5140 alaşımından mamül cıvata üretiminde ısıl işlem parametrelerinin çeliğin mekanik özelliklere etkisi
The effect of heat treatment parameters on the mechanical properties of steel in the production of bolts made of 5140 alloy
- Tez No: 767808
- Danışmanlar: DOÇ. DR. YASİN RAMAZAN EKER
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Civata, Demir çelik sektörü, Paslanmaz çelik, Sertleştirilmiş çelik, Tavlama, Östenitleme, Bolt, Iron steel sector, Stainless steel, Hardened steel, Annealing, Austenization
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Necmettin Erbakan Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Metalurji ve Malzeme Mühendisliği Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Cıvata, birbirine bağlanmak istenen parçaları birleştirmek için kullanılan bağlantı elemanıdır. Makine, inşaat, otomotiv vb. sektörlerde en çok ihtiyaç duyulan bağlantı elemanıdır. Cıvata üretiminde en çok kullanılan çelik AISI 5140 ıslah çeliğidir. Islah işlemi ile istenilen mekanik özellikleri sağlamak mümkündür. Endüstride sıklıkla kullanılan SAE 5140 çeliğinden üretilmiş numuneler 400 °C 'de ön ısıtma yapıldıktan sonra 30 dk. 860 °C'de bekletilip yağda su verme işlemine tabi tutulmuştur. Martenzit yapı elde edildikten sonra, 4 farklı menevişleme sıcaklığı (30 dk.) uygulanmıştır. Uygulanan farklı meneviş sıcaklıkları sonrasında numunelerin çekme testleri yapıp mekanik özellikleri değerlendirilmiştir. AISI 5140 çeliğine ovalama yöntemiyle diş açılıp menevişleme işlemine tabi tutulduktan sonra parçalar bakalite alınıp parçaların sertlikleri incelenmiştir. Sertliğin en yüksek olduğu bölgenin diş üstü bölgesi olduğu tespit edilmiştir. Menevişleme sıcaklığındaki artışla çekme ve akma mukavemet değerlerinde azalma görülürken, uzama değerinde artma tespit edilmiştir. Artan menevişleme sıcaklığıyla AISI 5140 çeliğinde süneklik eğiliminin arttığı görülmüştür. Numunelerin SEM görüntüleri değerlendirilmiştir.
Özet (Çeviri)
Bolt is the connecting element used to join the parts to be connected to each other. Machinery, construction, automotive etc. It is the most needed fastener in the industry. The most commonly used steel in bolt production is AISI 5140 tempered steel. It is possible to provide the desired mechanical properties with the improvement process. Samples made of SAE 5140 steel, which is frequently used in the industry, are preheated at 400 °C for 30 minutes. It was kept at 860 °C and subjected to oil quenching. After obtaining the martensite structure, 4 different tempering temperatures (30 min.) were applied. After the different tempering temperatures applied, the tensile tests of the samples were performed and their mechanical properties were evaluated. After the AISI 5140 steel was threaded with the rubbing method and subjected to the tempering process, the parts were mounted and the hardness of the parts was examined. It has been determined that the region with the highest hardness is the upper tooth region. With the increase in tempering temperature, a decrease was observed in the tensile and yield strength values, while an increase in the elongation value was detected. It was observed that the ductility tendency of AISI 5140 steel increased with increasing tempering temperature. SEM images of the samples were evaluated..
Benzer Tezler
- Demir çelik sektörü ve demir çelik sektöründe sermaye maliyeti
Iron and steel sector and cost of capital in iron and steel sector
ALİ DİKMEN
Yüksek Lisans
Türkçe
2002
İşletmeMarmara ÜniversitesiSermaye Piyasası ve Borsa Ana Bilim Dalı
YRD. DOÇ. DR. MAHMUT HAYATİ ERİŞ
- Krom ve nikelin Fe-C alaşımına direkt redüksiyonu
Direct reduction of chrome and nickel to Fe-C alloy
TİMUR UZUNOĞLU
Yüksek Lisans
Türkçe
2004
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ONURALP YÜCEL
- Toz katkılı elektriksel kıvılcımla işlenen Ti-6Al-4V alaşımında yüzey değişimleri ve biyouyumluluk özellikleri
Surface modifications and biocompatibility properties of Ti-6Al-4V alloy in powder mixed electrical discharge machining
HAMİDULLAH YAŞAR
Doktora
Türkçe
2021
Makine MühendisliğiZonguldak Bülent Ecevit ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. BÜLENT EKMEKCİ
- Kendiliğinden ilerleyen yüksek sıcaklık sentezi yöntemi ile yeni ve özel alaşımların üretimi ve geliştirilmesi
Investigation of new and noble alloys productions by self-propagating high-temperature synthesis method
MURAT ALKAN
Doktora
Türkçe
2014
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ONURALP YÜCEL
DOÇ. DR. CEVAT BORA DERİN
- Pirinç alaşımlarının farklı sıcaklık ve tutma sürelerinde çinkosuzlaşma davranışlarının incelenmesi
Investigation of dezincification behaviours of brass alloys at different temperatures and holding times
CANER KARADEMİR
Yüksek Lisans
Türkçe
2024
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. NECİP ÜNLÜ