Karaçam odunundan üretilen Çapraz Tabakalı Kereste (ÇTK) malzemenin farklı koşullardaki mekanik dayanımı üzerine bir araştırma
Research on the mechanical strength of Cross-Laminated Timber (CLT) material produced from pine wood under different conditions
- Tez No: 824344
- Danışmanlar: PROF. DR. BEKİR CİHAD BAL
- Tez Türü: Yüksek Lisans
- Konular: Ağaç İşleri, İnşaat Mühendisliği, Wood Products, Civil Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Kahramanmaraş Sütçü İmam Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Malzeme Bilimi ve Mühendisliği Bilim Dalı
- Sayfa Sayısı: 76
Özet
Bu çalışmada, Kahramanmaraş bölgesinde yetişen karaçam odunundan elde edilen çapraz tabakalı kereste (ÇTK) malzemenin mekanik özellikleri incelenmiştir. Poliüretan tutkalı kullanılarak karaçam odunundan çapraz tabakalı kereste üretilmiştir. Üretilen yapı malzemesi hem hava kurusu hem de yaş halde çeşitli mekanik testlere tabi tutulmuştur. Masif halde 16 x 100 x 1000 mm ebatlarında (kalınlık, genişlik, uzunluk) olan karaçam kerestesinden 48x500x1000 mm ebatlarında her tabaka birbirine dik olacak şekilde 3 tabakalı 5 adet ÇTK üretilmiştir. Elde edilen malzemenin 3 nokta eğilme direnci ve elastikiyet modülü, makaslama direnci, çivi tutma direnci testleri ile yoğunluğu ve rutubeti tespit edilmiştir. Ayrıca, ÇTK üretiminde kullanılan karaçam masif odununun testleri de yapılmıştır. Yapılan testlerin sonucuna göre; hava kurusu haldeki test örneklerinin yaş haldeki test örneklerinden daha büyük mekanik özelliklere sahip olduğu tespit edilmiştir. Eğilme direnci testinde, yaş haldeki test örneklerinin deformasyon miktarı kuru haldeki test örneklerinin deformasyon miktarından daha yüksek olduğu tespit edilmiştir. Çivi tutma deneyinde maksimum deformasyon ortalamasının hava kurusu örneklerde 13,9 mm ile yaş haldeki örneklerden 29,33 mm ile daha düşük olduğu belirlenmiştir. Makaslama direnci testi sonunda yaş haldeki örneklerden sadece üç tanesinde delaminasyon (tutkal hattından ayrılma) meydana gelmiştir. Hava kurusu örneklerden iki tanesinde delaminasyon gerçekleşmiştir. Yaş haldeki örneklerin, eğilme direnci testi esnasında, daha esnek davranış gösterdiği sonucuna ulaşılmıştır.
Özet (Çeviri)
In this study, the mechanical properties of cross-layered timber (ÇTK) material obtained from black pine wood grown in Kahramanmaraş region were investigated. Cross-laminated timber was produced from black pine wood using polyurethane glue. The produced building material was subjected to various mechanical tests in both air-dry and wet state. Five different samples with 3 layers were prepared from black pine timber with dimensions of 16 x 100 x 1000 mm (thickness, width, length) in solid form, with the dimensions of 48x500x1000 mm, each layer perpendicular to each other. Density, moisture content, 3-point modulus of rupture and modulus of elasticity, shear strength, nail holding strength tests were determined. According to data obtanied; It has been determined that the air-dried test specimens have greater mechanical properties than the wet test specimens. In the bending strength test, it was determined that the amount of displacement of the wet test samples was higher than the amount of displacement of the dry test samples. In the nail holding test, it was determined that the average displacement was 13.9 mm in air-dry samples, and was 29.3 mm in the wet samples. Delamination (separation from the glue line) occurred in only three of the wet samples as a result of the shear strength test. Delamination occurred in two of the air-dried samples. It was concluded that the water-saturated samples showed more ductile behaviour than that of dry samples.
Benzer Tezler
- Türkiye'de yonga levha endüstrisi sorunları ve çözüm yolları
Die spanplatten indüstrie in der Türkei ihre probleme und lösungsmöglichkeiten
ABDİ EKİZOĞLU
- Veritabanlarında genetik algoritma ve bulanık mantık tabanlı esnek sorgulama
Genetic algorithm and fuzzy logic based flexible querying in databases
ALİ ŞENOL
Yüksek Lisans
Türkçe
2013
Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve KontrolGazi ÜniversitesiBilgisayar Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. HACER KARACAN
- Karaçam odunundan elde edilen sulu ekstrelerin diyabet oluşturulmuş dişi sıçanlarda hypergliseminin kontrolü ile bazı komplikasyonlar üzerinde etkisi
Effects on the some complications with control of hyperglicemia obtained from pine wood aqueous extract, induced diabetic female rats
SEDA ESMA TUĞ
- Derin ötektik çözücü kullanılarak karaçam ve titrek kavak odunundan lignin nanopartiküllerinin hazırlanması ve karakterizasyonu
Preparation and characterization of lignin nanoparticles from black pine and aspen woods by using deep eutectic solvents
MAHMUT ÖZAYDIN
Yüksek Lisans
Türkçe
2024
Ağaç İşleriBartın ÜniversitesiOrman Endüstri Mühendisliği Ana Bilim Dalı
PROF. DR. DENİZ AYDEMİR
- Emprenyeli kapı ve pencere doğramalarının emprenyesiz kapı ve pencere doğramalarına göre maliyetlerinin karşılaştırılması
The comparison of the cost of door and window woodworks prepared within and without impregnation
İBRAHİM AYBEY
Yüksek Lisans
Türkçe
1999
Ormancılık ve Orman MühendisliğiKaradeniz Teknik ÜniversitesiOrman Endüstri Mühendisliği Ana Bilim Dalı
DOÇ.DR. HİCABİ CINDIK