T6 ve derin kriyojenik ısıl işlemleri uygulanmış alüminyum esaslı magnezyum alaşımlarının mikroyapı, aşınma ve deniz suyu korozyonu performansının incelenmesi
Investigation of microstructure, wear and seawater corrosion performance of T6 and deep cryogenic heat treated aluminum based magnesium alloys
- Tez No: 812195
- Danışmanlar: DOÇ. MUSTAFA ÖZGÜR ÖTEYAKA
- Tez Türü: Yüksek Lisans
- Konular: Havacılık ve Uzay Mühendisliği, Aeronautical Engineering
- Anahtar Kelimeler: Magnezyum, Magnesium
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Eskişehir Osmangazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Havacılık Bilimi ve Teknolojileri Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, AZ91 ve AM60 magnezyum alaşımlarına T6 (çözeltiye alma ve yaşlandırma) ısıl işlemi ve ardından derin kriyojenik (DC) ısıl işlemi uygulanmıştır. Çözeltiye alma ısıl işlemi 400°C'de farklı sürelerde (4, 5 ve 6 saat) yapılmıştır. Yaşlandırmada ısıl işlemi ise 200°C'de 10 saat fırında tavlanarak gerçekleştirilmiştir. Bu işlemler sonrası numuneler -196°C'de 48 saat boyunca derin kriyojenik (DC) ısıl işlemine tabii tutulmuştur. Numunelerin aşınma direncini ölçmek için pin-on-disc yöntemi ve korozyon direncini ağırlıkça %3.5 NaCl içeren sulu çözeltide elektrokimyasal deneyler yapılarak ölçülmüştür. Elde edilen bulgularda, AZ91 ve AM60'ın mikroyapısının ısıl işlemlerden sonra değiştiği gözlemlenmiştir. AZ91 için ötektik fazın, matris içinde daha fazla çözündüğü diğer taraftan AM60 alaşımında ise 6 saat hariç 4 ve 5 saatlik süreler sonrasında ötektik fazın mikroyapıda dağıldığı ve matriste çözündüğü gözlemlenmiştir. Aşınma hızının AZ91 alaşımında süre ile beraber artarken, AM60 alaşımında 5 saat sonrasında düşüş gözlemlendiği tespit edilmiştir. Korozyon çalışmalarında ise ısıl işlem görmemiş AZ91 alaşımının açık devre potansiyelinin (Eocp), ısıl işlem görmüş numunelere göre daha pozitif olduğu görülmüştür. Buna karşın, AM60 alaşımında ise T6 ısıl işlem süresinin artması ile Eocp pozitif yönde artış olduğu gözlemlenmiştir. Ayrıca, ısıl işlem görmüş veya görmemiş AZ91 ve AM60 alaşımları için elde edilen polarizasyon eğrilerinde herhangi bir pasivasyon bölgesi oluşmadığı anlaşılmıştır.
Özet (Çeviri)
In this study, T6 (solution and aging) heat treatment followed by deep cryogenic (DC) heat treatment was applied to AZ91 and AM60 magnesium alloys. Solution heat treatment was carried out at 400°C for different times (4, 5 and 6 hours). Heat treatment in aging was carried out by annealing in an oven at 200°C for 10 hours. After these processes, the samples were subjected to deep cryogenic (DC) heat treatment at -196°C for 48 hours. In order to measure the wear resistance of the samples, the pin-on-disc method and the corrosion resistance were measured by performing electrochemical experiments in an aqueous solution containing 3.5% NaCl by weight. In the obtained findings, it was observed that the microstructure of AZ91 and AM60 changed after heat treatment. For AZ91, it was observed that the eutectic phase dissolved more in the matrix, on the other hand, in AM60 alloy, after 4 and 5 hours, excluding 6 hours, the eutectic phase dispersed in the microstructure and dissolved in the matrix. It was determined that while the wear rate increased with time in the AZ91 alloy, it decreased after 5 hours in the AM60 alloy. In corrosion studies, the open circuit potential (Eocp) of the untreated AZ91 alloy was found to be more positive than the heat treated samples. On the other hand, it was observed that Eocp increased positively with the increase of T6 heat treatment time in AM60 alloy. In addition, it was understood that no passivation zone was formed in the polarization curves obtained for the heat treated or untreated AZ91 and AM60 alloys.
Benzer Tezler
- Experimental and numerical analysis of deep drawability of aluminium alloys AA5754-H22 and AA6061-T6
Alüminyum alaşımları AA5754-H22 ve AA6061-T6'nın deneysel ve sayısal analizlerle derin çekme kabiliyetlerinin incelenmesi
ONUR ERBAŞ
Yüksek Lisans
İngilizce
2015
Makine MühendisliğiTürk-Alman Üniversitesiİmalat Mühendisliği Ana Bilim Dalı
YRD. DOÇ. MEHMET İPEKOĞLU
PROF. DR. AHMET ERMAN TEKKAYA
- Havacılık sanayisinde kullanılan alüminyum alaşımlarının derin çekme yöntemiyle şekillendirilebilirliği ve sonlu elemanlar yöntemiyle analizi
Formability of aluminum alloys used in aviation industry by deep drawing method and analysis by finite element method
TURAL YUSIFOV
Yüksek Lisans
Türkçe
2025
Havacılık ve Uzay MühendisliğiSelçuk ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. RECAİ KUŞ
- Ilık derin çekme prosesi için şekillendirme sıcaklıklarının belirlenmesi ve karakterizasyonu
Determination and characterization of forming temperatures for warm deep drawing process
MUHAMMET HÜSEYİN ÇETİN
Doktora
Türkçe
2015
Mühendislik BilimleriKarabük ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. EROL ARCAKLIOĞLU
- Yerli olarak tasarlanmış ve üretilmiş“derin iç altıgen şekilli implant gövde ve destek bağlantılarının”çiğneme kuvvetleri altındaki davranışlarının değerlendirilmesi
Evaluation of the behavior of“deep internal hexagonal shaped implant body and abutment connections”designed and produced domestically under masticatory forces
YEZDAN DİLAN ERKCAN
Doktora
Türkçe
2021
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. MEHMET ALİ KILIÇARSLAN
PROF. DR. BURAK BİLECENOĞLU
- Dental implant sistemlerinin tanımlanmasında yapay zeka ve insan gözlemci performansları: Derin öğrenme algoritmalarının etkisi
Performance of artificial intelligence and human observers in the identification of dental implant systems: The effect of deep learning algorithms
OĞUZ ALP KÖSE
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiAydın Adnan Menderes ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. MUSA ŞAMİL AKYIL