill for 60 minutes, and then the pellets are reduced at 1000°C for 120 minutes it was obtained as %98,25.
Benzer Tezler
- Kendiliğinden ilerleyen yüksek sıcaklık sentezi ile tufalden demir esaslı kompozit (Mo2FeB2-Fe) üretimi
Production of iron based composite (Mo2FeB2-Fe) from scale by self propagating high temperature synthesis
BUSE YILMAZ
Yüksek Lisans
Türkçe
2019
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. CEVAT BORA DERİN
- SHS yöntemiyle tufal ve hematit kaynağı kullanılarak Fe3Al intermetalik bileşiğinin üretimi ve Ni, Cr, W ilavelerinin etkileri
Production of Fe3Al intermetallic compound using scale and hematite source by SHS method and the effects of Ni, Cr, W additions
GİZEM ÖZÖZTÜRK BARUTÇU
Yüksek Lisans
Türkçe
2022
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. CEVAT BORA DERİN
- Tek taraflı delmede kuvvet ve malzeme akışına etkiyen faktörlerin incelenmesi
Investigation of the factors affecting the force and material flow in single punch indentation
ŞABAN MARAŞLIOĞLU
- 20MnB4 özel alaşımlı çelik tel çubukların haddelenmesi esnasındaki soğuma hızının ve serme kafa sıcaklığının tufal yapısına etkisi
Influence of cooling rate and laying head temperature on structure of scale during rolling of 20MnB4 special alloy steel wire rod
ONUR MEYDAN
Yüksek Lisans
Türkçe
2017
Metalurji MühendisliğiSakarya ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. MUSTAFA AKÇİL
- SHS yöntemi ile tufal kullanılarak AlFe2B2 intermetalik bileşiğinin üretimi
Production of AlFe2B2 intermetallic compound by using mill scale with SHS method
ECEM TURHAN
Yüksek Lisans
Türkçe
2019
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. CEVAT BORA DERİN