The effect of water cement ratio and curing temperature on alkali aggregate reaction

Su çimento oranı ve kür sıcaklığının alkali agrega reaksiyonu üzerindeki etkisi

  1. Tez No: 826835
  2. Yazar: LINA MOHAMMAD ABED ALJAWAD
  3. Danışmanlar: PROF. DR. LUTFULLAH TURANLI
  4. Tez Türü: Yüksek Lisans
  5. Konular: İnşaat Mühendisliği, Civil Engineering
  6. Anahtar Kelimeler: Alkali silika reaksiyonu, Hızlandırılmış harç çubuğu testi, Taramalı elektron mikroskobu, Alkali-jel, Kürleme sıcaklıkları, Su-çimento oranı, Alkali silica reaction, Accelerated mortar bar test, Scanning electron microscopy, Alkali-gel, Curing temperatures, Water cement ratio
  7. Yıl: 2023
  8. Dil: İngilizce
  9. Üniversite: Ankara Yıldırım Beyazıt Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: İnşaat Mühendisliği Bilim Dalı
  13. Sayfa Sayısı: 129

Özet

Alkali-silika reaksiyonu (ASR), Portland çimento betonunda, su alımı üzerine şişen ve betonun çatlamasına neden olan bir alkali jel oluşumuyla sonuçlanan yaygın bir kimyasal reaksiyondur. Şişmenin boyutu üç faktöre bağlıdır: toplam reaktivite, sıcaklık ve nem. Bu deneysel çalışmada, sıcaklık ve su/çimento oranı (w/c) olmak üzere iki faktörün ASR üzerindeki etkisi araştırılmıştır. ASTM C 1260'a eşdeğer RILEM AAR-2 yöntemi kullanılarak iki tip agrega (A ve B) incelenmiştir. 54 çubuk harç dökülmüş ve karışımdaki w/c içeriğine ve kür sıcaklıklarına göre alt bölümlere ayrılmıştır (40°C, 60°C,ve 80°C). Harç çubuklarının genleşmesi 28 güne kadar her üç günde bir ölçülmüştür. Ayrıca, çalışılan numunelerin iç katmanlarını ve alkali jel dahil reaksiyon ürünlerini analiz etmek için enerji dağılımlı X-ışını spektroskoplu (SEM/EDX) taramalı elektron mikroskobu kullanılmış. Çalışmanın sonuçları, ASR'nin sıcaklık ve w/c oranı arttığında harç çubukları üzerinde tahrip edici bir etkiye sahip olduğunu göstermiştir. Harç çubuklarının genleşmesi, ASR'nin neden olduğu açık bir içsel çatlama göstergesidir. SEM görüntüleri, alkali jelin, özellikle yüksek sıcaklıklara ve yüksek w/c oranlarına maruz kalan çubuklar için, düşük sıcaklıklara ve w/c oranlarına maruz kalanlara kıyasla, çubukların iç yapısının geniş bir alanını kapladığı görülmüştür. Bu çalışmanın sınırlı sonuçlarına dayanarak, teste maksimum 0.50 w/c oranı ve minimum 60°C kürleme sıcaklığı kullanılması önerilmisti.

Özet (Çeviri)

The alkali-silica reaction (ASR) is a common chemical reaction in Portland cement concrete that results in the formation of an alkali gel that swells upon water intake and causes cracking of concrete. The extent of swelling depends on three factors: aggregate reactivity, temperature, and moisture. In this experimental study, the effect of two factors, temperature and water/cement ratio (w/c) on ASR was investigated. Two types of aggregates (A and B) were investigated using the RILEM AAR-2 method that is equivalent of ASTM C 1260. 54 mortar bars were cast and subdivided according to the w/c content in the mixture and the curing temperatures (40°C, 60°C, and 80°C). The expansion of the mortar bars was measured every three days up to 28 days. Moreover, scanning electron microscopy with energy dispersive X-ray spectroscope (SEM/EDX) was used to analyze the inner layers of the studied specimens and the reaction products, including the alkali gel. The results of the study showed that ASR had a destructive effect on the mortar bars when the temperature and w/c ratio increased. The expansion of the mortar bars had clear signs of internal cracking caused by ASR. The SEM imagery showed that the alkali gel covered a large area of the internal structure of the bars, especially for the bars exposed to high temperatures and high w/c ratios compared to those exposed to lower temperatures and w/c ratios. Based on the limited results of this study a recommended to utilize a maximum w/c ratio of 0.50 and a minimum curing temperature of 60 °C in testing.

Benzer Tezler

  1. Kür koşulları ve yalıtımın yüksek dayanımlı betonların geçirimlilik, iç-yapı ve mekanik özeliklerine etkileri

    Effects of curing conditions and insulation on permeability, microstructure and mechanical properties of high strength concrete

    FATİH ÖZALP

    Doktora

    Türkçe

    Türkçe

    2016

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ÖZKAN ŞENGÜL

  2. Farklı sıcaklıklardaki su kürünün harç numuneleri üzerine etkisi

    Effect of water curing at different temperatures on mortar samples

    SEMA YILDIRIM

    Yüksek Lisans

    Türkçe

    Türkçe

    2020

    İnşaat MühendisliğiKocaeli Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. SALİH TANER YILDIRIM

  3. Kürün betonun kuruma etkisinde büzülme davranışına etkisi

    The effect of curing on the shrinkage behavior of concrete

    UBEYDULLAH AYVAZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ ÜNAL ANIL DOĞAN

  4. Ortalama hafif agrega boyutunun yarı hafif betonların dona dayanıklılığı üzerindeki etkileri

    The Effect of light weight aggregate fraction on the freezing-thawing resistance of semi-light weight concretes

    GÜL HATİCE ÖZTÜTÜNCÜ

    Yüksek Lisans

    Türkçe

    Türkçe

    1992

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    DR. OSMAN OKTAR

  5. Influence of powder and emulsion polymer addition on strength and capillary properties of cement mortars

    Toz ve emülsyon polimer katkılarının çimentolu harçların dayanım ve kılcallık özelliklerine etkisi

    ZEHRA KÖKMEN

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. MUSTAFA HULUSİ ÖZKUL